A INFLUÊNCIA DA FASE Δ E DO VAPOR D’ÁGUA NO ESTÁGIO INICIAL DE OXIDAÇÃO A QUENTE DA LIGA VAT46®

THE INFLUENCE OF PHASE δ AND WATER VAPOR IN INITIAL STAGE OF HIGH TEMPERATURE OXIDATION OF THE VAT46 ALLOY

Autoria

Jr, Jorge Luiz Meyrelles

Jr, Jorge Luiz Meyrelles

Eu sou esse autor

DOI

10.5151/2594-5327-34245

Downloads

Resumo

A LIGA VAT46® TEM GRANDE POTENCIAL DE APLICAÇÃO EM VÁLVULAS DE MOTOR, ONDE É MANDATÓRIO QUE A LIGA APRESENTE BOA PROPRIEDADE MECÂNICA E RESISTÊNCIA À CORROSÃO A ALTAS TEMPERATURAS. EM OUTRAS LIGAS COMUMENTE UTILIZADAS EM VÁLVULAS, DOIS FATORES INFLUENCIAM TANTO NO PROCESSO QUANTO NO TIPO DE OXIDAÇÃO: A FASE Δ E ÁGUA NO ESTADO VALOR. NA LIGA VAT46®, POR SER UMA LIGA EM DESENVOLVIMENTO, AINDA NÃO HÁ DADOS SUFICIENTES SOBRE A INFLUÊNCIA DA PRESENTA DE VAPOR D’ÁGUA DURANTE O PROCESSO DE OXIDAÇÃO E NEM SE A FASE Δ INFLUENCIA NO TIPO DE OXIDAÇÃO E NA NUCLEAÇÃO DOS ÓXIDOS. POR ISSO, FORAM OXIDADAS DUAS AMOSTRAS, UMA COM FASE Δ E OUTRA SEM, EM AMBIENTE DIFERENTES: UM SECO E OUTRO COM VAPOR D’ÁGUA, POR 10 HORAS, UM PERÍODO SUFICIENTE PARA ANALISAR A INFLUÊNCIA DA FASE Δ E DO VAPOR D’ÁGUA NO ESTÁGIO INICIAL DA OXIDAÇÃO. PARA A EXPERIMENTAÇÃO, O FORNO UTILIZADO POSSIBILITAVA O CONTROLE DE PRESSÃO E COMPOSIÇÃO QUÍMICA DO AMBIENTE, E PARA A ANÁLISE DOS RESULTADOS, FOI UTILIZADO MICROSCÓPIO ELETRÔNICO DE VARREDURA E ESPECTROSCOPIA DE DISPERSÃO DE RAIO-X. OS DADOS INDICAM UMA VARIAÇÃO NA TAXA DE OXIDAÇÃO COM A PRESENÇA DE VAPOR D’ÁGUA E A PREFERÊNCIA DA NUCLEAÇÃO DE OXIDO EM REGIÕES DISTINTAS ÀQUELAS RICAS EM FASE Δ.

VAT46® ALLOY HAS GREAT APPLICATION POTENTIAL IN ENGINE VALVES, WHERE IT IS MANDATORY THAT THE ALLOY HAS GOOD MECHANICAL PROPERTY AND HIGH TEMPERATURE CORROSION RESISTANCE. IN OTHER ALLOYS COMMONLY USED IN VALVES, TWO FACTORS INFLUENCE BOTH THE PROCESS AND THE TYPE OF OXIDATION: THE PHASE δ AND WATER IN VALUE STATE. IN VAT46®, BEING AN ALLOY IN DEVELOPMENT STAGE, THERE IS STILL NOT ENOUGH DATA ABOUT THE INFLUENCE OF THE WATER VAPOUR PRESENCE DURING THE OXIDATION PROCESS AND IF THE PHASE δ INFLUENCES THE TYPE OF OXIDATION AND THE OXIDES NUCLEATION. THEREFORE, TWO SPECIMENS WERE OXIDIZED, ONE WITH PHASE δ AND THE OTHER WITHOUT, IN DIFFERENT ENVIRONMENT: ONE DRY AND THE OTHER ONE WITH WATER VAPOR, FOR 10 HOURS, A PERIOD SUFFICIENT TO ANALYZE THE INFLUENCE OF PHASE δ AND WATER VAPOR IN THE OXIDATION INITIAL STAGE. FOR THE EXPERIMENTAL PURPOSES, THE FURNACE UTILIZED MADE IT POSSIBLE TO CONTROL THE PRESSURE AND THE ENVIRONMENT CHEMICAL COMPOSITION, AND FOR THE ANALYSIS OF THE RESULTS, AN ELECTRONIC SCANNING MICROSCOPE AND X-RAY DISPERSION SPECTROSCOPY WERE ALSO USED. THE DATA INDICATE A VARIATION IN THE OXIDATION RATE WITH THE WATER VAPOR PRESENCE AND THE PREFERENCE FOR OXIDE NUCLEATION IN DISTINCT REGIONS FROM THOSE RICH IN PHASE δ.

Palavras-chave

VAT46®; Oxidação a altas temperaturas; Estágio inicial; Corrosão

VAT46®; High temperature oxidation; Initial stage; Corrosion