AVALIAçãO DA CORROSãO POR CLORETOS EM CâMARAS DE SPRAY NO PROCESSO DE LINGOTAMENTO CONTíNUO DE PLACAS

EVALUATION OF CHLORIDE CORROSION IN SPRAY CHAMBERS IN THE CONTINUOUS SLAB CASTING PROCESS

DOI

10.5151/2594-3626-41216

Downloads

Baixar Artigo 1 Downloads

Resumo

O CONTATO DA áGUA COM A PLACA A TEMPERATURAS SUPERIORES A 1300 ºC DESENCADEIA SUA VAPORIZAçãO, INICIANDO O PROCESSO CORROSIVO CONHECIDO COMO ESFOLIAçãO NAS ESTRUTURAS DA CâMARA. DIANTE DISSO, O OBJETIVO DESTA PESQUISA é AVALIAR A CORROSãO NA CâMARA DE SPRAY, CAUSADA POR CLORETOS PRESENTES NA áGUA DE RESFRIAMENTO. O USO DE HIPOCLORITO DE SóDIO COMO BIOCIDA é A PRINCIPAL FONTE DOS CLORETOS NESSE SISTEMA, POIS A APLICAçãO DE BIOCIDAS é NECESSáRIA PARA O CONDICIONAMENTO QUíMICO DA áGUA. PARA ISSO, FORAM REALIZADOS ENSAIOS DE EMERSãO, DE MICROSCOPIA óPTICA PARA INVESTIGAR A SUPERFíCIE DAS AMOSTRAS, OBTENçãO DE CURVAS DE POLARIZAçãO, E TESTES INDUSTRIAIS COM CORPOS DE PROVA. FORAM FEITOS EXPERIMENTOS SIMULANDO O CONDICIONAMENTO QUíMICO EM CONDIçõES REAIS DE OPERAçãO, VISANDO DETERMINAR AS TAXAS DE CORROSãO. OS RESULTADOS EVIDENCIAM UMA REDUçãO DE APROXIMADAMENTE 50% NA TAXA DE CORROSãO QUANDO A CONCENTRAçãO DE CLORETOS FOI DIMINUíDA NO AMBIENTE OPERACIONAL, VALIDANDO OS ACHADOS OBTIDOS NOS ENSAIOS DE IMERSãO/EMERSãO E NAS ANáLISES ELETROQUíMICAS. ESSE CENáRIO APONTA PARA UMA SIGNIFICATIVA MITIGAçãO DOS EFEITOS DA CORROSãO, COM IMPLICAçõES POSITIVAS NA ECONOMIA E NA DURABILIDADE DAS ESTRUTURAS METáLICAS DENTRO DA CâMARA DE SPRAY.

 

THE CONTACT OF WATER WITH THE PLATE AT TEMPERATURES EXCEEDING 1300 ºC TRIGGERS ITS VAPORIZATION, INITIATING THE CORROSIVE PROCESS KNOWN AS EXFOLIATION WITHIN THE CHAMBER STRUCTURES. IN LIGHT OF THIS, THE OBJECTIVE OF THIS RESEARCH IS TO ASSESS CORROSION IN THE SPRAY CHAMBER CAUSED BY CHLORIDES PRESENT IN THE WATER USED FOR COOLING. THE USE OF SODIUM HYPOCHLORITE AS A BIOCIDE IS THE PRIMARY SOURCE OF CHLORIDES IN THIS SYSTEM, AS THE APPLICATION OF BIOCIDES IS ESSENTIAL FOR THE CHEMICAL CONDITIONING OF WATER. TO ACHIEVE THIS, IMMERSION TESTS, POLARIZATION CURVE ACQUISITION, OPTICAL MICROSCOPY ASSAYS TO INVESTIGATE SAMPLE SURFACES, AND INDUSTRIAL TESTS WITH SPECIMENS WERE CONDUCTED. EXPERIMENTS SIMULATING CHEMICAL CONDITIONING UNDER REAL OPERATING CONDITIONS WERE PERFORMED TO DETERMINE CORROSION RATES AFTER THE USE OF SODIUM BROMIDE AS A BIOCIDE. THE RESULTS DEMONSTRATE AN APPROXIMATELY 50% REDUCTION IN CORROSION RATE WHEN CHLORIDE CONCENTRATION WAS DECREASED IN THE OPERATIONAL ENVIRONMENT, VALIDATING THE FINDINGS OBTAINED IN IMMERSION/EMERSION TESTS AND ELECTROCHEMICAL ANALYSES. THIS SCENARIO POINTS TOWARDS A SIGNIFICANT MITIGATION OF CORROSION EFFECTS, WITH POSITIVE IMPLICATIONS FOR THE ECONOMY AND DURABILITY OF METALLIC STRUCTURES WITHIN THE SPRAY CHAMBER..

Palavras-chave

Corrosão; Corrosão por cloretos; Ensaios de campo; Impedância eletroquímica.

Corrosion; Chloride corrosion; Field tests; Electrochemical impedance.