ANÁLISE DA CORROSÃO POR PITES DO AÇO INOXIDÁVEL DUPLEX S31803 SUBMETIDO AO MEIO CORROSIVO

PITTING CORROSION ANALYSIS OF STAINLESS STEEL DUPLEX S31803 SUBMITTED TO THE CORROSIVE MEDIA

DOI

10.5151/2594-5327-33832

Downloads

Baixar Artigo 327 Downloads

Resumo

Neste trabalho foi analisada a influência do meio corrosivo e da temperatura na propriedade de resistência a corrosão do aço inoxidável duplex S31803. O processo corrosivo foi realizado em duas amostragens, utilizando solução de ácido clorídrico 1,5% a temperatura ambiente e a mesma solução a temperatura de 50ºC. A microestrutura da amostra conforme recebida foi analisada antes e após processo corrosivo utilizando a técnica de microscopia confocal. Em seguida, foram realizados os ensaios mecânicos de dureza e determinadas às taxas de corrosão, a fim de analisar a resistência do aço ao meio corrosivo. Verificou-se que a amostra conforme recebida (CR) apresenta uma microestrutura constituída de uma dupla fase, sendo uma a ferrita e a outra a austenita em proporções de 50% cada uma. Foi evidenciado que o aço inoxidável duplex S31803 após o processo corrosivo (APC) na temperatura de 25ºC manteve os mesmos limites de resistência à tração, ductilidade e também tenacidade em relação a amostra conforme recebida. Porém quando submetido ao meio corrosivo a temperatura de 50ºC houve uma diminuição nos valores de suas propriedades, justificando assim uma maior taxa de corrosão quando submetido ao meio de ácido clorídrico a 50ºC.

 

In this work the influence of the corrosive medium and the temperature on the corrosion resistance property of the duplex stainless steel S31803 was analyzed. The corrosive process was carried out in two samples using 1.5% hydrochloric acid solution at room temperature and the same solution at 50ºC. The microstructure of the sample as received was analyzed before and after a corrosive process using the confocal microscopy technique. Then, the hardness, tensile tests were carried out to determine the mechanical properties and the corrosion rate, in order to analyze the corrosion resistance. It was verified that the sample as received presents a microstructure consisting of a double phase, one being the ferrite and the other the austenite in proportions of 50% each. It was evidenced that the duplex stainless steel S31803 after the corrosive process in the temperature of 25ºC maintained the same limits of tensile strength, ductility and also tenacity in relation to the sample as received. However, when subjected to the corrosive medium at 50ºC, there was a decrease in the values of its properties, thus justifying a higher corrosion rate when submitted to the hydrochloric acid medium at 50ºC.

Palavras-chave

Duplex; Corrosão; Dureza; Tração

Duplex; Corrosion; Toughness; Tension.