Título

ANÁLISE DA INFLUÊNCIA DE ADITIVOS E RESÍDUO DE VIDRO NA PLASTICIDADE DE MASSAS CERÂMICAS UTILIZANDO O MÉTODO DE PFEFFERKORN

ANALYSIS OF THE INFLUENCE OF ADDITIVES AND GLASS WASTE ON THE PLASTICITY OF CERAMIC MASSES USING THE PFEFFERKORN METHOD

Autoria

FERREIRA, PAULA MUNIER; DELAQUA, GEOVANA CARLA GIRONDI; VIEIRA, CARLOS MAURÍCIO FONTES

FERREIRA, PAULA MUNIER

Eu sou esse autor

DELAQUA, GEOVANA CARLA GIRONDI

Eu sou esse autor

VIEIRA, CARLOS MAURÍCIO FONTES

Eu sou esse autor

DOI

10.5151/2594-5327-40786

Downloads

Resumo

A FORMULAçãO DE MASSAS CERâMICAS REQUER UM LONGO PROCESSO DE PESQUISA E TESTES PARA SE ALCANçAR A COMPOSIçãO IDEAL. NA CONFORMAçãO DOS PRODUTOS CERâMICOS, ESPECIALMENTE NA EXTRUSãO, A PLASTICIDADE é CRUCIAL, DETERMINANDO A ADAPTABILIDADE DA MASSA. ADITIVOS COMO PLASTIFICANTES E DEFLOCULANTES SãO UTILIZADOS PARA MELHORAR A PLASTICIDADE, GARANTINDO UM FLUXO IDEAL. ESTE ESTUDO ANALISA O IMPACTO DE DIFERENTES ADITIVOS NA PLASTICIDADE DAS MASSAS CERâMICAS, VISANDO REDUZIR A QUANTIDADE DE áGUA NECESSáRIA PARA A CONFORMAçãO. TAMBéM SE INVESTIGOU A INCLUSãO DE RESíDUO DE VIDRO NA MASSA, UMA VEZ QUE A INDúSTRIA CERâMICA SE DESTACA PELO APROVEITAMENTO DE RESíDUOS. FORMULAçõES FORAM DESENVOLVIDAS COM MASSA ARGILOSA, RESíDUO DE VIDRO E QUATRO TIPOS DE ADITIVOS: AMIDO DE MILHO, SILICATO DE SóDIO, CMC E áCIDO CíTRICO. OS RESULTADOS DESTACARAM QUE TODOS OS ADITIVOS, COM EXCEçãO DO CMC, DIMINUíRAM A UMIDADE E A PLASTICIDADE EM COMPARAçãO COM A MASSA 0 (REFERêNCIA), SENDO O áCIDO CíTRICO O MAIS EFICAZ. ALéM DISSO, TAMBéM SE EVIDENCIOU O POTENCIAL DO VIDRO, QUE EM TODOS OS CASOS CONTRIBUIU PARA DIMINUIçãO DA PLASTICIDADE DAS MASSAS E, CONSEQUENTEMENTE, DA QUANTIDADE DE áGUA NECESSáRIA.

THE FORMULATION OF CERAMIC MASSES REQUIRES A LONG PROCESS OF RESEARCH AND TESTING TO ACHIEVE THE IDEAL COMPOSITION. IN THE SHAPING OF CERAMIC PRODUCTS, ESPECIALLY IN EXTRUSION, PLASTICITY IS CRUCIAL, DETERMINING THE ADAPTABILITY OF THE MASS. ADDITIVES SUCH AS PLASTICIZERS AND DEFLOCCULANTS ARE USED TO IMPROVE PLASTICITY, ENSURING OPTIMAL FLOW. THIS STUDY ANALYZES THE IMPACT OF DIFFERENT ADDITIVES ON THE PLASTICITY OF CERAMIC MASSES, AIMING TO REDUCE THE AMOUNT OF WATER REQUIRED FOR FORMING. THE INCLUSION OF GLASS WASTE IN THE MASS WAS ALSO INVESTIGATED, SINCE THE CERAMIC INDUSTRY STANDS OUT FOR ITS USE OF WASTE. FORMULATIONS WERE DEVELOPED WITH CLAY MASS, GLASS WASTE AND FOUR TYPES OF ADDITIVES: CORN STARCH, SODIUM SILICATE, CMC AND CITRIC ACID. THE RESULTS HIGHLIGHTED THAT ALL ADDITIVES, WITH THE EXCEPTION OF CMC, REDUCED MOISTURE AND PLASTICITY COMPARED TO MASS 0 (REFERENCE), WITH CITRIC ACID BEING THE MOST EFFECTIVE. FURTHERMORE, THE POTENTIAL OF GLASS WAS ALSO HIGHLIGHTED, WHICH IN ALL CASES CONTRIBUTED TO REDUCING THE PLASTICITY OF THE MASSES AND, CONSEQUENTLY, THE AMOUNT OF WATER REQUIRED.

Palavras-chave

Massa cerâmica; Plasticidade; Aditivos; Resíduo de vidro.

Clay mass; Plasticity; Additives; Glass waste.