Título

AVALIAÇÃO COMPARATIVA DA APTIDÃO PARA O PROCESSO DE TÊMPERA E PARTIÇÃO DE DUAS LIGAS DE AÇOS MICROLIGADOS DE ALTA RESISTÊNCIA MECÂNICA

COMPARATIVE ASSESSMENT OF THE ABILITY FOR THE QUENCHING AND PARTITIONING OF TWO HIGH STRENGHT MICROALLOYED STEELS

Autoria

Tolomelli, Flavia Tereza dos Santos Fernandes; Paula, Andersan dos Santos; Assunção, Fernando Cosme Rizzo

DOI

10.5151/2594-5327-34838

Downloads

Baixar Artigo 9 Downloads

Resumo

UMA AVALIAÇÃO COMPARATIVA DE DUAS LIGAS DE AÇOS MICROLIGADOS DE ALTA RESISTÊNCIA, QUANTO ÀS SUAS APTIDÕES PARA O PROCESSO DE TÊMPERA E PARTIÇÃO (T&P) FOI REALIZADA. O ESTUDO FOI CONDUZIDO COM AUXÍLIO DO PROGRAMA THERMOCALC (TCFE9) QUE SERVIU DE BASE PARA A DETERMINAÇÃO DA COMPOSIÇÃO DA AUSTENITA NO CAMPO INTERCRÍTICO, DETERMINAÇÃO DAS TEMPERATURAS DE EQUILÍBRIO DE FASES (AE1 E AE3) E OBTENÇÃO DOS MAPAS DE PRECIPITAÇÃO DAS REFERIDAS LIGAS. FORAM UTILIZADAS EQUAÇÕES EMPÍRICAS PARA DETERMINAÇÃO DAS TEMPERATURAS DE INÍCIO DAS TRANSFORMAÇÕES DE FASE BAINÍTICA E MARTENSÍTICA (BI E MI) AS QUAIS FORAM UTILIZADAS PARA A REALIZAÇÃO DOS TRATAMENTOS TÉRMICOS DE TÊMPERA E PARTIÇÃO DE UM ESTÁGIO. OS TRATAMENTOS TÉRMICOS FORAM FEITOS EM ESCALA PILOTO, EM FORNO TIPO MUFLA, COM MONITORAMENTO DE TEMPERATURA E COM RESFRIAMENTO EM ÓLEO. O SOFTWARE IMAGEJ FOI UTILIZADO PARA ANÁLISE QUANTITATIVA DAS LIGAS DE FORMA A SE TER UMA ESTIMATIVA DO PERCENTUAL DE AUSTENITA RETIDA PRESENTE NAS LIGAS (ESTIMADA EM FUNÇÃO DO % DE CONSTITUINTE MA). COMO CONCLUSÃO DO TRABALHO FOI OBSERVADO QUE A LIGA A, COM ADIÇÕES DE MO-TI-NB-B (MA > 9%) COMPARATIVAMENTE À LIGA B COM ADIÇÕES DE CR-MO-NB-B (%MA < 8%) APRESENTOU OS MAIORES VALORES DE ALONGAMENTO TOTAL INDICANDO QUE ESSA LIGA APRESENTA MAIOR APTIDÃO AO PROCESSO DE T&P.

 

A COMPARATIVE EVALUATION OF TWO HIGH STRENGTH LOW ALLOY STEELS, REGARDING THEIR ABILITY FOR THE QUENCHING AND PARTITIONING (T&P) PROCESS, WAS PERFORMED. TO CARRY OUT THE STUDY, THE THERMOCALC PROGRAM WAS USED WITH A DATABASE IN THE TCFE9 VERSION, WHICH SERVED AS THE BASIS FOR: DETERMINATION OF THE COMPOSITION OF AUSTENITE IN THE INTERCRITICAL FIELD; DETERMINATION OF THE EQUILIBRIUM TEMPERATURES OF PHASES THAT DELIMIT THE INTERCRITICAL FIELD (AE1 AND AE3), AND OBTAINING THE PRECIPITATION MAPS OF THE REFERRED ALLOYS. WITH THE AID OF EMPIRICAL EQUATIONS, THE ONSET TEMPERATURES OF THE BAINITIC AND MARTENSITIC TRANSFORMATIONS (BI AND MI) WERE DETERMINED, WHICH WERE USED AS A BASIS FOR THE PERFORMANCE OF THE ONE-STAGE QUENCHING AND PARTITIONING HEAT TREATMENTS. THE QUENCHING HEAT TREATMENTS WERE CARRIED OUT ON A PILOT SCALE IN A MUFFLE FURNACE WITH TEMPERATURE MONITORING AND OIL COOLING. THE IMAGEJ SOFTWARE WAS USED FOR QUANTITATIVE ANALYSIS OF THE ALLOYS IN ORDER TO HAVE AN ESTIMATE OF THE PERCENTAGE OF RETAINED AUSTENITE PRESENT IN THE ALLOYS (ESTIMATED AS A FUNCTION OF THE % OF MA CONSTITUENT). AS A CONCLUSION OF THE WORK, IT WAS OBSERVED THAT ALLOY A, WITH ADDITIONS OF MO-TI-NB-B (MA > 9%) COMPARED TO ALLOY B WITH ADDITIONS OF CR-MO-NB-B (%MA < 8%) PRESENTED THE HIGHER VALUES OF TOTAL ELONGATION INDICATING THAT THIS ALLOY HAS GREATER SUITABILITY FOR THE T&P PROCESS.

Palavras-chave

Aços microligados; T&P; Têmpera, Partição

Microalloyed steels; Q&P; Quenching; Partitioning