Título

ANÁLISE COMPARATIVA DA RESISTÊNCIA A FLEXÃO DE COMPÓSITO EPOXÍDICO HÍBRIDO AÇAÍ E CHAMOTE

COMPARATIVE ANALYSIS OF FLEXURAL RESISTANCE OF HYBRID EPOXYDE COMPOSITES REINFORCED WITH AÇAÍ FIBER AND CHAMOTTE

Autoria

OLIVEIRA, JAQUELINE MOREIRA DE

OLIVEIRA, JAQUELINE MOREIRA DE

Eu sou esse autor

DOI

10.5151/2594-5327-41434

Downloads

Resumo

COM O PASSAR DOS ANOS E A EVOLUçãO INDUSTRIAL E POPULACIONAL TORNOU-SE ESSENCIAL O ESTUDO ENVOLTO DE MATERIAIS REFORçADOS COM FIBRAS VEGETAIS, E TEM SE TORNADO DESTAQUE NAS PESQUISAS E NAS POSSIBILIDADES DE IMPLEMENTAçãO NA INDúSTRIA. O OBJETIVO DESTA PESQUISA é FAZER UM ESTUDO DE COMO O COMPóSITO EPOXíDICO HíBRIDO REFORçADO COM AçAí E CHAMOTE SE COMPORTA NO ENSAIO MECâNICO DE FLEXãO E COMPARAR OS RESULTADOS COM O ENSAIO DE FLEXãO COM RESINA PURA, PARA ANALISAR A VIABILIDADE DA UTILIZAçãO COMO REFORçO. PORTANTO, FORAM PREPARADOS SEIS TIPOS DE COMBINAçõES DE FORMULAçõES DOS COMPóSITOS HíBRIDOS INCORPORADOS A RESINA EPóXI COM UM SISTEMA DGEBA/DETA COM O PHR DE 16, SENDO ELES 5% DE AçAí COM 5% DE CHAMOTE, 10% DE AçAí E 5% DE CHAMOTE, 15% DE AçAí E 5% DE CHAMOTE, 5% DE AçAí COM 10% DE CHAMOTE, 10% DE AçAí E 10% DE CHAMOTE, 5% DE AçAí E 15% DE CHAMOTE. UTILIZAMOS A NORMA ASTM D790 COMO SUPORTE PARA O ENSAIO, A UMA TAXA DE 1MM/MIN.

OVER THE YEARS AND WITH INDUSTRIAL AND POPULATION EVOLUTION, THE STUDY OF MATERIALS REINFORCED WITH VEGETABLE FIBERS HAS BECOME ESSENTIAL AND HAS BECOME A HIGHLIGHT IN RESEARCH AND IN THE POSSIBILITIES OF IMPLEMENTATION IN INDUSTRY. THE OBJECTIVE OF THIS RESEARCH IS TO STUDY HOW THE HYBRID EPOXY COMPOSITE REINFORCED WITH AçAí AND CHAMOTTE BEHAVES IN THE MECHANICAL FLEXION TEST AND COMPARE THE RESULTS WITH THE FLEXION TEST WITH PURE RESIN, TO ANALYZE THE FEASIBILITY OF USING IT AS REINFORCEMENT. THEREFORE, SIX TYPES OF COMBINATIONS OF HYBRID COMPOSITE FORMULATIONS INCORPORATED INTO EPOXY RESIN WITH A DGEBA/DETA SYSTEM WITH A PHR OF 16 WERE PREPARED, BEING 5% AçAí WITH 5% CHAMOTTE, 10% AçAí AND 5% CHAMOTTE, 15% AçAí AND 5% CHAMOTE, 5% AçAí WITH 10% CHAMOTE, 10% AçAí AND 10% CHAMOTE, 5% AçAí AND 15% CHAMOTE. WE USED THE ASTM D790 STANDARD AS SUPPORT FOR THE TEST, AT A RATE OF 1MM/MIN.

Palavras-chave

Fibra de açaí; Chamote; Compósitos; Resina epóxi, Flexão.

Acai fiber; Chamotte ; Composites; Epoxy resin, Flexural.