ANÁLISE DO DESEMPENHO QUÍMICO E MECÂNICO DE TELHAS METÁLICAS REVESTIDAS

CHEMICAL AND MECHANICAL PERFORMANCE EVALUATION OF METALIC ROOFS

Autoria

Hauegen, Christien Guisard

DOI

10.5151/2594-5327-34218

Downloads

Baixar Artigo 10 Downloads

Resumo

O AMBIENTE EM QUE UMA ESTRUTURA METÁLICA É CONSTRUÍDA AFETA A DURABILIDADE DE SEUS COMPONENTES, VIS-À-VIS OS ÍNDICES NORMATIZADOS DE CORROSIVIDADE SEGUNDO A ABNT NBR 14643:2001 E EN ISO 9223:2012. NO TOCANTE ÀS TELHAS DE AÇO, A ALTERNATIVA DE PROTEÇÃO MAIS COMUM E EFETIVA É O DEPÓSITO DE UMA CAMADA METÁLICA SOBRE O METAL-BASE, UTILIZANDO DIVERSAS LIGAS EXISTENTES NO MERCADO. CABE RESSALTAR QUE, DEPENDENDO DO MATERIAL ESCOLHIDO, O DESEMPENHO FRENTE AO AMBIENTE SERÁ DIFERENTE. ALÉM DISSO, A DURABILIDADE DE TELHAS TAMBÉM ESTÁ ASSOCIADA AOS ASPECTOS MECÂNICOS, SOBRETUDO NO TOCANTE ÀS ESPESSURAS E AO GRAU DE AÇO, QUE DEVEM SER COMPATÍVEIS COM AS CONDIÇÕES DE PROJETO. NESTE CONTEXTO, ESTE ARTIGO APRESENTA UMA REVISÃO SOBRE OS PRINCIPAIS REVESTIMENTOS DISPONÍVEIS PARA TELHAS METÁLICAS BEM COMO CONSIDERAÇÕES SOBRE REQUISITOS MECÂNICOS MÍNIMOS PARA GARANTIA DA PERFORMANCE AO LONGO DE SUA VIDA ÚTIL. OBSERVOU-SE QUE A LIGA ZINCO-MAGNÉSIO-ALUMÍNIO FIGURA COMO A MELHOR ALTERNATIVA PARA PROTEÇÃO DO AÇO EM MEIOS ALCALINOS E, AO MESMO TEMPO, TELHAS COM ESPESSURAS REDUZIDAS, SOBRETUDO INFERIORES A 0,40 MM, SÃO MAIS SUSCEPTÍVEIS À OCORRÊNCIA DE ESTADOS-LIMITES DE SERVIÇO POR SUA RIGIDEZ EFETIVA À FLEXÃO REDUZIDA.

 

THE ENVIRONMENT IN WHICH A STEEL STRUCTURE IS BUILT AFFECTS THE DURABILITY OF ITS COMPONENTS, VIS-à-VIS THE CORROSION INDEXES ACCORDING TO ABNT NBR 14643:2001 AND EN ISO 9223:2012. REGARDING STEEL TILES, THE MOST EFFECTIVE PROTECTION ALTERNATIVE CORRESPONDS TO THE DEPOSIT OF A METALLIC COATING OVER THE METAL BASE. DEPENDING ON CHOSEN MATERIAL, MULTIPLE PERFORMANCES ARE POSSIBLE FACE TO THE ENVIRONMENT. IN ADDITION, MECHANICAL PARAMETERS ALSO INFLUENCE DURABILITY, IN SPECIAL THICKNESS AND STEEL GRADE, WHICH MUST BE COMPATIBLE WITH PROJECT PREMISES. AS SUCH, THIS ARTICLE PRESENTS A REVIEW ON MAIN COATING ALTERNATIVES AVAILABLE FOR STEEL TILES AS WELL AS MINIMUM MECHANICAL REQUIREMENTS TO ENSURE WELL PERFORMANCE DURING ITS LIFETIME. HENCE, ZINC-MAGNESIUM-ALUMINIUM ALLOY WAS FOUND TO BE THE BEST ALTERNATIVE IN ALKALINE ENVIRONMENTS AND, AT THE SAME TIME, THINNER TILES, AT MOST THOSE WITH THICKNESS LESS THAN 0,40 MM, ARE MORE SUSCEPTIBLE TO SERVICEABILITY LIMIT STATES DUE TO THEIR REDUCED EFFECTIVE FLEXURAL STIFFNESS.

Palavras-chave

telha metálica; revestimento; durabilidade; dimensionamento.

steel tiles; coating; durability; design.