ANÁLISE DAS CARACTERÍSTICAS DO COLMO DO SORGO VASSOURA COMO POSSÍVEL REFORÇO EM COMPÓSITOS POLIMÉRICOS

ANALYSIS OF THE CHARACTERISTICS OF BROOMCORN STALK AS A POTENTIAL REINFORCEMENT IN POLYMERIC COMPOSITES

DOI

10.5151/2594-5327-41019

Downloads

Baixar Artigo 2 Downloads

Resumo

A DEMANDA POR MATERIAIS SUSTENTáVEIS E DE ALTO DESEMPENHO TEM CRESCIDO BASTANTE, SENDO IMPULSIONADA PELAS PREOCUPAçõES AMBIENTAIS E A NECESSIDADE DE REDUZIR A DEPENDêNCIA DE RECURSOS NãO RENOVáVEIS. NESSE CONTEXTO, OS COMPóSITOS REFORçADOS POR FIBRAS NATURAIS TêM SE DESTACADO COMO ALTERNATIVAS PROMISSORAS. ESTE ESTUDO TEVE COMO OBJETIVO ANALISAR O COLMO DO SORGO VASSOURA (SORGHUM BICOLOR) COMO POTENCIAL REFORçO EM COMPóSITOS POLIMéRICOS, FOCANDO EM SUAS VARIáVEIS DE DIâMETRO, DENSIDADE E CARACTERíSTICAS SUPERFICIAIS. FORAM MEDIDOS OS DIâMETROS DE COLMOS ALEATóRIOS EM TRêS PONTOS AO LONGO DE SEU COMPRIMENTO. A DENSIDADE RELATIVA FOI DETERMINADA POR PICNOMETRIA E A DENSIDADE APARENTE FOI CALCULADA COM BASE NAS DIMENSõES E MASSA DOS COLMOS. ALéM DISSO, FOI REALIZADA UMA ANáLISE SUPERFICIAL UTILIZANDO MICROSCOPIA ELETRôNICA DE VARREDURA (MEV). HOUVE UMA GRANDE VARIAçãO NOS DIâMETROS DOS COLMOS, COM UMA MAIOR CONCENTRAçãO ENTRE 5 E 7 MM. AS DENSIDADES RELATIVA E APARENTE MOSTRARAM VARIAçõES SIGNIFICATIVAS. A ANáLISE SUPERFICIAL REVELOU UMA ESTRUTURA LIGNOCELULóSICA RUGOSA E POROSA, CONTRIBUINDO PARA A BAIXA DENSIDADE E BOA RESISTêNCIA àS CARGAS. O COLMO DO SORGO VASSOURA SE MOSTROU PROMISSOR COMO REFORçO EM COMPóSITOS POLIMéRICOS, COM EXPECTATIVA DE PROPORCIONAR MELHORIAS NAS PROPRIEDADES MECâNICAS E PRODUZIR COMPóSITOS COM BAIXA DENSIDADE.

 

THE DEMAND FOR SUSTAINABLE AND HIGH-PERFORMANCE MATERIALS HAS BEEN GROWING SIGNIFICANTLY, DRIVEN BY ENVIRONMENTAL CONCERNS AND THE NEED TO REDUCE DEPENDENCE ON NON-RENEWABLE RESOURCES. IN THIS CONTEXT, COMPOSITES REINFORCED WITH NATURAL FIBERS HAVE EMERGED AS PROMISING ALTERNATIVES. THIS STUDY AIMED TO ANALYZE THE BROOMCORN (SORGHUM BICOLOR) STALK AS A POTENTIAL REINFORCEMENT IN POLYMER COMPOSITES, FOCUSING ON ITS DIAMETER, DENSITY, AND SURFACE CHARACTERISTICS. THE DIAMETERS OF 100 RANDOM STALKS WERE MEASURED AT THREE POINTS ALONG THEIR LENGTH. THE RELATIVE DENSITY WAS DETERMINED BY PYCNOMETRY, AND THE APPARENT DENSITY WAS CALCULATED BASED ON THE DIMENSIONS AND MASS OF THE STALKS. ADDITIONALLY, A SURFACE ANALYSIS WAS PERFORMED USING SCANNING ELECTRON MICROSCOPY (SEM).THERE WAS A WIDE VARIATION IN STALK DIAMETERS, WITH A HIGHER CONCENTRATION BETWEEN 5 AND 7 MM. BOTH RELATIVE AND APPARENT DENSITIES SHOWED SIGNIFICANT VARIATIONS. THE SURFACE ANALYSIS REVEALED A ROUGH AND POROUS LIGNOCELLULOSIC STRUCTURE, CONTRIBUTING TO LOW DENSITY AND GOOD LOAD RESISTANCE. THE BROOMCORN STALK SHOWED PROMISE AS A REINFORCEMENT IN POLYMER COMPOSITES, WITH THE POTENTIAL TO IMPROVE MECHANICAL PROPERTIES AND PRODUCE LOW-DENSITY COMPOSITES.

Palavras-chave

Compósitos poliméricos; Fibras naturais; Sorgo vassoura

Polymer composites; Natural fibers; Broomcorn sorghum

Como citar

SATIRO, ANTONIO RICARDO GRIPPA; CARVALHO, EDUARDO ATEM DE; LOPES, FELIPE PERISSÉ DUARTE; SIMONASSI, NOAN TONINI; MONTEIRO, SERGIO NEVES. ANÁLISE DAS CARACTERÍSTICAS DO COLMO DO SORGO VASSOURA COMO POSSÍVEL REFORÇO EM COMPÓSITOS POLIMÉRICOS , p. 1929-1939. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.