QUANDO EXPOSTOS À AÇÃO DE FLUIDOS, EQUIPAMENTOS ESTÃO SUJEITOS AO DESGASTE POR EROSÃO CAVITACIONAL. PARA AMENIZAR ESTE EFEITO, SUPERLIGAS E TRATAMENTOS TÉRMICOS COMO A SOLUBILIZAÇÃO PODEM SER USADOS. A SUPERLIGA DE COBALTO STELLITE 250 FOI SUBMETIDA À SOLUBILIZAÇÃO E AO ENSAIO DE CAVITAÇÃO VIBRATÓRIA, COM OBJETIVO DE INVESTIGAR SEU COMPORTAMENTO QUANTO AO DESGASTE POR EROSÃO CAVITACIONAL. AMOSTRAS FUNDIDAS FORAM SOLUBILIZADAS A 1200°C POR 12 HORAS, COM POSTERIOR TÊMPERA EM ÁGUA. A CARACTERIZAÇÃO FOI REALIZADA POR MICROSCÓPIO ÓTICO, ESTEREOSCÓPIO, MICRODUREZA E DIFRAÇÃO DOS RAIOS-X. O ENSAIO DE CAVITAÇÃO SEGUIU A NORMA ASTM G32. A RESISTÊNCIA À EROSÃO CAVITACIONAL FOI ANALISADA A PARTIR DA PERDA DE MASSA ACUMULADA EM FUNÇÃO DO TEMPO DE ENSAIO. OS MECANISMOS DE DESGASTE FORAM IDENTIFICADOS COM MICROSCÓPIO ELETRÔNICO DE VARREDURA. APÓS A SOLUBILIZAÇÃO, A LIGA APRESENTOU ESTRUTURA CRISTALINA MISTA (CFC E HC), RECRISTALIZAÇÃO PRIMÁRIA E NUCLEAÇÃO DE GRÃOS. A RESISTÊNCIA À EROSÃO CAVITACIONAL DA AMOSTRA SOLUBILIZADA FOI INFERIOR AO DA AMOSTRA NA CONDIÇÃO COMO FUNDIDA. OS MECANISMOS DE DESGASTE OBSERVADOS PARA A LIGA STELLITE 250 SOLUBILIZADA FORAM BANDAS DE DESLIZAMENTO, FORMAÇÃO DE PITES E CRATERAS.
WHEN EXPOSED TO THE ACTION OF FLUIDS, EQUIPMENTS ARE SUBJECT TO CAVITATION EROSION WEAR. TO MITIGATE THIS EFFECT, SUPERALLOYS AND HEAT TREATMENTS SUCH AS SOLUTION TREATMENT CAN BE USED. THE STELLITE 250 COBALT SUPERALLOY, WAS SUBJECTED TO SOLUTION TREATMENT AND VIBRATORY CAVITATION TEST, TO INVESTIGATE ITS BEHAVIOR REGARDING WEAR BY CAVITATION EROSION. THE AS-CAST SPECIMENS WERE SOLUBILIZED AT 1200 °C FOR 12 HOURS, WITH SUBSEQUENT QUENCHING IN WATER. THE CHARACTERIZATION WAS PERFORMED USING AN OPTICAL MICROSCOPE, STEREOSCOPE, MICROHARDNESS AND X-RAY DIFFRACTION. THE CAVITATION TEST WAS PERFORMED ACCORDING TO THE ASTM G32 STANDARD. THE CAVITATION EROSION RESISTANCE WAS ANALYZED BY THE ACCUMULATED MASS LOSS AS A FUNCTION OF THE EXPOSURE TIME. THE WEAR MECHANISMS WERE OBSERVED WITH THE SCANNING ELECTRON MICROSCOPE. AFTER THE SOLUTION TREATMENT, THE SPECIMEN SHOWED MIXED CRYSTALLINE STRUCTURE (FCC AND HC), PRIMARY RECRYSTALLIZATION AND GRAIN NUCLEATION. THE RESISTANCE TO CAVITATION EROSION OF THE SOLUTION TREATED SPECIMEN WAS LOWER THAN THE AS-CAST SPECIMEN. THE WEAR MECHANISMS OBSERVED FOR STELLITE 250 ALLOY WERE SLIDING BANDS, FORMATION OF PITS AND CRATERS.
Palavras-chave
Stellite 250; Solubilização; Erosão cavitacional.
Stellite 250; Solution treatment; Cavitation erosion.
Como citar
Fiorin, Ana Paula Favero;
Oliveira, Daniela Bahiense de;
Bozzi, Antônio César.
ANÁLISE DO DESGASTE POR EROSÃO CAVITACIONAL DA SUPERLIGA STELLITE 250 SOLUBILIZADA
,
p. 3569-3579.
In: 75° Congresso Anual da ABM,
São Paulo,
2022.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-34588