AVALIAÇÃ DO COMPORTAMENTO TRIBOCORROSIVO DE MINÉRIOS DE FERRO POR MEIO DO ENSAIO MILLER (ASTM G75): ASSESSMENT OF THE TRIBOCORROSION BEHAVIOR OF IRON ORE USING THE MILLER TEST (ASTM G75)

ABRASãO E A CORROSãO SãO FENôMENOS COMUNS NA MINERAçãO, ESPECIALMENTE EM OPERAçõES QUE ENVOLVEM POLPA DE MINéRIO. EMBORA SE SAIBA QUE DIFERENTES TIPOS DE MINéRIOS DE FERRO APRESENTAM VARIADOS NíVEIS DE ABRASIVIDADE EM CONDIçõES SECAS, O EFEITO DA ABRASãO-CORROSãO DE MATERIAIS EM CONTATO COM POLPAS AINDA é POUCO ESTUDADO. ESTE ESTUDO BUSCA PREENCHER ESSA LACUNA, TENDO COMO PERGUNTA DE PESQUISA: QUAL O COMPORTAMENTO TRIBOCORROSIVO DO FERRO FUNDIDO BRANCO COM 27% DE CROMO EM CONTATO COM POLPAS DE MINéRIOS DE FERRO? PARA RESPONDER ESTA PERGUNTA DE PESQUISA O PRINCIPAL OBJETIVO DESTE TRABALHO FOI AVALIAR O COMPORTAMENTO TRIBOCORROSIVO DO FERRO FUNDIDO EM CONTATO COM POLPAS DE QUATRO MINéRIOS DE FERRO POR MEIO DO ENSAIO MILLER CONFORME A NORMA ASTM G75. O PRESENTE ESTUDO INVESTIGOU A ABRASIVIDADE DE POLPAS DE MINéRIOS DE FERRO E COMO A CORROSãO INFLUENCIA ESSA CARACTERíSTICA. OS RESULTADOS MOSTRARAM QUE O MINéRIO JASPELITO FOI O MAIS ABRASIVO, SEGUIDO PELA HEMATITA FRIáVEL, O MINéRIO HIDRATADO E A HEMATITA COMPACTA. A ANáLISE DA INFLUêNCIA DA CORROSãO INDICOU QUE MINéRIOS MAIS ABRASIVOS FAVORECEM O DESGASTE POR ABRASãO, ENQUANTO MINéRIOS MENOS ABRASIVOS FAVORECEM A CORROSãO. ESTE ESTUDO CONTRIBUI PARA O AVANçO DO CONHECIMENTO SOBRE O COMPORTAMENTO TRIBOCORROSIVO DE POLPAS DE MINéRIOS DE FERRO, FORNECENDO INFORMAçõES RELEVANTES PARA A SELEçãO E O DESENVOLVIMENTO DE MATERIAIS MAIS ADEQUADOS PARA OS EQUIPAMENTOS DA MINERAçãO.

ABRASION AND CORROSION ARE COMMON IN MINING INDUSTRY, ESPECIALLY IN OPERATIONS INVOLVING ORE SLURRIES. ALTHOUGH IT IS KNOWN THAT DIFFERENT TYPES OF IRON ORES HAVE VARYING LEVELS OF ABRASIVENESS UNDER DRY CONDITIONS, THE EFFECT OF ABRASION-CORROSION OF MATERIALS IN CONTACT WITH IRON ORE SLURRIES IS STILL LITTLE STUDIED. THIS STUDY SEEKS TO FILL THIS GAP, WITH THE FOLLOWING RESEARCH QUESTION: WHAT IS THE TRIBOCORROSIVE BEHAVIOR OF WHITE CAST IRON WITH 27% CHROMIUM IN CONTACT WITH IRON ORES SLURRIES? TO ANSWER THIS RESEARCH QUESTION, THE MAIN OBJECTIVE OF THIS WORK WAS TO EVALUATE THE TRIBOCORROSIVE BEHAVIOR OF CAST IRON IN CONTACT WITH FOUR IRON ORES USING THE MILLER TEST ACCORDING TO ASTM G75. THIS STUDY INVESTIGATED THE ABRASIVENESS OF IRON ORES SLURRIES AND HOW CORROSION INFLUENCES THIS CHARACTERISTIC. THE RESULTS SHOWED THAT JASPELITE ORE WAS THE MOST ABRASIVE, FOLLOWED BY FRIABLE HEMATITE, HYDRATED ORE AND COMPACT HEMATITE. ANALYSIS OF THE INFLUENCE OF CORROSION INDICATED THAT MORE ABRASIVE ORES FAVORED ABRASIVE WEAR, WHILE LESS ABRASIVE ORES PROMOTED CORROSION. THIS STUDY CONTRIBUTES TO THE ADVANCEMENT OF KNOWLEDGE ON THE TRIBOCORROSIVE EFFECT OF IRON ORES SLURRIES, PROVIDING RELEVANT INFORMATION FOR THE SELECTION AND DEVELOPMENT OF MORE SUITABLE MATERIALS FOR MINING EQUIPMENT.

Palavras-chave

Minério de ferro; Abrasividade; Desgaste; Ensaio Miller.

Iron ore. Abrasiveness. Wear. Miller test.

Como citar

PINTO, LEANDRO MOREIRA; SANTOS, JEILCE MARIA ABREU DOS; PENAGOS, JOSÉ JIMMY; ARANGO, CRISTIAN CAMILO VIÁFARA; MION, FELIPE SILVA; PINTO, MARIA APARECIDA. AVALIAÇÃ DO COMPORTAMENTO TRIBOCORROSIVO DE MINÉRIOS DE FERRO POR MEIO DO ENSAIO MILLER (ASTM G75) , p. 104-115. In: 20º Seminário de Moldes, Matrizes e Ferramentas, São Paulo, Brasil, 2024.
ISSN: 5463-5463 , DOI 10.5151/5463-5463-41379