ANÁLISE DE FALHA DE UMA PLACA FEMORAL LONGA DE TI-AL-V

FAILURE ANALYSIS OF A TI-AL-V FEMORAL LONG PLATE

Autoria

Barbosa, Cassio; Abud, Ibrahim de Cerqueira; Monteiro, Maurício de Jesus; Santos, Claudio Teodoro dos; Gallo, Gerson Ortiz; Centeno, Robson Oliveira; Caminha, Ieda Maria Vieira

DOI

10.5151/2594-5327-33981

Downloads

Baixar Artigo 9 Downloads

Resumo

O CRESCENTE USO DE IMPLANTES CIRÚRGICOS ORTOPÉDICOS, TANTO DEVIDO AO AUMENTO DA LONGEVIDADE DAS PESSOAS, QUANTO À MAIOR EXPOSIÇÃO A DIFERENTES TIPOS DE ACIDENTES, TEM LEVADO À NECESSIDADE DE DESENVOLVIMENTO DE MATERIAIS METÁLICOS COM MELHOR DESEMPENHO NESTE TIPO DE APLICAÇÃO. O OBJETIVO DESTE TRABALHO É ANALISAR COMO OCORREU A FALHA DE UM PLACA DE LIGA TI-6AL-4V APÓS APENAS 45 DIAS DE INSERÇÃO DESTE IMPLANTE EM UMA PACIENTE COM CERCA DE 50 ANOS DE IDADE. A UTILIZAÇÃO DE TÉCNICAS DE ANÁLISE EXPERIMENTAL, COMO MICROSCOPIA ÓTICA E MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV), PERMITIU A CONCLUSÃO DE QUE A PLACA FRATUROU INICIALMENTE POR FADIGA, CAUSADA PELA CONCENTRAÇÃO DE TENSÕES RESULTANTE DE USINAGEM INADEQUADA NAS RAÍZES DOS FILETES DE ROSCA DOS FUROS DA PLACA, PROSSEGUINDO COMO FRATURA FRÁGIL TRANSGRANULAR PELO MECANISMO DE CLIVAGEM.

 

THE INCREASING USE OF ORTHOPEDIC SURGICAL IMPLANTS, BOTH DUE TO THE INCREASE IN PEOPLE'S LONGEVITY, AS WELL AS THE GREATER EXPOSURE TO DIFFERENT TYPES OF ACCIDENTS, HAS LED TO THE NEED TO DEVELOP METALLIC MATERIALS WITH BETTER PERFORMANCE IN THIS TYPE OF APPLICATION. THE AIM OF THIS WORK IS TO ANALYZE HOW THE FAILURE OF A TI-6AL-4V ALLOY PLATE OCCURRED AFTER ONLY 45 DAYS OF INSERTION OF THIS IMPLANT IN A PATIENT ABOUT 50 YEARS OLD. THE USE OF EXPERIMENTAL ANALYSIS TECHNIQUES, SUCH AS OPTICAL MICROSCOPY AND SCANNING ELECTRON MICROSCOPY (SEM), ALLOWED THE CONCLUSION THAT THE PLATE INITIALLY FRACTURED DUE TO FATIGUE, CAUSED BY THE CONCENTRATION OF STRESSES RESULTING FROM INADEQUATE MACHINING IN THE ROOTS OF THE THREAD THREADS OF THE HOLES IN THE HOLE. PLAQUE, PROCEEDING AS A FRAGILE TRANSGRANULAR FRACTURE THROUGH THE CLEAVAGE MECHANISM.

Palavras-chave

Implantes; Titânio; Microscopia Ótica; MEV; Análise de Falhas.

Implants; Titanium; Optical Microscopy; SEM; Failure Analysis.