Título

AÇO MULTIFÁSICO 1,2 GPA PARA USO NA INDÚSTRIA AUTOMOTIVA

MULTI-PHASE STEEL FOR AUTOMOTIVE AND AUTO PARTS SEGMENTS

Autoria

Tolomelli, Flavia Tereza dos Santos Fernandes; Fernandes, Vinicius Santiago; Quinelato, Fernando Paulucio; Carvalho, Edgar Estevão de; Assunção, Fernando Cosme Rizzo; Lima, Renan de Melo Correia; Cotrim, Francisco de Assis Diniz; Araújo, Fabio de Oliveria; Salazar, Ranieiri Correa

DOI

10.5151/2594-5327-34659

Downloads

Baixar Artigo 37 Downloads

Resumo

UMA LIGA DE AÇO BAIXO CARBONO, C-MN-SI, COM ADIÇÕES DE CR, MO, NB E B FOI SUBMETIDA A VÁRIOS TRATAMENTOS TÉRMICOS EM ESCALA PILOTO, EM FORNO DE MUFLA, PARA DE OBTENÇÃO DE UM AÇO MULTIFÁSICO COM RESISTÊNCIA ACIMA DE 1,2 GPA. OS TRATAMENTOS TÉRMICOS CONSISTIRAM DE CICLOS DE AQUECIMENTO, ENCHARQUE EM CAMPO INTERCRÍTICO E RESFRIAMENTO PARA OBTENÇÃO DE MICROESTRUTURA MULTIFÁSICA. FORAM UTILIZADAS AS TÉCNICAS DE MICROSCOPIA ÓTICA, MICROSCOPIA ELETRÔNICA DE VARREDURA, ENSAIO DE DOBRAMENTO, ENSAIO DE TRAÇÃO E ENSAIO DE EXPANSÃO DE FURO PARA AVALIAR O DESEMPENHO DO PRODUTO. EM SEGUIDA FORAM REALIZADOS TESTES EM ESCALA INDUSTRIAL, EM UMA LINHA DE GALVANIZAÇÃO POR IMERSÃO A QUENTE, DO TIPO HORIZONTAL, COM FORNO DE RECOZIMENTO ACOPLADO, ONDE FORAM REPRODUZIDOS OS RESULTADOS OBTIDOS EM ESCALA PILOTO DE FORMA APRIMORADA. OS RESULTADOS OBTIDOS (LIMITE DE RESISTÊNCIA ACIMA DE 1200 MPA, LIMITE DE ESCOAMENTO ACIMA DE 800 MPA E ALONGAMENTO DA ORDEM DE 10%, INDICAM QUE O PRODUTO PODE SER UTILIZADO EM PEÇAS QUE REQUEREM ELEVADAS PROPRIEDADES ANTI-INTRUSÃO NOS SEGMENTOS AUTOMOTIVOS E DE AUTO-PEÇAS

 

A LOW CARBON STEEL ALLOY WITH CR, MO, NB AND B ADDITIONS WAS SUBJECTED TO VARIOUS HEAT TREATMENTS ON A PILOT SCALE, IN A MUFFLE FURNACE, TO OBTAIN A MULTIPHASE STEEL WITH STRENGTH ABOVE 1200 MPA. THE HEAT TREATMENTS CONSISTED OF HEATING CYCLES, SOAKING IN AN INTERCRITICAL FIELD AND COOLING TO OBTAIN THE MULTIPHASE MICROSTRUCTURE. THE TECHNIQUES OF OPTICAL MICROSCOPY, SCANNING ELECTRON MICROSCOPY, FOLDING TEST, TENSILE TEST AND HOLE EXPANSION TEST WERE USED TO EVALUATE THE PRODUCT PERFORMANCE. THEN, TESTS WERE CARRIED OUT ON AN INDUSTRIAL SCALE, ON A HOT DIP GALVANIZING LINE, OF THE HORIZONTAL TYPE, WITH AN ANNEALING FURNACE COUPLED, WHERE THE RESULTS OBTAINED ON A PILOT SCALE WERE REPRODUCED. THE RESULTS OBTAINED (RESISTANCE LIMIT ABOVE 1200 MPA, YIELD LIMIT ABOVE 800 MPA AND ELONGATION OF THE ORDER OF 10%) SUGGEST THAT THE PRODUCT CAN BE USED IN PARTS THAT REQUIRE HIGH ANTI-INTRUSION PROPERTIES IN THE AUTOMOTIVE AND AUTO SEGMENTS

Palavras-chave

MP1200, Complex phase; Multifásicos

Multi-phase Steel, Complex Phase Steel, MP1200