ANÁLISE DA HOMOGENIZAÇÃO DO NIÓBIO NA LIGA DE ALUMÍNIO 5052F PELO FORJAMENTO PROVOCADO PELO PROCESSO FRICTION STIR WELDING

HOMOGENIZATION ANALYSIS FROM NIOBIUM IN THE ALUMINIUM ALLOY THROUGH THE FORGING CAUSED FOR THE FRICTION STIR WELDING PROCESS.

DOI

10.5151/1516-392X-30863

Downloads

Baixar Artigo 470 Downloads

Resumo

O presente artigo apresenta um estudo sobre a mistura do nióbio em chapas de alumínio pelo processo Friction Stir Welding (FSW), levando em consideração o efeito de forjamento envolvido na soldagem. O processo FSW, consiste em utilizar uma ferramenta rotativa que em contato com o material a ser soldado gera atrito, provocando aumento de temperatura e deformação plástica. O aquecimento gerado é abaixo do ponto de fusão dos materiais envolvidos, por isso é considerado como solda em estado sólido. Para alcançar os objetivos desta pesquisa, conta-se com a colaboração da Companhia Brasileira de Metalurgia e Mineração (CBMM), que forneceu amostras de Nióbio Metálico em cavaco para proceder aos experimentos deste artigo. A amostra adquirida foi triturada manualmente, em seguida, cominuido em moinho de bola para obtê-lo em forma de pó, viabilizando, assim, a inserção na junta a ser soldada. O nióbio foi colocado entre dois metais de base de Al-Mg 5052F que foi soldado pelo processo FSW, em uma máquina adaptada para esse processo. Após a soldagem foi feito a metalografia na seção transversal onde observou-se uma boa mistura do nióbio no metal soldado. Além disso, foi analisado a microestrutura formada e a composição química através do microscópio eletrônico de varredura (MEV).

 

This article presents study about the features of the Niobium and its introduction on the Aluminum sheets by the Friction Stir Welding (FSW), taking account the forging effect involved in welding. The FSW process, where we can call of friction welding with a non-consumable pin, it consists on utilizes a rotary tool which in contact with the stuff to be welded creates friction, causing heat and plastic deformation. This heat is below from the melting point of the stuff involved, so it’s considered as solid state welding. For achieve the goals of this research, it’s necessary the collaboration of the “Companhia Brasileira de Metalurgia e Mineração” (CBMM), that provides samples of Metal Niobium chips which proceeded the experiments of this article. The acquired sample was crushed by hand, then, it was comminuted in a ball mill to obtain it in powder form, in this way enabling the insertion on the point to be welded. The Niobium was put between two base metals, then it was welded by the FSW process. After welding, it was done the metallography in the transversal section, where was observed a satisfactory mixture in the metal welded. Besides that, it was verified microstructure formed and chemical composition by scanning electron microscopy (SEM).

Palavras-chave

Soldagem, Friction Stir Welding, Nióbio, Microscopia Eletrônica de Varredura.

Welding, Friction Stir welding, Niobium, Scanning electron microscopy (SEM).

Como citar

Boas, Gabriel Pessoa Vilas; Assunção, Paulo D’angelo Costa; Cardoso, Ivone Thatianne de Abreu dos Passos; Portal, Paulo Sérgio da Silva; Silva, Elenildo Barros da. ANÁLISE DA HOMOGENIZAÇÃO DO NIÓBIO NA LIGA DE ALUMÍNIO 5052F PELO FORJAMENTO PROVOCADO PELO PROCESSO FRICTION STIR WELDING , p. 3226-3236. In: 72nd ABM Annual Congress, São Paulo, 2017.