Título

AVALIAÇÃO DA ADERÊNCIA DA CAREPA PRIMÁRIA

EVALUATION OF PRIMARY OXIDE SCALE ADHERENCE

Autoria

Santiago, Gabriel Augusto de Avila; Araujo, Fábio de Oliveira; Netto, Vitor Hugo Maia; Tavares, Rogério Itaborahy; Cunha, Raphael Alexsander Ribeiro da

DOI

10.5151/2594-5327-34627

Downloads

Baixar Artigo 10 Downloads

Resumo

A FORMAÇÃO DE UMA CAMADA SUPERFICIAL DE ÓXIDO (CAREPA) DURANTE O REAQUECIMENTO DAS PLACAS DE AÇO É INEVITÁVEL. DURANTE A PASSAGEM DA PLACA PELO FORNO, DIFERENTES VARIÁVEIS PODEM AFETAR TANTO A CINÉTICA COMO A FORMA DA CAREPA FORMADA. OS ELEMENTOS DE LIGA PRESENTES NO AÇO AFETAM POR MEIO DE DIFERENTES MECANISMOS A MORFOLOGIA DA CAREPA GERADA, EM GERAL DIMINUINDO A CINÉTICA DE SUA FORMAÇÃO E/OU AUMENTANDO A ADERÊNCIA DA CAMADA DE ÓXIDO COM O METAL. ESTE TRABALHO AVALIOU A INFLUÊNCIA DO MN E DO SI NA FORMAÇÃO DA CAREPA EM AÇOS PROCESSADOS EM UM LAMINADOR DE TIRAS A QUENTE. APÓS A PASSAGEM PELO FORNO DE REAQUECIMENTO, AMOSTRAS FORAM ANALISADAS POR MICROSCOPIA ÓTICA E MICROSCOPIA ELETRÔNICA DE VARREDURA, INCLUINDO A DETERMINAÇÃO VIA EDS DAS FASES FORMADAS E A PRESENÇA DE ELEMENTOS DE LIGA. OS RESULTADOS INDICARAM A POSSIBILIDADE DE FORMAÇÃO DE FAYALITA, DO APARECIMENTO DE POROSIDADE E DO MECANISMO “DELAMINAÇÃO”. TAIS MECANISMOS SÃO PREJUDICIAIS À QUALIDADE DO MATERIAL, E SUA OCORRÊNCIA ESTÁ RELACIONADA COM A ADERÊNCIA DE CAREPA PRIMÁRIA.

 

FORMATION OF A SUPERFICIAL OXIDE LAYER (SCALE) DURING THE REHEATING OF STEEL PLATES IS INEVITABLE. DURING THE PASSAGE OF THE PLATE THROUGH THE WALKING BEAM FURNACE, DIFFERENT VARIABLES CAN AFFECT BOTH THE KINETICS AND THE SHAPE OF THE FORMED SCALE. THE ALLOYING ELEMENTS PRESENT IN THE CHEMICAL COMPOSITION OF STEEL AFFECT, THROUGH DIFFERENT MECHANISMS, THE MORPHOLOGY OF THE GENERATED SCALE, IN GENERAL DECREASING THE KINETICS OF ITS FORMATION AND/OR INCREASING THE ADHESION OF THE OXIDE LAYER WITH STEEL. THIS WORK EVALUATED THE INFLUENCE OF MN AND SI ON THE SCALE FORMATION IN STEELS PROCESSED IN A HOT STRIP ROLLING MILL. AFTER PASSING THROUGH THE REHEATING FURNACE, SAMPLES WERE ANALYZED USING OPTICAL MICROSCOPY AND SCANNING ELECTRON MICROSCOPY, INCLUDING THE DETERMINATION VIA EDS OF THE PHASES FORMED AND THE PRESENCE OF ALLOYING ELEMENTS. THE RESULTS INDICATED THE POSSIBILITY OF FAYALITE FORMATION, THE APPEARANCE OF POROSITY AND THE "DELAMINATION" MECHANISM. SUCH MECHANISMS ARE HARMFUL TO THE QUALITY OF THE MATERIAL, AND THEIR OCCURRENCE IS RELATED TO THE ADHERENCE OF PRIMARY SCALE.

Palavras-chave

Carepa; Reaquecimento de Placas de Aço; Fayalita

Oxide Scale; Reheating of Steel Plates; Fayalite