OS TIJOLOS DE SOLO-CIMENTO SãO CONHECIDOS COMO TIJOLOS ECOLóGICOS, EMBORA UTILIZAREM CIMENTO, POIS EMPREGAM MATERIAIS DE MENOR VALOR AGREGADO, CAUSAM MENOR IMPACTO AMBIENTAL E PERMITEM A INCORPORAçãO DE DIVERSOS RESíDUOS EM SUA COMPOSIçãO. NESSE CONTEXTO, NA PRESENTE PESQUISA FORAM PRODUZIDOS E AVALIADOS TIJOLOS DE SOLO-CIMENTO COM A ADIçãO DE REJEITOS DE MINéRIO DE FERRO. FORAM DESENVOLVIDAS QUATRO COMPOSIçõES DE BLOCOS: COMPOSIçãO DE REFERêNCIA (TR: APENAS SOLO); SOLO COM 5% (T1), 15% (T2) E 20% (T3) DE RESíDUOS DE REJEITO DE MINéRIO. OS ENSAIOS INCLUíRAM A ABSORçãO DE ÁGUA INICIAL (AAI), A ABSORçãO DE ÁGUA E A RESISTêNCIA A COMPRESSãO. QUANTO à AAI, NãO HOUVE VARIAçãO ESTATíSTICA ENTRE OS TIJOLOS COM AS COMPOSIçõES. A ABSORçãO DE áGUA (AA) INDICOU VALORES VARIANDO DE "13,8±2,52% A 17,1±1,01%" , AOS 28 DIAS. A RESISTêNCIA à COMPRESSãO FOI AVALIADA AOS 7 E 28 DIAS DE CURA, COM VALORES SUPERIORES A 1",8±0,2 MPA" DE RESISTêNCIA. OS RESULTADOS MOSTRARAM QUE TODOS OS TIJOLOS APRESENTARAM COMPOSIçõES INTERESSANTES PARA A FABRICAçãO DE TIJOLOS DE SOLO-CIMENTO, POIS A INCORPORAçãO DE RESíDUO CERâMICO NãO COMPROMETEU AS PROPRIEDADES TECNOLóGICAS. CONCLUI-SE COM AS INFORMAçõES DA PRESENTE PESQUISA QUE, POR QUESTõES AMBIENTAIS, A COMPOSIçãO COM 20% DE RESíDUO é MAIS INDICADA.
SOIL-CEMENT BRICKS ARE KNOWN AS ECOLOGICAL BRICKS, ALTHOUGH THEY USE CEMENT, AS THEY USE MATERIALS WITH LOWER ADDED VALUE, CAUSE LESS ENVIRONMENTAL IMPACT AND ALLOW THE INCORPORATION OF VARIOUS WASTES INTO THEIR COMPOSITION. IN THIS CONTEXT, IN THE PRESENT RESEARCH, SOIL-CEMENT BRICKS WERE PRODUCED AND EVALUATED WITH THE ADDITION OF IRON ORE WASTE. FOUR BLOCK COMPOSITIONS WERE DEVELOPED: REFERENCE COMPOSITION (TR: SOIL ONLY); SOIL WITH 5% (T1), 15% (T2) AND 20% (T3) ORE WASTE RESIDUES. THE TESTS INCLUDED INITIAL WATER ABSORPTION (AAI), WATER ABSORPTION AND COMPRESSIVE STRENGTH. AS FOR AAI, THERE WAS NO STATISTICAL VARIATION BETWEEN THE BRICKS WITH THE COMPOSITIONS. WATER ABSORPTION (AA) INDICATED VALUES RANGING FROM "13.8±2.52% TO 17.1±1.01%" AT 28 DAYS. COMPRESSIVE STRENGTH WAS EVALUATED AT 7 AND 28 DAYS OF CURING, WITH VALUES GREATER THAN 1.8±0.2 MPA" OF RESISTANCE. THE RESULTS SHOWED THAT ALL BRICKS PRESENTED INTERESTING COMPOSITIONS FOR THE MANUFACTURE OF SOIL-CEMENT BRICKS, AS THE INCORPORATION OF CERAMIC WASTE DID NOT COMPROMISE THE TECHNOLOGICAL PROPERTIES. IT IS CONCLUDED WITH THE INFORMATION FROM THIS RESEARCH THAT, FOR ENVIRONMENTAL REASONS, THE COMPOSITION WITH 20% RESIDUE IS MORE INDICATED.
Palavras-chave
Solo-Cimento; Incorporação de Resíduos; rejeito de Minério de Ferro; Tijolos Ecológicos
Soil-Cement; Waste Incorporation; Iron Ore Reject; Ecological Bricks.
Como citar
CERQUEIRA, NIANDER AGUIAR;
JUNIOR, ELIAS SÓCRATES DO NASCIMENTO;
ALVES, GABRYEL DE CARVALHO;
CEREJA, KEIZE DELVALLE DOS SANTOS FERRAZ;
AZEVEDO, AFONSO RANGEL GARCEZ DE;
XAVIER, GUSTAVO DE CASTRO;
ALEXANDRE, JONAS.
AVALIAÇÃO DA INCORPORAÇÃO DE REJEITOS DE MINÉRIO NA PRODUÇÃO DE TIJOLO DE SOLO-CIMENTO
,
p. 1633-1640.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-40897