Título

ANÁLISE DE FRETTING-CORROSION NO TAPER TRUNNION DE PRÓTESES DE QUADRIL FABRICADAS EM AÇO INOXIDÁVEL ISO 5832-1 E 5832-9

FRETTING-CORROSION ANALYSE IN THE TAPER TRUNION OF HIP PROSTHESIS MANUFACTURED IN WROUGHT STAINLESS STEEL ISO 5832-1 AND 5832-9

Autoria

Santos, Vinícius Oliveira dos; Cubillos, Patricia Ortega; Pizzolatti, André Luís Almeida; Santos, Claudio Teodoro dos; Caminha, Ieda Maria Vieira; Monteiro, Maurício de Jesus; Roesler, Carlos Rodrigo de Melo

DOI

10.5151/1516-392X-260

Downloads

Baixar Artigo 340 Downloads

Resumo

A presente pesquisa visa investigar o processo de fretting-corrosion no cone da haste femoral de próteses de quadril fabricadas em aço inoxidável. Foram avaliados dois grupos de componentes femorais. As hastes analisadas foram fabricadas em aço inoxidável ISO 5832-1 (grupo I) e aço inoxidável ISO 5832-9 (grupo II). A metodologia consistiu em realizar o ensaio de fadiga em meio corrosivo e posterior análise de fretting-corrosion de forma qualitativa e quantitativa. Os resultados demonstraram que os requisitos químicos e metalúrgicos dos componentes dos dois grupos estavam de acordo com as exigências das normas técnicas. As hastes do grupo I, tiveram um desempenho inferior às hastes do grupo II com relação ao desempenho em freeting-corrosion. As hastes do grupo I apresentaram uma área afetada por corrosão muito elevada, fato que pode aumentar a probabilidade de eventos adversos no corpo humano relacionados as partículas metálicas, reduzindo assim a segurança e eficácia desses componentes a longo prazo no corpo humano.

 

The present study aim investigates the fretting-corrosion process in the taper trunnion of hip prosthesis manufactured with metallic alloys of stainless steel that comply the requirements of standards ISO 5832-1 and ISO 5832-9. Two groups of femoral components were evaluated: group I - manufactured with wrought stainless steel according ISO 5832-1; group II – manufactured with wrought high nitrogen stainless steel according ISO 5832-9. The samples were submitted to fatigue trial in corrosive medium and the fretting-corrosion was analyzed qualitatively (Goldberg criterion) and quantitatively (affected area). Results showed that chemical and metallurgical requirements of the analyzed stems and heads of both groups were in accordance with the requirements of ISO technical standards. The stems of the group I had a lower performance than the stems of group II. Stems group I showed a high area affected by corrosion, which can increase the probability of adverse events in the human body related to the metal particles. and reduce the safety and efficacy of these components during a long-time period inside of human body.

Palavras-chave

FRETTING-CORROSION, HASTE FEMORAL; ISO 5832-1; ISO 5832-9.

FRETTING-CORROSION, FEMORAL HEAD; ISO 5832-1; ISO 5832-9