ANÁLISE DE MICROESTRUTURAL, DE RESISTÊNCIA À CORROSÃO E DE MICRODUREZA DO AÇO ASTM 890 GRAU 3A EM DIFERENTES TEMPOS DE SOLUBILIZAÇÃO

MICROSTRUCTURE, CORROSION RESISTANCE AND MICROHARDNESS ANALYSIS OF ASTM 890 GRADE 3A IN DIFFERENT SOLUBILITY TIMES

DOI

10.5151/2594-4711-33677

Downloads

Baixar Artigo 18 Downloads

Resumo

O aço inoxidável duplex (AID) ASTM 890 de grau 3A tem grande utilização na indústria de tubulações de petróleo no Brasil e no mundo. O estudo da variação do tempo necessário para solubilizar um material é importante, pois, diminuindo esse tempo, pode ser reduzido gastos com forno. O objetivo desse trabalho é comparar diferentes resultados para três tempos distintos de solubilização do aço inoxidável duplex fundido ASTM 890 de grau 3A. A literatura indica que a solubilização desse aço deve ocorrer na temperatura de 1120°C, no período de 4 horas. Entretanto, não existem trabalhos que mostrem a influência da diminuição do tempo do tratamento térmico na resistência á corrosão desse material. A fim de analisar isso, foram feitos trés tratamentos térmicos a 1120°C, em tempos 30 minutos, 2 horas e 4 horas. O grau 3A tem como característica, por exemplo, não conter cobre em sua composição, ter 1%p Mn e ter também 25%p Cr. Para tal estudo foi feito uma análise microestrutural em microscópio ótico para observar diferenças nas fases do material. Em seguida, foi usado ensaios eletroquímicos de monitoramento de potencial de circuito aberto, espectroscopia de impedância e polarização pontenciodinâmica anódica, utilizando um eletrólito de NaCl 1M, para ver o desempenho contra a corrosão nessa liga. Também foi feita uma avaliação mecânica do aço sendo exposto a testes de microdureza. Por fim, foi obtido, com esses resultados, pouca mudança significativa no comportamento do material após diferentes tempos.

 

ASTM 890 grade 3 stainless steel duplex (AID) has great use in the oil tube industry in Brazil and worldwide. The material of the time variation necessary to solubilize a material is important, therefore, by decreasing this time, it can become spent with an furnace. The objective of this paper is the comparison of results for the different solubilization times of ASTM 890 grade 3A molten duplex stainless steel. A literature indicates that a solubilization a year must have the temperature of 1120 ° C, in the period of 4 hours. However, there are no results that show the influence of time intensity on the corrosion resistance of this material. In order to analyze it, 3 thermal intervals were made at 1120 ° C, in times 30 minutes, 2 hours and 4 hours. Grade 3A is characteristic, for example, it does not cover its composition, for example 1% w M and also 25% w Cr. The study was made a microstructural analysis under optical microscope to observe the differences in the phases of the material. Then, electrochemical tests of open circuit potential, impedance spectroscopy and anodic polarization, using a 1M NaCl electrolytic system, were used to verify the corrosion in the alloy. The test was made a review of the steel being exposed to tests of microhardness. Finally, the results were obtained with which expectations do not evolve.

Palavras-chave

Aço inoxidável; Resistência à corrosão; Solubilização; Ensaios Eletrolíticos.

Stainless steel; Corrosion resistence; Solubilization; Electrochemical tests.

Como citar

Silva Junior, Francisco Carlos Gomes da; Rodrigues, Matheus Souza; Mata, Stephany Aparecida Santos da; Machado, Janaina Goncalves Maria Da Silva; Araújo, Walney Silva. ANÁLISE DE MICROESTRUTURAL, DE RESISTÊNCIA À CORROSÃO E DE MICRODUREZA DO AÇO ASTM 890 GRAU 3A EM DIFERENTES TEMPOS DE SOLUBILIZAÇÃO , p. 109-116. In: 19° Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas (ENEMET), São Paulo, 2019.