Título

ANÁLISES TERMODINÂMICA E CALORIMETRICA EXPLORATÓRIA DIFERENCIAL EM NOVOS AÇOS COM AL E NB

THERMODYNAMIC AND DIFFERENTIAL SCANNING CALORIMETRY ANALYSIS IN NEW AL AND NB STEEL

Autoria

Junior, Eustaquio de Souza Baeta; Gurgel, Mônica Aline Magalhães; Aguilera, Letícia dos Santos; Paula, Andersan dos Santos; Brandão, Luiz Paulo Mendonça

DOI

10.5151/2594-5327-34750

Downloads

Baixar Artigo 14 Downloads

Resumo

OS AÇOS DO SISTEMA FEMNALC TEM GANHADO GRANDE NOTORIEDADE, POIS SÃO UMA CLASSE PROMISSORA PARA UTILIZAÇÃO EM VEÍCULOS. A MAIOR PARTE DESSAS LIGAS TÊM TEORES DE ALUMÍNIO SUFICIENTES PARA ESTABILIZAR FERRITA-Δ EM TEMPERATURA AMBIENTE E, DEVIDO AO DESENVOLVIMENTO RECENTE, DIFERENTES COMPOSIÇÕES TÊM SIDO TESTADAS VISANDO OTIMIZAR AS MICROESTRUTURAS. ESTE TRABALHO BUSCOU SELECIONAR COMPOSIÇÕES E COMPARAR ANÁLISES TERMODINÂMICAS UTILIZANDO O SOFTWARE THERMO-CALC COM ANÁLISES DE CALORIMETRIA EXPLORATÓRIA DIFERENCIAL (DSC), PARA VERIFICAR SE AS FASES E TRANSFORMAÇÕES PREDITAS OCORREM NO MATERIAL. FORAM REALIZADOS CÁLCULOS EM EQUILÍBRIO PARA MAPEAR A PROPORÇÃO DE FASES EM DIFERENTES COMPOSIÇÕES, A PARTIR DOS QUAIS FORAM SELECIONADAS QUATRO. FORAM CALCULADOS DIAGRAMAS DE FASES PSEUDO BINÁRIOS, DE SOLIDIFICAÇÃO E DE EVOLUÇÃO DAS FASES COM A TEMPERATURA. FORAM CONFECCIONADAS AMOSTRAS COM AS COMPOSIÇÕES SELECIONADAS PARA ANÁLISES EM DSC E MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV). FOI ENCONTRADO BOA CORRELAÇÃO ENTRE AS ANÁLISES MOSTRANDO QUE O MÉTODO DESCREVE CORRETAMENTE AS TRANSFORMAÇÕES DE FASES EM AÇOS LIGADOS AO AL E NB.

 

STEELS FROM THE FEMNALC SYSTEM HAVE GAINED GREAT NOTORIETY FOR BEING A PROMISING TYPE FOR USE IN VEHICLES. MOST OF THESE ALLOYS HAVE ALUMINUM CONTENTS SUFFICIENT TO STABILIZE THE δ FERRITE AT ROOM TEMPERATURE AND, DUE TO RECENT DEVELOPMENT, DIFFERENT COMPOSITIONS HAVE BEEN TESTED TO OPTIMIZE THE MICROSTRUCTURES. THIS WORK AIMS TO SELECT COMPOSITIONS AND COMPARE THERMODYNAMIC ANALYZES USING THERMOCALC SOFTWARE WITH DIFFERENTIAL SCANNING CALORIMETRY (DSC) ANALYSIS, TO VERIFY IF THE PREDICTED PHASES AND TRANSFORMATIONS OCCUR IN THE MATERIAL. EQUILIBRIUM CALCULATIONS WERE PERFORMED TO MAP THE PROPORTION OF PHASES IN DIFFERENT COMPOSITIONS, OF WHICH FOUR WERE SELECTED. PSEUDO BINARY PHASES, SOLIDIFICATION AND PHASE EVOLUTION DIAGRAMS WITH TEMPERATURE WERE CALCULATED. THE SAMPLES WERE MADE WITH SELECTED COMPOSITIONS FOR ANALYSIS IN DSC AND SCANNING ELECTRON MICROSCOPY (SEM). A GOOD CORRELATION WAS FOUND BETWEEN THE ANALYZES SHOWING THAT THE METHOD CORRECTLY DESCRIBES THE PHASE TRANSFORMATIONS IN STEEL ALLOYED WITH AL AND NB

Palavras-chave

Aços Leves; FeMnAlC; DSC; Termodinâmica Computacional

Light Steels; FeMnAlC; DSC; Computational Thermodynamics