ANÁLISE DA RESISTÊNCIA À COMPRESSÃO DO COLMO DE SORGO VASSOURA COM POSSÍVEL APLICAÇÃO EM MATERIAIS COMPÓSITOS: ANALYSIS OF THE COMPRESSION RESISTANCE OF BROOMCORN SORGHUM STALK WITH POTENTIAL APPLICATION IN COMPOSITE MATERIALS

NOS úLTIMOS ANOS, O INTERESSE POR MATERIAIS SUSTENTáVEIS E BIODEGRADáVEIS TEM CRESCIDO, IMPULSIONANDO PESQUISAS EM COMPóSITOS REFORçADOS COM FIBRAS NATURAIS. O SORGO VASSOURA (SORGHUM BICOLOR) FOI O OBJETO DE ESTUDO DESTE TRABALHO PRINCIPALMENTE PELA SUA BAIXA DENSIDADE. ESTE ESTUDO TEVE COMO OBJETIVO INVESTIGAR O COMPORTAMENTO MECâNICO DO COLMO DE SORGO VASSOURA, USANDO ENSAIOS DE COMPRESSãO PARA DETERMINAR A RESISTêNCIA à COMPRESSãO E O MóDULO DE ELASTICIDADE. O ENSAIO DE COMPRESSãO FOI UTILIZADO PARA AVALIAR O COMPORTAMENTO DO COLMO, CASCA E NúCLEO DO SORGO VASSOURA SOB CARGAS COMPRESSIVAS SEPARADAMENTE. OS RESULTADOS MOSTRARAM QUE A CASCA APRESENTOU A MAIOR RESISTêNCIA, SEGUIDO PELO COLMO COMPLETO E NúCLEO. A CASCA DEMONSTROU UM COMPORTAMENTO FRáGIL, ENQUANTO O NúCLEO FOI MAIS MALEáVEL. O COLMO COMPLETO APRESENTOU UM COMPORTAMENTO INTERMEDIáRIO, COM UMA BOA RESISTêNCIA INICIAL DEVIDO à CASCA, SEGUIDA POR TRINCAS QUE REDUZEM TEMPORARIAMENTE A RESISTêNCIA, SEGUIDA PELA COMPACTAçãO DO MATERIAL QUE AUMENTA NOVAMENTE A RESISTêNCIA. EM GERAL, OS VALORES DE RESISTêNCIA DO COLMO COMPLETO FORAM SIGNIFICATIVOS, CONFIRMANDO SEU POTENCIAL COMO REFORçO EM COMPóSITOS POLIMéRICOS.

IN RECENT YEARS, INTEREST IN SUSTAINABLE AND BIODEGRADABLE MATERIALS HAS GROWN, DRIVING RESEARCH INTO COMPOSITES REINFORCED WITH NATURAL FIBERS. BROOMCORN (SORGHUM BICOLOR) WAS THE SUBJECT OF THIS STUDY PRIMARILY DUE TO ITS LOW DENSITY. THE AIM OF THIS STUDY WAS TO INVESTIGATE THE MECHANICAL BEHAVIOR OF BROOMCORN STALKS USING COMPRESSION TESTS TO DETERMINE COMPRESSIVE STRENGTH AND MODULUS OF ELASTICITY. COMPRESSION TESTS WERE USED TO EVALUATE THE BEHAVIOR OF THE STALK, BARK, AND CORE OF BROOMCORN SEPARATELY UNDER COMPRESSIVE LOADS. THE RESULTS SHOWED THAT THE BARK EXHIBITED THE HIGHEST STRENGTH, FOLLOWED BY THE WHOLE STALK AND THE CORE. THE BARK DEMONSTRATED BRITTLE BEHAVIOR, WHILE THE CORE WAS MORE DUCTILE. THE WHOLE STALK SHOWED INTERMEDIATE BEHAVIOR, WITH GOOD INITIAL STRENGTH DUE TO THE BARK, FOLLOWED BY CRACKS THAT TEMPORARILY REDUCED STRENGTH, AND THEN MATERIAL COMPACTION THAT INCREASED STRENGTH AGAIN. OVERALL, THE STRENGTH VALUES OF THE WHOLE STALK WERE SIGNIFICANT, CONFIRMING ITS POTENTIAL AS REINFORCEMENT IN POLYMER COMPOSITES.

Palavras-chave

Sorgo vassoura; Ensaio de compressão; Materiais compósitos

Broomcorn sorghum; Compression testing; Composite materials.

Como citar

SATIRO, ANTONIO RICARDO GRIPPA; CARVALHO, EDUARDO ATEM DE; LOPES, FELIPE PERISSÉ DUARTE; SIMONASSI, NOAN TONINI; MONTEIRO, SERGIO NEVES. ANÁLISE DA RESISTÊNCIA À COMPRESSÃO DO COLMO DE SORGO VASSOURA COM POSSÍVEL APLICAÇÃO EM MATERIAIS COMPÓSITOS , p. 1948-1955. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-41021