Título

APLICAÇÃO DO MÉTODO DE RIETVELD NA SÍNTESE E CARACTERIZAÇÃO DA HIDROXIAPATITA

APPLICATION OF THE RIETVELD METHOD IN THE SYNTHESIS AND CHARACTERIZATION OF HYDROXYAPATITE

Autoria

Nascimento, Damares da Cruz Barbosa; Belo, Francilene da Luz; Matos, Taiana de Sousa; Silva, Alisson Clay Rios da; Monteiro, Sérgio Neves; Vasconcelos, Esleane Vilela; Candido, Verônica Scarpini

DOI

10.5151/2594-5327-34972

Downloads

Baixar Artigo 10 Downloads

Resumo

A HIDROXIAPATITA É UMA BIOCERÂMICA QUE DESPERTA GRANDE INTERESSE CIENTÍFICO POR APRESENTAR SEMELHANÇAS AOS ÓSSOS E DENTES HUMANOS. O OBJETIVO DESTE ESTUDO FOI PRODUZIR E CARACTERIZAR MICROESTRUTURALMENTE A HIDROXIAPATITA UTILIZANDO A TÉCNICA DE PRECIPITAÇÃO E, MÉTODO DE VIA ÚMIDA E CALCINAÇÃO A 1000 ºC POR 2 HORAS. A OBTENÇÃO DO PÓ DE HA FOI POR MEIO DE UMA SOLUÇÃO COM PRECURSORES ÁCIDO-BASE A 1,5 MOLAR, DENTRE ESSES, ÁCIDO FOSFÓRICO (H3PO2), HIDRÓXIDO DE CÁLCIO (CA(OH2)) E HIDRÓXIDO DE AMÔNIO (NH4OH), PELO MÉTODO DE VIA ÚMIDA. EM SEGUIDA CARACTERIZOU-SE O PÓ POR DIFRAÇÃO DE RAIO – X (DRX), ESPECTROSCOPIA POR TRANSFORMADA DE FOURIER (FTIR) E ANÁLISES QUANTITATIVOS POR REFINAMENTO DE RIETVELD. OS RESULTADOS MOSTRARAM AS PRESENÇAS DAS FASES CRISTALINAS DE HIDROXIAPATITA E ÓXIDO DE CÁLCIO, ALÉM DE BANDAS DOS GRUPAMENTOS PO42-, CO32- E OH-. O REFINAMENTO DE RIETVELD APRESENTOU FASES QUANTITATIVAS DA HIDROXIAPATITA, CERCA DE 93,3% DE HA E 6,7% E GOF DE 1,15% DE ACORDO COM OS PARÂMETROS MATEMÁTICOS QUALITATIVOS COMUNS. A PARTIR DISSO, FOI POSSÍVEL CONSTATAR A OBTENÇÃO DA HIDROXIAPATITA COM ESTRUTURA HEXAGONAL, CONFIRMANDO E VIABILIDADE E O BAIXO CUSTO DA SÍNTESE UTILIZANDO O MÉTODO DE VIA ÚMIDA.

 

HYDROXYAPATITE IS A BIOCERAMIC THAT AROUSES GREAT SCIENTIFIC INTEREST BECAUSE IT HAS SIMILARITIES TO HUMAN BONES AND TEETH. THE OBJECTIVE OF THIS STUDY WAS TO PRODUCE AND MICROSTRUCTURALLY CHARACTERIZE THE HYDROXYAPATITE USING THE PRECIPITATION TECHNIQUE AND THE WET METHOD AND CALCINATION AT 1000 ºC FOR 2 HOURS. THE HA POWDER WAS OBTAINED THROUGH A SOLUTION WITH 1.5 MOLAR ACID-BASE PRECURSORS, INCLUDING PHOSPHORIC ACID (H3PO2), CALCIUM HYDROXIDE (CA(OH2)) AND AMMONIUM HYDROXIDE (NH4OH), AT WET METHOD. THEN, THE POWDER WAS CHARACTERIZED BY X-RAY DIFFRACTION (XRD), FOURIER TRANSFORM SPECTROSCOPY (FTIR) AND QUANTITATIVE ANALYSIS BY RIETVELD REFINEMENT. THE RESULTS SHOWED THE PRESENCE OF HYDROXYAPATITE AND CALCIUM OXIDE CRYSTALLINE PHASES, AS WELL AS BANDS OF PO42-, CO32- AND OH- GROUPS. THE RIETVELD REFINEMENT SHOWED QUANTITATIVE HYDROXYAPATITE PHASES, ABOUT 93.3% HA AND 6.7% AND 1.15% GOF ACCORDING TO COMMON QUALITATIVE MATHEMATICAL PARAMETERS. FROM THIS, IT WAS POSSIBLE TO VERIFY THE OBTAINING OF HYDROXYAPATITE WITH HEXAGONAL STRUCTURE, CONFIRMING THE VIABILITY AND LOW COST OF SYNTHESIS USING THE WET METHOD.

Palavras-chave

Hidroxiapatita; Biocerâmicas; Síntese; Caracterização

Hydroxypatite; Bioceramic; Synthesis; Characterization