AVALIAÇÃO DA DUREZA VICKERS NO COMPÓSITO DE MATRIZ CERÂMICA DE SIC COM LAS: EVALUATION OF VICKERS HARDNESS IN THE SIC CERAMIC MATRIX COMPOSITE WITH LAS

É INEGÁVEL QUE A RELEVÂNCIA DOS COMPÓSITOS DE MATRIZ CERÂMICA (CMC) TEM CRESCIDO NOS MEIOS CIENTÍFICOS E INDUSTRIAIS. A COMBINAÇÃO DOS DIFERENTES MATERIAIS CERÂMICOS PERMITE MITIGAR DIFICULDADES DE FABRICAÇÃO E PROCESSAMENTO OU MELHORAR O DESEMPENHO QUE CADA MATERIAL TERIA ISOLADAMENTE. PARA INVESTIGAR O CMC FORMADO POR CARBETO DE SILÍCIO (SIC), ALUMINA (AL2O3), ÍTRIA (Y2O3) E VITROCERÂMICA DO SISTEMA LÍTIO-ALUMÍNIO-SILÍCIO (LAS), FORAM PREPARADAS 6 AMOSTRAS DE CADA ADITIVAÇÃO REFERENTE AO PERCENTUAL EM PESO DE LAS, SENDO 0, 1, E 5 %. O MATERIAL FOI MISTURADO EM MOINHO VERTICAL POR 1 HORA A SECO. A MISTURA RESULTANTE FOI PRENSADA COM 175 MPA, UNIAXIALMENTE, E SINTERIZADA A 1800ºC. APÓS SINTERIZADO, O CMC FOI CARACTERIZADO POR MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV) E DUREZA VICKERS. PARA APLICAÇÃO DA DUREZA VICKERS, A CONDIÇÃO DE PROCESSAMENTO DO GRUPO COM 1% EM PESO DE LAS SE MOSTROU A MELHOR, COM VALOR MÉDIO DE 25,11 ± 1,67 GPA.

IT IS UNDENIABLE THAT THE RELEVANCE OF CERAMIC MATRIX COMPOSITES (CMC) HAS GROWN IN SCIENTIFIC AND INDUSTRIAL CIRCLES. THE COMBINATION OF DIFFERENT CERAMIC MATERIALS ALLOWS TO MITIGATE DIFFICULTIES IN MANUFACTURING AND PROCESSING OR TO IMPROVE THE PERFORMANCE THAT EACH MATERIAL WOULD HAVE IN ISOLATION. TO INVESTIGATE THE CMC FORMED BY SILICON CARBIDE (SIC), ALUMINA (AL2O3), YTTRIA (Y2O3) AND GLASS-CERAMICS FROM THE LITHIUM-ALUMINUM-SILICON SYSTEM (LAS), 6 SAMPLES OF EACH ADDITIVE WERE PREPARED REGARDING THE WEIGHT PERCENTAGE OF LAS, 0, 1, AND 5%. THE MATERIAL WAS DRY MIXED IN A VERTICAL MILL FOR 1 HOUR. THE MIXTURE WAS PRESSED WITH 175 MPA, UNIAXIALLY, AND SINTERED AT 1800ºC. AFTER SINTERED, THE CMC WAS CHARACTERIZED BY SCANNING ELECTRON MICROSCOPY (SEM) AND VICKERS HARDNESS. FOR THE APPLICATION OF VICKERS HARDNESS, THE PROCESSING CONDITION OF THE GROUP WITH 1%W OF LAS PROVED TO BE THE BEST, WITH AN AVERAGE VALUE OF 25.11 ± 1.67 GPA.

Palavras-chave

SiC; LAS; Sinterização; Vickers

SiC; LAS; SinteriNG; Vickers

Como citar

Carvalho, Magno Torres; Campos, José Brant de; Melo, Francisco Cristovão Lourenço de; Lima, Eduardo de Sousa. AVALIAÇÃO DA DUREZA VICKERS NO COMPÓSITO DE MATRIZ CERÂMICA DE SIC COM LAS , p. 2646-2659. In: 75° Congresso Anual da ABM, São Paulo, 2022.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-34550