AVALIAÇÃO DO COMPORTAMENTO DAS TRAÇÕES TRATIVAS EM COMPÓSITOS DE MATRIZ POLIESTER REFORÇADOS COM FIBRAS DE SISAL, BAMBU E MALVA

TENSILE PROPERTIES OF POLYESTER COMPOSITES REINFORCED WITH CONTINUOUS SISAL, BAMBOO AND MALVA FIBERS

Autoria

Margem, Jean Igor; Margem, Marina Rangel; Moraes, Ygor Macabu de; Margem, Frederico Muylaert; Monteiro, Sergio Neves

DOI

10.5151/1516-392X-30808

Downloads

Baixar Artigo 287 Downloads

Resumo

Nestes dias materiais ecológicos como compósitos com fibras naturais em matriz polimérica estão chamando a atenção de pesquisadores científicos, devido ao seu bom desempenho na substituição de materiais como madeira, polímeros à base de petróleo e outros. Neste trabalho foram avaliadas as propriedades de tração de compósitos de matriz poliéster reforçados com diferentes espécimes de fibras lignocelulósicas. Compósitos reforçados com até 30% em volume de fibras longas, contínuas e alinhadas de malva, sisal e bambu foram testados em uma máquina Instron a temperatura ambiente. A fratura foi analisada por SEM. Os resultados mostraram alterações significativas nas propriedades mecânicas com a quantidade dessas fibras. Estas propriedades mecânicas foram comparados com outros resultados em compósitos testados em ensaio de tração. Como esperado, a análise da fratura revelou uma fraca interação da interface fibra / matriz, o que corrobora o comportamento típico das fibras naturais quando incorporadas em matriz polimérica.

 

In these days environmentally friendly materials as composites with natural fibers in polymeric matrix are gained attention of scientific researchers, due to its good performance in the replacement of materials such as wood, petroleum-based polymers and other. In this work the tensile properties of polyester matrix composites reinforced with different specimens of lignocellulosic fibers were evaluated. Composites reinforced with up to 30% in volume of long, continuous and aligned malva, sisal, and bamboo fibers were room temperature tested in an Instron machine. The fracture was analyzed by SEM. The results showed significant changes in the mechanical properties with the amount of those fibers. These mechanical properties were compared with other tensile-tested composites results. The fracture analysis revealed a weak fiber/matrix interface, which could be responsible for the higher performance of some properties. As expected, the fracture analysis revealed a poor interaction of the fiber / matrix interface, which corroborates the typical behavior of natural fibers when incorporated into a polymeric matrix.

Palavras-chave

Fibras de Sisal, Bambo, Malva, Matriz Poliester, Ensaio Tração

Sisal, Bamboo, Malva Fibers, Polyester Matrix, Tensile Strength Tests