AVALIAÇÃO DA INCORPORAÇÃO DE RESÍDUO DE AÇO INOX EM ARGAMASSAS DE REVESTIMENTO NO ESTADO ENDURECIDO: EVALUATION OF THE INCORPORATION OF STAINLESS STEEL WASTE IN COATING MORTARS IN THE HARDENED STATE

A BUSCA POR SOLUçõES INOVADORAS E SUSTENTáVEIS NA INDúSTRIA DA CONSTRUçãO CIVIL TORNOU-SE IMPERATIVA DIANTE DA CRESCENTE DEMANDA POR RECURSOS NATURAIS. ESTE ESTUDO ABORDA A UTILIZAçãO DE RESíDUOS PROVENIENTES DO CORTE DE PEçAS DE AçO INOXIDáVEL COMO MATéRIA-PRIMA PARA A PRODUçãO DE ARGAMASSAS EMPREGADAS NO REVESTIMENTO DE ALVENARIAS EM OBRAS CIVIS. O OBJETIVO PRIMORDIAL é CONTRIBUIR PARA A REDUçãO DOS PASSIVOS AMBIENTAIS ASSOCIADOS AOS FRAGMENTOS REMANESCENTES DO CORTE A LASER DAS PLACAS DE AçO INOXIDáVEL AISI 304, BEM COMO MINIMIZAR OS POTENCIAIS IMPACTOS AMBIENTAIS E OS CUSTOS OPERACIONAIS RELACIONADOS AO DESCARTE E RECICLAGEM DESSE MATERIAL. PARA AVALIAR A VIABILIDADE TéCNICA DAS ARGAMASSAS PROPOSTAS, FORAM CONDUZIDOS ENSAIOS LABORATORIAIS EM CONFORMIDADE COM AS NORMAS BRASILEIRAS. AS ARGAMASSAS FORAM PREPARADAS EM UMA PROPORçãO DE 1:1:6, CONTENDO CIMENTO, CAL E AREIA. DIFERENTES AMOSTRAS FORAM PRODUZIDAS, INCLUINDO AQUELAS COM ADIçãO DE RESíDUO EM PROPORçõES DE 5% E 10%, ALéM DE AMOSTRAS DE REFERêNCIA, COM IDADES DE 7 E 28 DIAS. EM SEGUIDA, AS ARGAMASSAS FORAM SUBMETIDAS A ENSAIOS DE RESISTêNCIA MECâNICA DE TRAçãO NA FLEXãO E DE COMPRESSãO AXIAL, ALéM TAMBéM DE ENSAIO DE ABSORçãO POR CAPILARIDADE, COM O INTUITO DE CLASSIFICá-LAS COM BASE EM SEUS RESULTADOS EM CONCORDâNCIA COM AS NORMAS BRASILEIRAS VIGENTES.

THE SEARCH FOR INNOVATIVE AND SUSTAINABLE SOLUTIONS IN THE CONSTRUCTION INDUSTRY HAS BECOME IMPERATIVE GIVEN THE GROWING DEMAND FOR NATURAL RESOURCES. THIS STUDY ADDRESSES THE USE OF WASTE FROM THE CUTTING OF STAINLESS STEEL PIECES AS RAW MATERIAL FOR THE PRODUCTION OF MORTARS USED TO COAT MASONRY IN CIVIL WORKS. THE PRIMARY OBJECTIVE IS TO CONTRIBUTE TO THE REDUCTION OF ENVIRONMENTAL LIABILITIES ASSOCIATED WITH FRAGMENTS REMAINING FROM THE LASER CUTTING OF AISI 304 STAINLESS STEEL PLATES, AS WELL AS MINIMIZING POTENTIAL ENVIRONMENTAL IMPACTS AND OPERATIONAL COSTS RELATED TO THE DISPOSAL AND RECYCLING OF THIS MATERIAL. TO EVALUATE THE TECHNICAL FEASIBILITY OF THE PROPOSED MORTARS, LABORATORY TESTS WERE CARRIED OUT IN ACCORDANCE WITH BRAZILIAN STANDARDS. THE MORTARS WERE PREPARED IN A RATIO OF 1:1:6, CONTAINING CEMENT, LIME AND SAND. DIFFERENT SAMPLES WERE PRODUCED, INCLUDING THOSE WITH RESIDUE ADDED IN PROPORTIONS OF 5% AND 10%, AS WELL AS REFERENCE SAMPLES, AGED 7 AND 28 DAYS. NEXT, THE MORTARS WERE SUBJECTED TO MECHANICAL TENSILE STRENGTH TESTS IN FLEXION AND AXIAL COMPRESSION, AS WELL AS CAPILLARY ABSORPTION TESTS, WITH THE AIM OF CLASSIFYING THEM BASED ON THEIR RESULTS IN ACCORDANCE WITH CURRENT BRAZILIAN STANDARDS.

Palavras-chave

Argamassas de revestimento; Resíduo de aço inoxidável; Sustentabilidade.

Coating mortars; Stainless steel waste; Sustainability.

Como citar

FARIA, RAQUEL AMENDRO; SIQUEIRA, ROMÁRIO MOREIRA; PEREIRA, RITA DE KASSIA GONÇALVES; TEIXEIRA, ANA CAROLINA MORATO; VIEIRA, CARLOS MAURÍCIO FONTES; CERQUEIRA, NIANDER DE AGUIAR; ALEXANDRE, JONAS. AVALIAÇÃO DA INCORPORAÇÃO DE RESÍDUO DE AÇO INOX EM ARGAMASSAS DE REVESTIMENTO NO ESTADO ENDURECIDO , p. 2884-2892. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-41308