ANÁLISE DA INFLUÊNCIA DA TRANSFORMAÇÃO DE FASE NA OVALIZAÇÃO DE BOBINAS LAMINADAS A QUENTE

ANALYSIS OF THE INFLUENCE OF PHASE TRANSFORMATION ON COIL SLUMP OF HOT ROLLED COILS'

Autoria

Andrade, Saulo Morais de

Andrade, Saulo Morais de

Eu sou esse autor

DOI

10.5151/2594-5297-34950

Downloads

Resumo

A LAMINAÇÃO A QUENTE É UM PROCESSO TERMOMECÂNICO CARACTERIZADO PELA AUSTENITIZAÇÃO DURANTE O REAQUECIMENTO DE PLACAS, SEGUIDO DAS ETAPAS DE LAMINAÇÃO E RESFRIAMENTO. UMA IMPORTANTE ETAPA DESTE PROCESSO É A DECOMPOSIÇÃO, OU TRANSFORMAÇÃO, DA AUSTENITA DURANTE O RESFRIAMENTO. É SABIDO QUE QUANDO ESTA TRANSFORMAÇÃO NÃO É COMPLETADA, AO MENOS EM SUA MAIORIA, ANTERIOR AO BOBINAMENTO, EXISTE UMA MAIOR TENDÊNCIA À OVALIZAÇÃO. ESTE COMPORTAMENTO É EXPLICADO PELA ALTERAÇÃO VOLUMÉTRICA INERENTE À DECOMPOSIÇÃO DA AUSTENITA. A OVALIZAÇÃO É UM DEFEITO CRÍTICO, POIS DEPENDENDO DE SUA MAGNITUDE AS BOBINAS NÃO PODEM SER ENVIADAS À PROCESSOS SUBSEQUENTES OU CLIENTES. O ARTIGO APRESENTA UMA CARACTERIZAÇÃO LABORATORIAL DA TRANSFORMAÇÃO DE FASE DURANTE O RESFRIAMENTO, PARA MELHOR COMPREENDER A OCORRÊNCIA DE OVALIZAÇÃO EM UM AÇO MÉDIO CARBONO, E UMA AVALIAÇÃO BASEADA EM DADOS INDUSTRIAS DE OVALIZAÇÃO EM AÇOS COM CARBONO EM TORNO DE 0,10%, COM E SEM ADIÇÃO DE NIÓBIO, EM FUNÇÃO DA TEMPERATURA DE BOBINAMENTO. PARA ANALISAR OS DADOS INDUSTRIAIS, A EQUAÇÃO DE CHOO FOI UTILIZADA PARA DETERMINAR A TEMPERATURA AR3 PARA INFERIR A INFLUÊNCIA DA TRANSFORMAÇÃO DE FASE. FOI CONFIRMADO QUE A TRANSFORMAÇÃO DE FASE PODE SER CONSIDERADA COMO UM FATOR DETERMINANTE NA OVALIZAÇÃO DE BOBINAS LAMINADAS A QUENTE.

THE HOT ROLLING IS A THERMOMECHANICAL PROCESS CHARACTERIZED BY THE AUSTENITIZATION DURING THE REHEATING OF SLABS, FOLLOWED BY ROLLING AND COOLING STEPS. AN IMPORTANT STEP OF THIS PROCESS IS THE DECOMPOSITION, OR TRANSFORMATION, OF AUSTENITE DURING COOLING. IT IS KNOWN THAT WHEN THIS TRANSFORMATION IS NOT COMPLETED, OR AT LEAST IN ITS MAJORITY, PRIOR THE COILING, THERE IS A HIGHER TENDENCY OF COIL SLUMP. THIS BEHAVIOR IS EXPLAINED BY THE VOLUMETRIC CHANGE INHERENT OF AUSTENITE DECOMPOSITION. COIL SLUMP IS A CRITICAL DEFECT BECAUSE DEPENDING ON ITS MAGNITUDE, THE COILS CANNOT BE SENT TO SUBSEQUENT PROCESSES OR CUSTOMER. THE PAPER PRESENTS A LABORATORY CHARACTERIZATION OF THE PHASE TRANSFORMATION DURING COOLING TO BETTER UNDERSTAND THE OCCURRENCE OF COIL SLUMP IN A MEDIUM CARBON STEEL AND AN EVALUATION BASED ON INDUSTRIAL DATA OF COIL SLUMP IN STEELS WITH CARBON CONTENT NEAR TO 0.10%, WITH AND WITHOUT MICROALLOYING ELEMENTS, AS A FUNCTION OF COILING TEMPERATURE. TO ANALYZE THE INDUSTRIAL DATA, THE CHOO EQUATION WAS USED TO DETERMINE AR3 TEMPERATURE TO INFER THE INFLUENCE OF PHASE TRANSFORMATION. IT WAS CONFIRMED THAT PHASE TRANSFORMATION CAN BE ASSOCIATED AS A DETERMINING FACTOR IN THE COIL SLUMP OF HOT ROLLED COILS.

Palavras-chave

aço laminado a quente; transformação de fase; ovalização.

Hot Rolled Steel; Phase Transformation; Coil Slump.