ANÁLISE DAS PROPRIEDADES NO ESTADO FRESCO DE ARGAMASSAS CONTENDO RESÍDUO DE REBOCO TERMOATIVADO: ANALYSIS OF THE FRESH STATE PROPERTIES OF MORTARS CONTAINING THERMAL-ACTIVATED PLASTER RESIDUE

O SETOR DA CONSTRUçãO CIVIL é O GRANDE RESPONSáVEL POR MATERIALIZAR OS PROJETOS DE ENGENHARIA E ARQUITETURA, GERAR EMPREGOS E IMPACTAR DIRETAMENTE A ECONOMIA. NO ENTANTO, GERA RESíDUOS EM LARGA ESCALA, CAUSANDO IMPACTOS NEGATIVOS NOS âMBITOS SOCIAIS, ECONôMICOS E AMBIENTAIS. VISANDO A MITIGAçãO DE TAIS IMPACTOS, ESTA PESQUISA RECICLOU E REAPROVEITOU O RESíDUO CIMENTíCIO DE REBOCO (RCR) POR TERMOATIVAçãO EM TEMPERATURA DE 550°C. COM O INTUITO DE AVALIAR O POTENCIAL DO RCR TERMOATIVADO, FORAM PREPARADAS ARGAMASSAS CONTENDO 0, 10, 20 E 30% DE SUBSTITUIçãO PARCIAL DA AREIA NATURAL PELO RCR, TRAçO 1:6 E CIMENTO CPV ARI. A ANáLISE QUíMICA POR FLUORESCêNCIA DE RAIOS-X (FR-X) MOSTROU QUE O RESíDUO CONSTITUI-SE PRINCIPALMENTE POR SIO2 E CAO, Já OS ENSAIOS DE MASSA ESPECíFICA E DENSIDADE DEMONSTRARAM QUE O RCR POSSUI MAIOR DENSIDADE QUE A AREIA. POR MEIO DOS ENSAIOS DE íNDICE DE CONSISTêNCIA, RETENçãO DE áGUA E TEOR DE AR INCORPORADO PôDE-SE CONSTATAR QUE O TRAçO MAIS INDICADO FOI O CPV30, POIS AUMENTOU A RETENçãO DE áGUA, DIMINUIU O TEOR DE AR INCORPORADO EM RELAçãO AO TRAçO CPV00 E OBTEVE MAIOR FLUIDEZ E CONSEQUENTEMENTE, MAIOR TRABALHABILIDADE.

THE CIVIL CONSTRUCTION SECTOR IS LARGELY RESPONSIBLE FOR MATERIALIZING ENGINEERING AND ARCHITECTURAL PROJECTS, GENERATING JOBS AND DIRECTLY IMPACTING THE ECONOMY. HOWEVER, IT GENERATES WASTE ON A LARGE SCALE, CAUSING NEGATIVE IMPACTS IN THE SOCIAL, ECONOMIC AND ENVIRONMENTAL SPHERES. AIMING TO MITIGATE SUCH IMPACTS, THIS RESEARCH RECYCLED AND REUSED CEMENTITIOUS PLASTER WASTE (RCR) THROUGH THERMOACTIVATION AT A TEMPERATURE OF 550°C. IN ORDER TO EVALUATE THE POTENTIAL OF HEAT-ACTIVATED RCR, MORTARS WERE PREPARED CONTAINING 0, 10, 20 AND 30% PARTIAL REPLACEMENT OF NATURAL SAND WITH RCR, 1:6 MIX AND CPV ARI CEMENT. CHEMICAL ANALYSIS BY FR-X SHOWED THAT THE RESIDUE CONSISTS MAINLY OF SIO2 AND CAO, WHILE SPECIFIC MASS AND DENSITY TESTS DEMONSTRATED THAT RCR HAS A HIGHER DENSITY THAN SAND. THROUGH CONSISTENCY INDEX, WATER RETENTION AND INCORPORATED AIR CONTENT TESTS, IT WAS POSSIBLE TO VERIFY THAT THE MOST SUITABLE MIX WAS CPV30, AS IT INCREASED WATER RETENTION, DECREASED THE INCORPORATED AIR CONTENT IN RELATION TO CPV00 AND OBTAINED GREATER FLUIDITY AND CONSEQUENTLY, GREATER WORKABILITY.

Palavras-chave

Termoativado; Resíduo Cimentício; Reaproveitamento; Construção civil.

Thermoactivation; Cement Waste; Reuse; Civil Construction.

Como citar

TAVARES, KARINE MIRANDA DE SOUZA; BARROSO, LAIMARA DA SILVA; PEREIRA, MARIA MARIANA DIAS; CHERENE, MARIANA GOMES PINTO; SOUSA, LETÍCIA BARCELOS DE; XAVIER, GUSTAVO DE CASTRO; SOUSA, SIDNEI JOSÉ GOMES; AZEVEDO, AFONSO RANGEL GARCEZ DE; MONTEIRO, SÉRGIO NEVES. ANÁLISE DAS PROPRIEDADES NO ESTADO FRESCO DE ARGAMASSAS CONTENDO RESÍDUO DE REBOCO TERMOATIVADO , p. 1723-1736. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-40924