A INJEçãO SOB PRESSãO DE METAIS NãO FERROSOS é UM PROCESSO ESSENCIAL PARA INDúSTRIAS QUE DEMANDAM COMPONENTES DE ALTA QUALIDADE E ALTOS VOLUMES. COM O AVANçO DA INDúSTRIA AUTOMOTIVA, HOUVE UM AUMENTO NA EXIGêNCIA DE QUALIDADE DOS COMPONENTES E DO RENDIMENTO DOS FERRAMENTAIS USADOS NESSES PROCESSOS. A NADCA ATRAVéS DO SEU GUIA #207 DEFINE UMA SéRIE DE EXIGêNCIAS EM RELAçãO à QUALIDADE DO AçO E CONTROLE DO PROCESSO DE TRATAMENTO TéRMICO DESSES FERRAMENTAIS. O ATENDIMENTO AOS REQUISITOS DESSA NORMA E A COMPROVAçãO TéCNICA DE RESULTADOS SãO ESSENCIAIS PARA GARANTIA DE RENDIMENTO DE MOLDES E MATRIZES DE ALTíSSIMO VALOR AGREGADO. DENTRE OS ENSAIOS DE APROVAçãO ESTá A AVALIAçãO METALOGRáFICA E DE TENACIDADE AO IMPACTO DE CORPOS DE PROVA PRESOS AO FERRAMENTAL DURANTE A TêMPERA. APESAR DO ALTO GRAU DE DETALHAMENTO DA NORMA, O ATENDIMENTO DE PONTOS BáSICOS INFELIZMENTE é NEGLIGENCIADO POR TRATADORES TéRMICOS. O PRESENTE ARTIGO APRESENTA TRêS SITUAçõES DE MATRIZES DE INJEçãO IDêNTICAS COM DIFERENTES RENDIMENTOS EM USO. OS RESULTADOS DOS ENSAIOS DE APROVAçãO DO TRATAMENTO TéRMICO APLICADO FORAM COMPARADOS COM RESULTADOS DA ANáLISE DE FALHA DAS FERRAMENTAS. POR CONTA DA INFLUêNCIA DO CICLO DE TRATAMENTO TéRMICO NA VIDA EM FADIGA DAS FERRAMENTAS DE INJEçãO, O ARTIGO ABRE UMA DISCUSSãO SOBRE O DESENVOLVIMENTO DE UM ENSAIO PRáTICO (E DE SIMPLES CONDUçãO) PARA AVALIAçãO DE TENACIDADE à FRATURA (KIC) A SER INCORPORADO àS EXIGêNCIAS DE APROVAçãO DA NADCA#207.

HIGH PRESSURE DIE CASTING OF NON-FERROUS METALS IS AN ESSENTIAL PROCESS FOR INDUSTRIES DEMANDING QUALITY AND HIGH-VOLUME COMPONENTS. WITH ADVANCEMENTS IN THE AUTOMOTIVE INDUSTRY, THERE HAS BEEN AN INCREASED DEMAND FOR QUALITY IN COMPONENTS AND THE PERFORMANCE OF TOOLS APPLIED. NADCA, THROUGH ITS GUIDE #207, DEFINES A SERIES OF REQUIREMENTS REGARDING STEEL QUALITY AND CONTROL OF THE HEAT TREATMENT PROCESS FOR THESE TOOLS. MEETING THESE STANDARDS AND TECHNICALLY VERIFYING RESULTS ARE CRUCIAL TO ENSURE THE PERFORMANCE OF HIGH-VALUE MOLDS AND DIES. AMONG THE APPROVAL TESTS ARE METALLOGRAPHIC EVALUATION AND IMPACT TOUGHNESS OF SPECIMENS ATTACHED TO THE TOOLING DURING QUENCHING. DESPITE THE HIGH LEVEL OF DETAIL IN THE STANDARD, BASIC COMPLIANCE IS UNFORTUNATELY NEGLECTED BY HEAT TREATERS. THIS ARTICLE PRESENTS THREE SCENARIOS OF IDENTICAL INJECTION MOLDS WITH VARYING PERFORMANCE LEVELS IN USE. THE RESULTS OF THE APPLIED HEAT TREATMENT APPROVAL TESTS WERE COMPARED WITH THE RESULTS OF TOOL FAILURE ANALYSIS. DUE TO THE INFLUENCE OF THE HEAT TREATMENT CYCLE ON THE FATIGUE LIFE OF INJECTION TOOLS, THE ARTICLE DISCUSSES THE DEVELOPMENT OF A PRACTICAL AND STRAIGHTFORWARD TEST FOR EVALUATING FRACTURE TOUGHNESS (KIC) TO BE INCORPORATED INTO THE NADCA #207 APPROVAL REQUIREMENTS.

Palavras-chave

Aço ferramenta; Tratamento Térmico; H11; Tenacidade

Tool steel; Heat Treatment; H11; Toughness.