ANÁLISE DO DESEMPENHO BALÍSTICO DAS CERÂMICAS PRODUZIDAS COM E SEM FLUORTETO DE LÍTIO

ANALYSIS OF THE BALLISTIC PERFORMANCE OF CERAMICS PRODUCED WITH AND WITHOUT LITHIUM FLUORTURE

DOI

10.5151/2594-5327-33388

Downloads

Baixar Artigo 107 Downloads

Resumo

O aumento da criminalidade impulsiona pesquisadores a buscarem alternativas para melhorar os equipamentos destinados a segurança pessoal de civis e militares, através de materiais que mantenham a eficiência da proteção balística, no entanto, possibilitem a manutenção da adequada mobilidade, além de possuírem custos competitivos com os atuais materiais utilizados em proteção individual. Em vista disso, a presente pesquisa tem por objetivo avaliar a presença do Fluoreto de Lítio nas cerâmicas que compõe um sistema de blindagem multicamada (SBM). Os SBMs são compostos, geralmente, por três camadas de materiais distintos e a primeira camada é composta por uma cerâmica que tende absorver, em torno de 55% da energia, e a fragmentar o projétil. Portanto, foram produzidas as amostras cerâmicas de Alumina (Al2O3) e Nióbia (Nb2O5) e foram comparadas com as cerâmicas dopadas com Fluoreto de Lítio (LiF). A presença do LiF apresenta uma melhor densificação e produz uma ligeira mudança na morfologia das partículas. Além disso, notou-se que a presença do LiF na blindagem balística produz uma indentação maior quando comparada com as cerâmicas sem o composto. Entretanto, por maior que fosse à indentação, ainda sim os resultados foram satisfatórios com o que preconiza na norma, NIJ 0101.04 isto é, uma indentação inferior a 44 milímetros.

 

The increase in crime prompts researchers to seek alternatives to improve equipment for the personal safety of civilians and soldiers, through materials that maintain the efficiency of ballistic protection, however, allow the maintenance of adequate mobility, and have competitive costs with materials used for individual protection. In view of this, the present research aims to evaluate the presence of Lithium Fluoride in the ceramics that makes up a multilayer armor system (MAS). MASs are generally composed of three layers of distinct materials and the first layer consists of a ceramic that tends to absorb about 55% of the energy and to fragment the projectile. Therefore, the ceramic samples of Alumina (Al2O3) and Nióbia (Nb2O5) were produced and compared with the ceramics doped with Lithium Fluoride (LiF). The presence of LiF exhibits better densification and produces a slight change in the morphology of the particles. Furthermore, it has been noted that the presence of LiF in ballistic armor produces a greater indentation when compared to ceramics without the compound. However, however large the indentation, the results were still satisfactory with what is stated in the standard, NIJ 0101.04 ie an indentation of less than 44 millimeters.

Palavras-chave

Cerâmica; Alumina; Fluoreto de Lítio; Blindagem balística

Ceramics; Alumina; Lithium Fluoride; Ballistic Shielding

Como citar

Demosthenes, Luana Cristyne da Cruz; Oliveira, Michelle Souza; Filho, Fabio da Costa Garcia; Luz, Fernanda dos Santos; Monteiro, Sergio Neves; Nascimento, Lucio Fabio Cassiano. ANÁLISE DO DESEMPENHO BALÍSTICO DAS CERÂMICAS PRODUZIDAS COM E SEM FLUORTETO DE LÍTIO , p. 1299-1310. In: 74º Congresso Anual da ABM, São Paulo, 2019.