A CRESCENTE DEMANDA POR MATERIAIS DE CONSTRUçãO SUSTENTáVEIS IMPACTA NA PRODUçãO DE NOVOS LIGANTES QUE APRESENTEM BAIXA EMISSãO DE CO2. UMA NOVA CLASSE CIMENTOS ALTERNATIVOS NOMEADOS DE GEOPOLíMEROS PODEM SER PRODUZIDOS UTILIZANDO RESíDUOS DA INDúSTRIA DE MINERAçãO E AGRíCOLA. OS GEOPOLíMEROS SãO FORMADOS A PARTIR DE UM MATERIAL RICO EM ALUMINOSSILICATOS E UMA SOLUçãO ALCALINA. AS LIGAçõES DE SI-O-AL PRESENTES NO GEOPOLíMEROS LHES CONFEREM ALTA RESISTêNCIA MECâNICA, DURABILIDADE E REFRATARIABILIDADE. COM BASE NISSO, O PRESENTE TRABALHO, AVALIOU A INFLUêNCIA DA CURA TéRMICA NA RESISTêNCIA A COMPRESSãO DE ARGAMASSAS GEOPOLIMéRICAS COM ADIçãO DE ESCóRIA DE ALTO FORNO, E TAMBéM A SUA MORFOLOGIA APóS RUPTURA. PARA ISSO, FORAM UTILIZADOS METACAULIM OBTIDO A 850°C POR 2H, 35% DE ESCóRIA DE ALTO-FORNO, HIDRóXIDO DE SóDIO, SILICATO DE SóDIO E AREIA COMERCIAL PARA A PRODUçãO DA ARGAMASSA GEOPOLIMéRICA. APóS A MOLDAGEM, OS CORPOS-DE-PROVA FORAM SUBMETIDOS A 25°C, 60°C E 120°C POR 20H. APóS 7 DIAS DE CURA EM TEMPERATURA AMBIENTE, OS CORPOS-DE-PROVA FORAM SUBMETIDOS AO ENSAIO DE RESISTêNCIA A COMPRESSãO, E EM SEGUIDA A MORFOLOGIA DA FRATURA FOI ANALISADA VIA MICROSCOPIA óPTICA (MO). A ARGAMASSA GEOPOLIMéRICA CURADA TERMICAMENTE A 60°C APRESENTOU MELHOR RESISTêNCIA à COMPRESSãO, COM 59,78 MPA, COM UMA MICROESTRUTURA DENSA E COMPACTADA.
THE GROWING DEMAND FOR SUSTAINABLE CONSTRUCTION MATERIALS IMPACTS THE PRODUCTION OF NEW BINDERS THAT HAVE LOW CO2 EMISSIONS. A NEW CLASS OF ALTERNATIVE CEMENTS CALLED GEOPOLYMERS CAN BE PRODUCED USING WASTE FROM THE MINING AND AGRICULTURAL INDUSTRIES. GEOPOLYMERS ARE PRODUCED FROM A MATERIAL RICH IN ALUMINOSILICATES AND AN ALKALINE SOLUTION. THE SI-O-AL BONDS PRESENT IN GEOPOLYMERS GIVE THEM HIGH MECHANICAL STRENGTH, DURABILITY AND REFRACTORINESS. BASED ON THIS, THE PRESENT WORK EVALUATED THE INFLUENCE OF THERMAL CURING ON THE COMPRESSIVE STRENGTH OF GEOPOLYMER MORTARS WITH THE ADDITION OF BLAST FURNACE SLAG, AND ALSO THEIR MORPHOLOGY AFTER RUPTURE. FOR THIS, METAKAOLIN OBTAINED AT 850°C FOR 2H, 35% BLAST FURNACE SLAG, SODIUM HYDROXIDE, SODIUM SILICATE AND COMMERCIAL SAND WERE USED FOR THE PRODUCTION OF GEOPOLYMERIC MORTAR. AFTER MOLDING, THE SPECIMENS WERE SUBJECTED TO 25°C, 60°C AND 120°C FOR 20H. AFTER 7 DAYS OF CURING AT ROOM TEMPERATURE, THE SPECIMENS WERE SUBJECTED TO A COMPRESSIVE STRENGTH TEST, AND THEN THE FRACTURE MORPHOLOGY WAS ANALYZED VIA OPTICAL MICROSCOPY (OM). THE GEOPOLYMER MORTAR THERMALLY CURED AT 60°C SHOWED BETTER COMPRESSIVE STRENGTH, WITH 59.78 MPA, WITH A DENSE AND COMPACTED MICROSTRUCTURE.
Palavras-chave
Geopolímeros; argamassa; cura térmica.
Geopolymers; mortar; thermal cure.
Como citar
FERREIRA, PAULO ANDERSON ARANHA;
FRANÇA, GIOVANA ZAGALO DE;
SANTANA, RAYANNE OLIVEIRA LEÃO;
BOTELHO, EMILY DE FÁTIMA PINHEIRO;
CANDIDO, VERÔNICA SCARPINI;
SILVA, ALISSON CLAY RIOS DA.
A INFLUÊNCIA DA CURA TÉRMICA NA RESISTÊNCIA A COMPRESSÃO DE ARGAMASSAS GEOPOLIMÉRICAS
,
p. 409-418.
In: 22º Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas,
São Paulo, Brasil,
2024.
ISSN: 2594-4711
, DOI 10.5151/2594-4711-41181