Título

AVALIAÇÃO DA EFICÁCIA DE MÉTODOS EXPERIMENTAIS PARA INCORPORAÇÃO DE ESPODUMÊNIO COMO REFORÇO EM COMPÓSITO COM MATRIZ METÁLICA DE LIGA DE ALUMÍNIO A356.0

EFFICACY EVALUATION OF EXPERIMENTAL METHODS AIMING TO INCORPORATE SPODUMENE AS STRENGTHENING COMPOUND IN A METALLIC COMPOSITE WITH A356.0 ALUMINUM ALLOY MATRIX

DOI

10.5151/2594-5327-40516

Downloads

Baixar Artigo 5 Downloads

Resumo

NAS úLTIMAS DéCADAS, A BUSCA POR MATERIAIS DE BAIXA DENSIDADE E BOM DESEMPENHO MECâNICO TEM FOMENTADO INúMEROS ESTUDOS SOBRE COMPóSITOS DE MATRIZ METáLICA (CMM). DIVERSOS TIPOS DE MATERIAIS TêM SIDO INVESTIGADOS COMO POSSIBILIDADE DE REFORçO EM MATRIZES CONSTITUíDAS POR LIGAS DE ALUMíNIO. NESTE CONTEXTO, O PRESENTE TRABALHO APRESENTA UMA AVALIAçãO PIONEIRA SOBRE A EFICáCIA DE DIFERENTES MéTODOS DE FABRICAçãO (EM ESCALA EXPERIMENTAL) PARA INCORPORAçãO DE ESPODUMêNIO (ALUMINOSSILICATO DE LíTIO) COMO REFORçO EM COMPóSITO COM MATRIZ METáLICA DE LIGA DE ALUMíNIO A356.0. INVESTIGOU-SE OS SEGUINTES PROCESSOS: (I) FUSãO COM AGITAçãO ELETROMAGNéTICA E ADIçãO DO REFORçO A FRIO; (II) FUSãO COM AGITAçãO ELETROMAGNéTICA E ADIçãO DO REFORçO A QUENTE; (III) FUSãO COM AGITAçãO ELETROMAGNéTICA E ADIçãO DO REFORçO A QUENTE SEGUIDO DE AGITAçãO MECâNICA; (IV) PROCESSAMENTO NO ESTADO SEMI-SóLIDO. BASEADO NOS RESULTADOS OBTIDOS, MOSTROU-SE QUE é POSSíVEL OBTER UM COMPóSITO DE MATRIZ METáLICA REFORçADO POR ESPODUMêNIO COM MICROESTRUTURA HOMOGêNEA E POUCO POROSA, SENDO O PROCESSAMENTO NO SEMI-SóLIDO O MAIS PROMISSOR ENTRE OS AQUI AVALIADOS.

 

IN LAST DECADES, THE DEMAND FOR LOW-DENSITY MATERIALS WITH GREAT MECHANICAL BEHAVIOR HAS SPURRED RESEARCH ON METALLIC MATRIX COMPOSITES (MMCS). SEVERAL MATERIALS HAVE BEEN STUDIED AS POTENTIAL REINFORCEMENT PARTICLES IN ALUMINUM MATRICES. IN THIS CONTEXT, THIS STUDY PRESENTS AN INEDITED EVALUATION ABOUT THE EFFICACY OF DIFFERENT MANUFACTURING METHODS AIMING TO INCORPORATE SPODUMENE (LITHIUM ALUMINOSILICATE) AS REINFORCEMENT IN A COMPOSITE MATERIAL WITH AN A356.0 ALUMINUM ALLOY MATRIX. THE EVALUATED PROCESSES WERE: (I) MELTING WITH ELECTROMAGNETIC STIRRING AND COLD REINFORCEMENT PARTICLE ADDITION; (II) MELTING WITH ELECTROMAGNETIC STIRRING AND HOT REINFORCEMENT PARTICLE ADDITION; (III) MELTING WITH ELECTROMAGNETIC STIRRING AND HOT REINFORCEMENT PARTICLE ADDITION FOLLOWED BY MECHANICAL STIRRING; (IV) SEMI-SOLID PROCESSING. BASED ON THE OBTAINED RESULTS, IT WAS CONCLUDED THAT IT IS POSSIBLE TO MANUFACTURE A HOMOGENEOUS AND LOW-POROSITY METALLIC MATRIX COMPOSITE REINFORCED WITH SPODUMENE. THE MOST PROMISING EVALUATED METHOD WAS THE SEMI-SOLID PROCESSING.

Palavras-chave

Compósito de matriz metálica; Liga de alumínio A356.0; Espodumênio; Métodos de incorporação.

Metallic matrix composite; Aluminum alloy A356.0; Spodumene; Incorporation method; Microstructure.

Como citar

FARIA, GERALDO LUCIO DE; MELO, DENILSON PEREIRA; MOREIRA, PAULO SÉRGIO; GONÇALVES, ALICE SILVA; REIS, ÉRICA LINHARES; SILVA, MARIANA CAROLINE ANDRADE. AVALIAÇÃO DA EFICÁCIA DE MÉTODOS EXPERIMENTAIS PARA INCORPORAÇÃO DE ESPODUMÊNIO COMO REFORÇO EM COMPÓSITO COM MATRIZ METÁLICA DE LIGA DE ALUMÍNIO A356.0 , p. 387-399. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.