A INFLUÊNCIA DA PERDA DA PLASTICIDADE DE UMA ARGILA CAULINÍTICA POR CALCINAÇÃO NA RESISTÊNCIA À COMPRESSÃO DE ARGAMASSAS : INFLUENCE OF THE LOSS OF PLASTICITY OF A KAOLINITIC CLAY DURING CALCINATION ON THE COMPRESSIVE STRENGTH OF MORTARS

A ARGILA é UM MATERIAL NATURAL UTILIZADO DESDE OS TEMPOS MAIS ANTIGOS NO QUE SE DIZ RESPEITO AS CONSTRUçõES E DESENVOLVIMENTO DE MORADIAS. SUA VASTA UTILIZAçãO é DECORRENTE DE SUAS PROPRIEDADES FíSICAS E QUíMICAS, ALéM DE SUA ABUNDâNCIA NA CROSTA E BAIXO CUSTO DE OBTENçãO, TORNANDO-A UMA ALTERNATIVA ECONôMICA E ACESSíVEL. ALéM DISSO, A ARGILA CONTRIBUI PARA A SUSTENTABILIDADE DO SETOR, ESPECIALMENTE QUANDO UTILIZADA COMO MATERIAL CIMENTíCIO SUPLEMENTAR, SUBSTITUINDO PARCIALMENTE O CIMENTO PORTLAND E REDUZINDO A PEGADA DE CARBONO. A UTILIZAçãO DE ARGILAS, SEJA EM SEU ESTADO NATURAL OU SUBMETIDAS A TRATAMENTO TéRMICO (CALCINAçãO), TEM SIDO OBJETO DE CRESCENTE INTERESSE DEVIDO à SUA ABUNDâNCIA, BAIXO CUSTO E POTENCIAL SUSTENTáVEL. EM TERMOS GERAIS, A ARGILA PROMOVE UM AUMENTO NA PLASTICIDADE DE ARGAMASSAS QUANDO EM SEU ESTADO NATURAL, NO ENTANTO, EM SEU ESTADO CALCINADO, QUANTO MAIOR A TEMPERATURA DO TRATAMENTO TéRMICO, MENOR SUA PLASTICIDADE. ESSES BENEFíCIOS FAZEM DA ARGILA UMA ESCOLHA RECORRENTE E EFICIENTE EM DIVERSAS APLICAçõES NA CONSTRUçãO CIVIL. ESTE ESTUDO AVALIA A INFLUêNCIA DA SUBSTITUIçãO DA ARGILA NATURAL POR ARGILA CALCINADA NA RESISTêNCIA à COMPRESSãO DE ARGAMASSAS. FORAM COMPARADAS TRêS FORMULAçõES: UMA ARGAMASSA DE REFERêNCIA, UMA COM ARGILA EM SEU ESTADO NATURAL E OUTRA COM ARGILA CALCINADA A 600 °C. OS RESULTADOS INDICAM QUE A CALCINAçãO DA ARGILA A 600 °C, APESAR DE PROMOVER MAIOR REATIVIDADE POZOLâNICA, ACARRETA UMA CONSIDERáVEL PERDA DE PLASTICIDADE E ORIGINA UMA PREDISPOSIçãO AO IMPEDIMENTO DA AGLOMERAçãO DO CIMENTO E AO MATERIAL CALCINADO NA MATRIZ CIMENTíCIA, RESULTANDO EM UMA REDUçãO SIGNIFICATIVA DA RESISTêNCIA à COMPRESSãO

CLAY IS A NATURAL MATERIAL THAT HAS BEEN USED SINCE ANCIENT TIMES FOR CONSTRUCTION AND HOUSING DEVELOPMENT. ITS WIDESPREAD USE IS DUE TO ITS UNIQUE PHYSICAL AND CHEMICAL PROPERTIES, WHICH MAKE IT AN ECONOMICAL AND ACCESSIBLE ALTERNATIVE DUE TO ITS UNIQUE PHYSICAL AND CHEMICAL PROPERTIES, AS WELL AS ITS ABUNDANCE AND LOW COST. IN ADDITION, CLAY CONTRIBUTES TO THE SUSTAINABILITY OF THE SECTOR, ESPECIALLY WHEN USED AS A SUPPLEMENTARY CEMENTITIOUS MATERIAL, PARTIALLY REPLACING PORTLAND CEMENT AND REDUCING THE CARBON FOOTPRINT. THE USE OF CLAYS, WHETHER IN THEIR NATURAL STATE OR SUBJECTED TO HEAT TREATMENT (CALCINATION), HAS BEEN THE SUBJECT OF GROWING INTEREST DUE TO THEIR ABUNDANCE, LOW COST AND SUSTAINABLE POTENTIAL. IN GENERAL TERMS, CLAY PROMOTES AN INCREASE IN THE PLASTICITY OF MORTARS WHEN IN ITS NATURAL STATE, HOWEVER, IN ITS CALCINED STATE, THE HIGHER THE TEMPERATURE OF THE HEAT TREATMENT, THE LOWER ITS PLASTICITY. THESE BENEFITS MAKE CLAY A RECURRENT AND EFFICIENT CHOICE IN VARIOUS CONSTRUCTION APPLICATIONS. THIS STUDY EVALUATES THE INFLUENCE OF REPLACING NATURAL CLAY WITH CALCINED CLAY ON THE COMPRESSIVE STRENGTH OF MORTARS. THREE FORMULATIONS WERE COMPARED: A REFERENCE MORTAR, ONE WITH CLAY IN ITS NATURAL STATE AND ANOTHER WITH CLAY CALCINED AT 600 °C. THE RESULTS INDICATE THAT CALCINING THE CLAY AT 600 °C, DESPITE PROMOTING GREATER POZZOLANIC REACTIVITY, DOES NOT AFFECT THE COMPRESSIVE STRENGTH OF THE MORTAR.

Palavras-chave

Argila; Argila Calcinada; Materiais de Construção; Propriedades

Clay; Calcined Clay; Building materials; Properties.

Como citar

PINHEIRO, VALBER DOMINGOS; ABREU, RAMON FERNANDES DE; FONSECA, LETÍCIA ABREU DA; AZEVEDO, AFONSO RANGEL GARCEZ DE; ALEXANDRE, JONAS. A INFLUÊNCIA DA PERDA DA PLASTICIDADE DE UMA ARGILA CAULINÍTICA POR CALCINAÇÃO NA RESISTÊNCIA À COMPRESSÃO DE ARGAMASSAS , p. 2957-2967. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-41323