ANÁLISE DE TÊMPERA DE LIGAS DE ALUMÍNIO EM SOLUÇÃO AQUOSA DE POLÍMERO. UM ESTUDO COMPARATIVO COM TÊMPERA EM ÁGUA: ANALYSIS OF THE ALUMINUM ALLOYS QUENCH IN AQUEOUS SOLUTION OF POLYMERS. A COMPARATIVE STUDY WITH WATER QUENCH

Kavalco, Patrícia M.; Canale, Lauralice C. F.; Totten, George E.

doi:10.5151/2594-5300-14580

Anais do Seminário de Aciaria, Fundição e Metalurgia de Não-ferrosos

ISSN 2594-5300

11º Seminário de Metais Não-Ferrosos — vol. 11, num.11 (2009)

Título

ANÁLISE DE TÊMPERA DE LIGAS DE ALUMÍNIO EM SOLUÇÃO AQUOSA DE POLÍMERO. UM ESTUDO COMPARATIVO COM TÊMPERA EM ÁGUA

ANALYSIS OF THE ALUMINUM ALLOYS QUENCH IN AQUEOUS SOLUTION OF POLYMERS. A COMPARATIVE STUDY WITH WATER QUENCH

Autoria

Kavalco, Patrícia M.; Canale, Lauralice C. F.; Totten, George E.

10.5151/2594-5300-14580

Downloads

Baixar Artigo 102 Downloads

Resumo

A têmpera com solução aquosa de polímero melhora as propriedades de distorção, dureza e corrosão intergranular. Neste trabalho, foi realizado um estudo comparativo entre a têmpera em água e em solução aquosa de polímero de ligas de alumínio aeronáutico 2024, 7475 e 7075 submetidas a diferentes condições de resfriamento, sendo a água em duas diferentes temperaturas (30°C e 70°C) e de soluções aquosas de polímero PAG com diferentes concentrações (12% e 20%) a 40°C. Os resultados de distorção e corrosão intergranular ficaram dentro do esperado. As soluções de polímero, por apresentarem uma troca de calor mais uniforme, garantiram propriedades de dureza com baixa distorção. Isso oferece subsídios para que as indústrias de tratamento térmico de alumínio melhorem a qualidade dos componentes tratados, diminuindo a porcentagem de retrabalho.

The quenching with aqueous solution of polymer improves the properties of distortion, hardness and intergranular corrosion. In this work was performed a comparative study between water quench and polymer aqueous solution quench of aircraft aluminum alloys 2024, 7475 and 7075 under different conditions of cooling, the water at two different temperatures (30°C and 70°C) and PAG polymer aqueous solutions with different concentrations (12% and 20%) at 40°C. The results of distortion and intergranular corrosion were within the expected. The solutions of polymer, for presenting a more uniform heat exchange, guaranteed properties of hardness with low distortion. It provides subsidies to the industries of heat treatment of aluminum components to improve the quality of treatment, decreasing the percentage of rework.

Palavras-chave

Têmpera de alumínio; Polímeros; Distorção; Corrosão intergranular.

Aluminum quench; Polymers; Distortion; Intergranular corrosion.