Resumo
O USO DE FIBRAS LIGNOCELULÓSICAS EM COMPÓSITOS POLIMÉRICOS É UMA ALTERNATIVA QUE PODE TRAZER CONTRIBUIÇÕES NAS ESFERAS ECONÔMICAS, AMBIENTAIS E TÉCNICAS QUANDO COMPARADOS COM OS COMPÓSITOS REFORÇADOS COM FIBRAS DE VIDRO. O OBJETIVO DESSE TRABALHO ESTUDO É COMPARAR COMPÓSITOS EPOXÍDICA REFORÇADOS COM TECIDOS DE JUTA COM COMPÓSITOS DE FIBRA DE VIDRO. NESTE SENTIDO, FORAM PREPARADOS CORPOS DE PROVA COMPARANDO A RESISTÊNCIA A FLEXÃO DA RESINA PURA (DGEBA/TETA) COM OS COMPÓSITOS REFORÇADOS COM TECIDO DE FIBRA DE VIDRO E OS REFORÇADOS COM TECIDO DE FIBRA DE JUTA. O ENSAIO FOI REALIZADO CONFORME A ASTM D790, A UMA TAXA DE 2MM/MIN. AS PROPRIEDADES DA RESINA EPÓXI E DOS COMPÓSITOS PRODUZIDOS FORAM AVALIADOS ESTATISTICAMENTE POR MEIO DE ANÁLISE POR VARIÂNCIA (ANOVA) E TESTE DE TUKEY. OS RESULTADOS INDICARAM QUE OS COMPÓSITOS DE TECIDO DE VIDRO E DE JUTA OBTIVERAM UM GANHO NO MÓDULO DE ELASTICIDADE EM RELAÇÃO A RESINA EPÓXI. ENTRETANTO, DIFERENTE DO TECIDO DE FIBRA DE VIDRO, A PRESENÇA DO TECIDO DE FIBRA DE JUTA NÃO COLABOROU PARA UMA ELEVAÇÃO NO LIMITE DE RESISTÊNCIA À FLEXÃO.
THE USE OF LIGNOCELLULOSIC FIBERS IN POLYMER COMPOSITES IS AN ALTERNATIVE THAT CAN BRING CONTRIBUTIONS IN ECONOMIC, ENVIRONMENTAL AND TECHNICAL SPHERES WHEN COMPARED TO COMPOSITES REINFORCED WITH GLASS FIBERS. THE AIM OF THIS STUDY IS TO COMPARE EPOXY COMPOSITES REINFORCED WITH JUTE FABRICS WITH FIBERGLASS COMPOSITES. THUS, SPECIMENS WERE PREPARED COMPARING THE FLEXURAL STRENGTH OF PURE RESIN (DGEBA/TETA) WITH COMPOSITES REINFORCED WITH FIBERGLASS FABRIC AND THOSE REINFORCED WITH JUTE FIBER FABRIC. THE TEST WAS PERFORMED IN ACCORDANCE WITH ASTM D790, AT A RATE OF 2MM/MIN. THE PROPERTIES OF THE EPOXY RESIN AND THE COMPOSITES PRODUCED WERE STATISTICALLY EVALUATED USING ANALYSIS BY VARIANCE (ANOVA) AND TUKEY'S TEST. THE RESULTS INDICATED THAT THE GLASS AND JUTE FABRIC COMPOSITES OBTAINED A GAIN IN THE MODULUS OF ELASTICITY IN RELATION TO EPOXY RESIN. HOWEVER, UNLIKE THE FIBERGLASS FABRIC, THE PRESENCE OF THE FIBERGLASS FABRIC DID NOT CONTRIBUTE TO AN INCREASE IN THE FLEXURAL STRENGTH LIMIT.
Palavras-chave
Compósitos; Fibra de Juta; Fibra de Vidro; Epóxi
Composites; Jute fiber; Fiberglass; Epoxy
Como citar
Velasco, David Coverdale Rangel;
Moreira, Mariane Oliveira;
Alves, Gustavo Maciel Rodrigues;
Duarte, Felipe Perissé;
Simonassi, Noan Tonini;
Monteiro, Sergio Neves;
Vieira, Carlos Maurício Fontes;
Loiola, Rômulo Leite.
ANÁLISE COMPARATIVA DA RESISTÊNCIA A FLEXÃO DE COMPÓSITOS EPOXÍDICOS REFORÇADOS COM TECIDO DE JUTA E COM TECIDO DE VIDRO
,
p. 2868-2876.
In: 75° Congresso Anual da ABM,
São Paulo,
2022.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-34697