Título

ANÁLISE MICROESTRUTURAL DE REVESTIMENTOS DE INCONEL 625 DEPOSITADOS POR PTA-P EM AÇO AISI 4130

MICROSTRUCTURAL ANALYSIS OF INCONEL 625 COATINGS DEPOSITED BY PTA-P ON AISI 4130 STEEL

Autoria

Souza, Gabriela Paula de; Oliveira, Bárbara Ferreira de; Tavares, Sérgio Souto Maior; Almeida, Laryssa dos Santos; Monteiro, Sérgio Neves; Matlakhova, Lioudmila Aleksandrovna

DOI

10.5151/2594-5327-34334

Downloads

Baixar Artigo 16 Downloads

Resumo

O PRESENTE TRABALHO APRESENTA A INFLUÊNCIA DE DUAS CONDIÇÕES DE SOLDAGEM NA MICROESTRUTURA DE INCONEL 625 DEPOSITADO SOBRE AÇO AISI 4130 POR SOLDAGEM PTA-P: CONDIÇÃO 1 (CORRENTE: 105 A, GÁS DE PLASMA: 1,7 L/MIN, ROTAÇÃO: 0,29 RPM) E CONDIÇÃO 2 (CORRENTE: 130 A, GÁS DE PLASMA: 1,5 L/MIN, ROTAÇÃO: 0,26 RPM), DE FORMA A VERIFICAR A POSSIBILIDADE DE REALIZAR REVESTIMENTOS EM ÚNICA CAMADA, COM MÍNIMA DILUIÇÃO DE FE. A CARACTERIZAÇÃO MICROESTRUTURAL FOI REALIZADA POR MICROSCOPIA ÓTICA CONFOCAL (MO), MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV), ESPECTROSCOPIA DE ENERGIA DISPERSIVA (EDS) NO METAL BASE, INTERFACE E REVESTIMENTO E DIFRAÇÃO DE RAIOS X (DRX) APENAS NO REVESTIMENTO. MEDIÇÕES DE DUREZA FORAM REALIZADAS AO LONGO DA SEÇÃO TRANSVERSAL DAS AMOSTRAS. OS RESULTADOS MOSTRARAM QUE O METAL BASE APRESENTOU UMA ZONA TERMICAMENTE AFETADA DE GRÃOS GROSSEIROS. NÃO FOI OBSERVADA MARTENSITA NA INTERFACE METAL BASE/ REVESTIMENTO, APESAR DA AMOSTRA DA CONDIÇÃO 1 APRESENTAR MICROTRINCAS NESSA REGIÃO. OS REVESTIMENTOS APRESENTARAM MICROESTRUTURA AUSTENÍTICA DENDRÍTICA COM DISPERSÃO DE CARBETOS NBC NA REGIÃO INTERDENDRÍTICA. NA CONDIÇÃO 2, HOUVE AUMENTO NA DILUIÇÃO DE FE, AFETANDO A FORMAÇÃO DE CARBETOS NBC E, CONSEQUENTEMENTE, A DUREZA DO REVESTIMENTO. DESSA FORMA, É NECESSÁRIA A DEPOSIÇÃO DE DUAS CAMADAS DE INCONEL SOBRE O AÇO AISI 4130

 

THE PRESENT WORK PRESENTS AN INFLUENCE OF TWO WELDING CONDITIONS ON THE MICROSTRUCTURE OF INCONEL 625 DEPOSITED ON AISI 4130 STEEL BY PTA-P WELDING: CONDITION 1 (CURRENT: 105 A, PLASMA GAS: 1.7 L / MIN, ROTATION: 0, 29 RPM) AND CONDITION 2 (CURRENT: 130 A, PLASMA GAS: 1.5 L / MIN, ROTATION: 0.26 RPM), IN ORDER TO CHECK THE POSSIBILITY OF MAKING COATINGS IN A SINGLE LAYER, WITH A MINIMUM FE DILUTION. MICROSTRUCTURAL CHARACTERIZATION WAS CARRIED OUT USING CONFOCAL OPTICAL MICROSCOPY (MO), SCANNING ELECTRON MICROSCOPY (SEM), DISPERSIVE ENERGY SPECTROSCOPY (EDS) OF THE BASE METAL, INTERFACE AND COATING AND X-RAY DIFFRACTION (XRD) ONLY IN THE COATING. HARDNESS MEASUREMENTS WERE MADE ALONG THE CROSS-SECTION OF SAMPLES. THE RESULTS SHOWED THAT THE METAL BASE PRESENT A THERMALLY AFFECTED ZONE OF COARSE GRAINS. NO MARTENSITE WAS OBSERVED AT THE BASE METAL / COATING INTERFACE, DESPITE THE CONDITION 1 SAMPLE SHOWING MICROCRACKS IN THIS REGION. THE COATINGS HAD A DENDRITIC AUSTENITIC MICROSTRUCTURE WITH DISPERSION OF NBC CARBIDES IN THE INTERDENDRITIC REGION. IN CONDITION 2, THERE WAS AN INCREASE IN THE DILUTION OF FE, AFFECTING THE FORMATION OF NBC CARBIDES AND, CONSEQUENTLY, THE HARDNESS OF THE COATING. THUS, IT IS NECESSARY TO DEPOSIT TWO LAYERS OF INCONEL ON AISI 4130 STEEL

Palavras-chave

soldagem de revestimento; PTA-P; Inconel 625; diluição

coating; PTA-P; Alloy 625; dilution