ANÁLISE MICROESTRUTURAL DE SOLDAGEM DISSIMILAR DOS AÇOS AISI 304 E AISI 430 SOLDADOS PELO PROCESSO GTAW: MICROSTRUCTURAL ANALYSIS OF DISSIMILAR WELDING OF AISI 304 AND AISI 430 STEEL WELDED BY THE GTAW PROCESS

O AçO INOXIDáVEL FOI DESENVOLVIDO NO INíCIO DO SéCULO XX E DESDE ENTãO TEM SIDO UTILIZADO EM DIFERENTES VARIAçõES DE ACORDO COM SUA COMPOSIçãO E FASES, GERANDO, ENTRE OUTROS, OS AçOS FERRíTICOS E AUSTENíTICOS. A SOLDAGEM TIG é O PROCESSO DE SOLDAGEM DE GáS DE PROTEçãO COM TUNGSTêNIO (GTAW) AMPLAMENTE UTILIZADO NA UNIãO DE JUNTAS DE AçO INOXIDáVEL. UTILIZADOS DESDE EQUIPAMENTOS DOMéSTICOS ATé AUTOMOBILíSTICOS, TAIS MATERIAIS OCUPAM GRANDE ESPAçO ENTRE OS MATERIAIS DE AçO INOX. DESTA FORMA ESTE TRABALHO PROPôS A ANáLISE DA UNIãO DE DOIS TIPOS DE AçO INOXIDáVEL, FERRíTICO (AISI 430) E AUSTENíTICO (AISI 304), A FIM DE AVALIAR SEUS RESULTADOS MICROESTRUTURAIS EM RELAçãO à QUALIDADE DA JUNTA OBTIDA. AS PROPRIEDADES METALúRGICAS POR MEIO DE ENSAIOS METALOGRáFICOS FORAM REALIZADAS POR MEIO DE MICROSCOPIA óPTICA, MICROSCOPIA ELETRôNICA DE VARREDURA, ESPECTROSCOPIA DE ENERGIA DISPERSIVA DE RAIOS X E ESPECTROMETRIA DE ENERGIA DISPERSIVA DE FLUORESCêNCIA DE RAIOS X. OS RESULTADOS INDICARAM QUE A MICROESTRUTURA DAS JUNTAS CONSISTIA EM GRãOS DE AUSTENITA ENVOLVIDOS EM FERRITA DELTA. O TAMANHO MéDIO DE GRãO FOI SIGNIFICATIVAMENTE MAIOR DO QUE O TAMANHO MéDIO DE GRãO EM AMBAS AS ZONAS AFETADAS PELO CALOR. A COMPOSIçãO QUíMICA DO METAL DE SOLDA CONSISTIU PRINCIPALMENTE DE FERRO E CROMO.

STAINLESS STEEL WAS DEVELOPED AT THE BEGINNING OF THE 20TH CENTURY AND SINCE THEN IT HAS BEEN USED IN DIFFERENT VARIATIONS ACCORDING TO ITS COMPOSITION AND PHASES, GENERATING, AMONG OTHERS, FERRITIC AND AUSTENITIC STEELS. GAS TUNGSTEN ARC WELDING (GTAW) IS WIDELY USED IN JOINING STAINLESS STEEL JOINTS. USED FROM DOMESTIC EQUIPMENT TO MOTORSPORT, SUCH MATERIALS OCCUPY A LARGE SPACE AMONG STAINLESS STEEL MATERIALS. IN THIS WAY THIS WORK IT WAS PROPOSED THE ANALYSIS OF THE UNION OF TWO TYPES OF STAINLESS STEEL, FERRITIC AND AUSTENITIC, IN ORDER TO EVALUATE THEIR MICROSTRUCTURE RESULTS IN RELATION TO THE QUALITY OF THE JOINT OBTAINED. METALLURGICAL PROPERTIES THROUGH METALLOGRAPHIC TESTS WERE CARRIED OUT USING OPTICAL MICROSCOPY, SCANNING ELECTRON MICROSCOPY, ENERGY-DISPERSIVE X-RAY SPECTROSCOPY AND ENERGY-DISPERSIVE X-RAY FLUORESCENCE SPECTROMETRY. THE RESULTS INDICATED THAT THE JOINTS MICROSTRUCTURE OF CONSISTED OF AUSTENITE GRAINS INVOLVED IN DELTA FERRITE. THE AVERAGE GRAIN SIZE WAS SIGNIFICANTLY LARGER THAN THE AVERAGE GRAIN SIZE IN BOTH HEAT AFFECTED ZONES. THE WELD METAL CHEMICAL COMPOSITION MAINLY CONSISTED OF IRON AND CHROMIUM.

Palavras-chave

Aço inoxidável; Metalografia; Metalurgia; Soldagem

Stainless steel; Metallography; Metallurgy; Welding.

Como citar

CONCEICAO, JOAO GABRIEL LUCIO; OLIVEIRA, MATHEUS JOSÉ CUNHA DE. ANÁLISE MICROESTRUTURAL DE SOLDAGEM DISSIMILAR DOS AÇOS AISI 304 E AISI 430 SOLDADOS PELO PROCESSO GTAW , p. 36-44. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-40456