ANÁLISE DA INFLUÊNCIA DA VELOCIDADE DE IMPRESSÃO NAS PROPRIEDADES MECÂNICAS DE SCAFFOLDS MANUFATURADOS POR FDM: ANALYSIS OF THE INFLUENCE OF PRINTING SPEED ON THE MECHANICAL PROPERTIES OF SCAFFOLDS MANUFACTURED BY FDM

ESSE ESTUDO INVESTIGA A INFLUêNCIA DA VELOCIDADE DE IMPRESSãO EM SCAFFOLDS MANUFATURADOS POR FDM. FORAM DESENHADOS DOIS MODELOS DISTINTOS NO SOFTWARE CREO PARAMETRIC 10.0.0.0, OS MODELOS FORAM IMPRESSOS PELA IMPRESSORA ENDER 3 V3 SE DA CREALITY COM VARIAçãO DE VELOCIDADE EM 20 MM/S E 60 MM/S; ENSAIADOS POR COMPRESSãO ATRAVéS MáQUINA UNIVERSAL DE ENSAIOS IM-50 DA INTERMETRIC. OS RESULTADOS REVELARAM MóDULO DE COMPRESSãO DE 0,177 GPA E 0,166 GPA PARA AS AMOSTRAS MANUFATURADAS A 20 MM/S E MóDULOS DE 0,130 GPA E 0,154 GPA PARA AS AMOSTRAS IMPRESSAS A 60 MM/S. A RESISTêNCIA A COMPRESSãO OBTIDA FORAM DE 5,296 MPA - 4,895 MPA E 4,248 MPA - 4,564 MPA, RESPECTIVAMENTE, PARA AS AMOSTRAS IMPRESSAS A 20 MM/S E 60 MM/S. A ANáLISE ESTATíSTICA REVELOU QUE A VELOCIDADE NãO FOI O PRINCIPAL AGENTE RESPONSáVEL PELA DIMINUIçãO DAS PROPRIEDADES MECâNICAS DO MATERIAL.

THIS STUDY INVESTIGATES THE INFLUENCE OF PRINTING SPEED ON SCAFFOLDS MANUFACTURED BY FDM. TWO DISTINCT MODELS WERE DESIGNED IN THE CREO PARAMETRIC 10.0.0.0 SOFTWARE; THE MODELS WERE PRINTED BY THE CREALITY ENDER 3 V3 SE PRINTER WITH SPEED VARIATION OF 20 MM/S AND 60 MM/S; THEY WERE TESTED BY COMPRESSION USING THE INTERMETRIC IM-50 UNIVERSAL TESTING MACHINE. THE RESULTS REVEALED COMPRESSIVE MODULUS OF 0.177 GPA AND 0.166 GPA FOR THE SAMPLES MANUFACTURED AT 20 MM/S AND MODULI OF 0.130 GPA AND 0.154 GPA FOR THE SAMPLES PRINTED AT 60 MM/S. THE COMPRESSIVE STRENGTH OBTAINED WERE 5.296 MPA - 4.895 MPA AND 4.248 MPA - 4.564 MPA, RESPECTIVELY, FOR THE SAMPLES PRINTED AT 20 MM/S AND 60 MM/S. STATISTICAL ANALYSIS REVEALED THAT SPEED WAS NOT THE MAIN AGENT RESPONSIBLE FOR THE DECREASE IN THE MECHANICAL PROPERTIES OF THE MATERIAL.

Palavras-chave

Scaffold; Impressão 3D; Manufatura aditiva; ASTM D695

Scaffold; 3D printing; Additive manufacturing; ASTM D695

Como citar

SOARES, EDSON MIRANDA; CONCEIÇÃO, ANA BEATRIZ DAS NEVES; PINHEIRO, MIRIANE ALEXANDRINO; NASCIMENTO, DAMARES DA CRUZ BARBOSA; SILVA, ALISSON CLAY RIOS DA; CANDIDO, VERÔNICA SCARPINI. ANÁLISE DA INFLUÊNCIA DA VELOCIDADE DE IMPRESSÃO NAS PROPRIEDADES MECÂNICAS DE SCAFFOLDS MANUFATURADOS POR FDM , p. 2735-2745. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-41289