ANÁLISE DA TENACIDADE AO IMPACTO DO AÇO CARBONO SOLDADO COM ARAME TUBULAR AWS E71T-1

ANALYSIS OF THE IMPACT TO TOUGHNESS OF CARBON STEEL WELDED WITH WIRE TUBULAR AWS E71T-1

DOI

10.5151/2594-5327-21423

Downloads

Baixar Artigo 266 Downloads

Resumo

Foi realizada uma avaliação da tenacidade ao impacto de uma junta de aço carbono soldada com arame tubular AWS E71T-1. Para tal foi soldada uma junta de 55 mm de espessura, material ASTM A516 Gr.70, na posição vertical ascendente. A junta soldada foi dividida em 3 partes, sendo que a Parte 1 foi mantida como soldada, a Parte 2 foi tratada termicamente a 630ºC com um ciclo de 2 h e 30 min, e a Parte 3 a 630ºC mas com um ciclo de 2 h e 30 min mais dois ciclos de 4 h. Foi realizado ensaio de impacto Charpy-V nas 3 partes, e os resultados foram comparados. Além disso, foi realizada avaliação metalúrgica da região fraturada dos corpos de prova, objetivando avaliar possíveis mudanças microestruturais resultantes do TTAT que poderiam influenciar na energia absorvida no ensaio de impacto. Foi verificado que a tenacidade após tratamento térmico de alívio de tensões (TTAT) no metal de solda atingiu valores satisfatórios, visto que não foram detectadas a presença de precipitados de Nb e V, que poderiam influenciar no decréscimo da mesma. Os valores de dureza tiveram uma pequena queda, conforme aumentava o tempo em que o material permanecia sobre o TTAT, levando a um aumento da ductilidade do material.

 

It was performed an assessment of the impact toughness of a joint carbon steel welded with tubular wire AWS E71T-1. For this purpose was welded a joint of 55mm thickness, ASTM A516 Gr.70 material, in a vertically upwards. The welded joint was separated into 3 parts, whereby the Part 1 was maintained as welded, Part 2 was treated heated at 630ºC with a cycle of 2 h and 30 min, and the Part 3 heated at 630ºC but with one cycle of 2 h and 30 min plus two cycles of 4 h. It was performed a Charpy impact test-V in a 3 parts, and the results will be compared. In addition, metallurgical evaluation it was conducted in the region of the fractured specimens, in order to evaluate possible micro structural changes resulting from PWHT that could influence the energy absorbed in the impact test. It was observed that the toughness after heat treatment for setree relief (PWHT) in the weld metal reached satisfactory values, since not detected the presence of precipitated Nb and V, which could influence the decrease thereof. The hardness values were slightly fall with increase in time at wich the material remained on the PWHT, leading to increased ductility of the material.

Palavras-chave

TTAT; Tenacidade; Solda; AWSE71T-1.

TTAT; Toughness; Weld; AWSE71T-1.

Como citar

Junior, José Mauro Moraes; Fari, Maria Ismênia Sodero Toledo; Anjo, Priscila Renata dos Santos dos; Norbert, Rafael Machado. ANÁLISE DA TENACIDADE AO IMPACTO DO AÇO CARBONO SOLDADO COM ARAME TUBULAR AWS E71T-1 , p. 3216-3224. In: 67º Congresso da ABM - Internacional / 12º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, Rio de Jabeiro, 2012.