A INDúSTRIA DE CERâMICA VERMELHA GERA UMA GRANDE PREOCUPAçãO PARA O MEIO AMBIENTE, CERCA DE 30% DOS MATERIAIS GERADOS, SãO DESPERDIçADOS POR FALHAS EM SEU PROCESSAMENTO. DESSA FORMA, A APLICAçãO DE RESíDUOS SóLIDOS NA CONSTRUçãO SUSTENTáVEL TEM ATRAíDO MUITA ATENçãO. O OBJETIVO DESTE ESTUDO é INVESTIGAR O USO DE RESíDUO CERâMICO COMO SUBSTITUTO PARCIAL DA AREIA NA PRODUçãO DE ARGAMASSAS. AS ARGAMASSAS FORAM FEITAS PARA ASSENTAMENTO DE BLOCOS E REVESTIMENTO DE PAREDES E TETOS, NA PROPORçãO DE MISTURA 1:6 (CIMENTO:AREIA) EM MASSA. A AREIA FOI SUBSTITUíDA POR RESíDUOS CERâMICOS EM DIFERENTES PROPORçõES (0%, 10%, 20% E 30%). A ATIVIDADE POZOLâNICA DO RESíDUO CERâMICO FOI TESTADA PELO TESTE DE LUXáN E CHAPELLE MODIFICADO INDICANDO UMA BOA POZOLANICIDADE E AS DISTRIBUIçõES DE TAMANHO DE PARTíCULA FORAM OBTIDAS A PARTIR DE GRANULOMETRIA DO RESíDUO CERâMICO. FORAM REALIZADOS OS ENSAIOS NO ESTADO FRESCO COMO íNDICE DE CONSISTêNCIA, DENSIDADE NO ESTADO FRESCO E TEOR DE AR INCORPORADO E RETENçãO DE áGUA. APóS A REALIZAçãO DOS TESTES E DOS DADOS OBTIDOS, CONCLUI-SE QUE AS ARGAMASSAS COM OS RESULTADOS MAIS SATISFATóRIOS, FORAM COM OS TRAçOS COM 10%, QUE APRESENTOU RESULTADOS SUPERIORES AOS TRAçOS DE REFERêNCIA
THE RED CERAMIC INDUSTRY GENERATES GREAT CONCERN FOR THE ENVIRONMENT, AROUND 30% OF THE MATERIALS GENERATED ARE WASTED DUE TO ERRORS IN THEIR PROCESSING. THEREFORE, THE APPLICATION OF SOLID WASTE IN SUSTAINABLE CONSTRUCTION HAS ATTRACTED A LOT OF ATTENTION. THE OBJECTIVE OF THIS STUDY IS TO INVESTIGATE THE USE OF CERAMIC WASTE AS A PARTIAL SUBSTITUTE FOR SAND IN THE PRODUCTION OF MORTAR.THE MORTARS WERE MADE FOR LAYING BLOCKS AND COVERING WALLS AND CEILINGS, IN A MIXTURE RATIO OF 1:6 (CEMENT:SAND) BY MASS. THE SAND WAS REPLACED BY CERAMIC WASTE IN DIFFERENT PROPORTIONS (0%, 10%, 20% AND 30%). THE POZZOLANIC ACTIVITY OF THE CERAMIC RESIDUE WAS TESTED BY THE LUXáN AND MODIFIED CHAPELLE TEST INDICATING GOOD POZZOLANICITY AND THE PARTICLE SIZE DISTRIBUTIONS WERE OBTAINED FROM PARTICLE SIZE OF THE CERAMIC RESIDUE AND SAND. TESTS WERE CARRIED OUT IN BOTH THE FRESH STATE AND CONSISTENCY INDEX, WATER RETENTION, INCORPORATED AIR CONTENT AND CALORIMETRY. AFTER CARRYING OUT THE TESTS AND THE DATA OBTAINED, IT WAS CONCLUDED THAT THE MORTARS WITH THE MOST SATISFACTORY RESULTS WERE WITH THE 10% MIXES, WHICH PRESENTED BETTER RESULTS THAN THE REFERENCE MIXTURES.
Palavras-chave
Cerâmica vermelha; Resíduo cerâmico; Argamassa; Pozolânica; Estado fresco
Red ceramic; Ceramic waste; Mortar; Pozzolanic; Fresh state
Como citar
CHERENE, MARIANA GOMES PINTO;
BARROSO, LAIMARA DA SILVA;
TAVARES, KARINE MIRANDA DE SOUZA;
XAVIER, GUSTAVO DE CASTRO;
AZEVEDO, AFONSO RANGEL GARCEZ DE.
ANÁLISE DAS PROPRIEDADES NO ESTADO FRESCO DE ARGAMASSAS CONTENDO RESÍDUO CERÂMICO
,
p. 1985-1995.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-41025