AN INVESTIGATION ON FRICTION SPOT WELDING IN AA6181-T4 ALLOY

INVESTIGAÇÃO DO PROCESSO DE SOLDAGEM POR FRICÇÃO POR PONTO PARA A LIGA AA6181-T4

Autoria

Parra, Bruno; Saccon, Vinícius Toledo; Alcântara, Nelson Guedes de; Rosendo, Tonilson; Santos, Jorge Fernandes dos

DOI

10.5151/2594-5327-16497

Downloads

Baixar Artigo 28 Downloads

Resumo

Friction spot welding is a new solid state welding process, invented and patented by the GKSS Research Centre GmbH in Germany, suitable for spot joining lightweight low melting point materials such as Al and Mg alloys. The process is performed with an especially designed rotating tool (comprised by a clamping ring, sleeve, and pin) that creates a joint between sheets in overlap configuration by means of frictional heat and mechanical work. The result is a spot welded lap joint with minimal material loss and a flat surface with no keyhole. In this work the application of Friction Spot Welding for spot joining the Al alloy 6181-T4 was investigated. Different rotational speeds (1900 to 2900 rpm) and welding times (2 to 3.4 s) were tested with the objective of finding the best suited ones for producing high quality joints in terms of microstructure and mechanical performance. The mechanical behavior of the joints was investigated by means of shear tensile tests and the final microstructure was assessed using OM and micro hardness measurements. Welds with strength in the order of 6.8 kN were obtained with high reproducibility. The results also showed that geometric elements of the weld play an important role on the fracture mechanisms and hence on the mechanical performance of the joints. In sum, the results revealed the potential of this process for industrial applications.

 

Friction Spot Welding (FSpW) é um processo de solda ponto no estado sólido recentemente desenvolvido no Centro de Pesquisas alemão GKSS. Este processo tem mostrado grande potencial de aplicação frente aos já estabelecidos RSW (automotivo) e rebitagem (aeronáutico). Neste trabalho pretende-se estudar a aplicabilidade deste novo processo para a produção de juntas sobrepostas da liga Al 6181-T4. Esta é uma liga Al-Si-Mg, endurecida por precipitação, que já tem utilização implementada na indústria automobilística. As amostras soldadas foram submetidas a diferentes ensaios mecânicos, além de medições de microdureza para investigação do desempenho mecânico da solda. Análises micro-estruturais utilizando microscopia óptica também foram realizadas, a fim de determinar o efeito dos parâmetros de solda na qualidade micro-estrutural da solda, tão quanto em eventuais defeitos e um estudo de análise de falha visando o entendimento dos mecanismos de fratura, correlacionando-os com os parâmetros de processo.

Palavras-chave

Joining; Welding; Friction spot welding; Aluminum alloy.

União por fricção; Alumínio; Soldagem.