OS MATERIAIS COMPóSITOS SURGIRAM A PARTIR DA NECESSIDADE DA INDúSTRIA POR MATERIAIS COM DESEMPENHO MECâNICO SUPERIOR AOS MATERIAIS CONVENCIONAIS, ALIADO à PREOCUPAçãO COM A SUSTENTABILIDADE. A UTILIZAçãO DE RESíDUOS ADVINDOS DE INDúSTRIAS MINERADORAS, SãO MATéRIAS-PRIMAS QUE PODEM SER UTILIZADAS NA COMPOSIçãO DESSES MATERIAIS. OBJETIVA-SE PRODUZIR MATERIAIS COMPóSITOS DE MATRIZ POLIMéRICA E RESíDUO DE CAULIM COMO AGENTE DE CARGA. A PRODUçãO DOS COMPóSITOS FOI PRODUZIDA DE FORMA MANUAL EM MOLDES DE SILICONE, SEGUINDO AS NORMAS ASTM D638-2014 E ASTM D790-2017. POSTERIORMENTE, FORAM CONDUZIDOS ENSAIOS MECâNICOS PARA AVALIAR AS PROPRIEDADES MECâNICAS DO MATERIAL. NO ENSAIO DE TRAçãO, FORAM ANALISADOS A RESISTêNCIA à TRAçãO, MóDULO DE YOUNG E DEFORMAçãO E NOS TESTES DE FLEXãO, FORAM AVALIADOS A RESISTêNCIA à FLEXãO E MóDULO DE ELASTICIDADE. DIANTE DISSO, PARA TRAçãO A COMPOSIçãO QUE APRESENTOU MAIOR RESISTêNCIA à TRAçãO, MAIOR MODULO DE YOUNG E MENOR DEFORMAçãO FOI O DE 15% DE ADIçãO DE RESíDUO DE CAULIM, PARA FLEXãO A COMPOSIçãO QUE APRESENTOU MAIOR RESISTêNCIA à FLEXãO E MAIOR MóDULO DE ELASTICIDADE FOI O DE 10% DE RESíDUO. CONCLUI-SE QUE, O ESTUDO DE RESíDUOS ADICIONADOS à MATRIZ POLIMéRICA APRESENTA BOAS CARACTERíSTICAS MECâNICAS, TORNANDO-OS PROMISSORES PARA O DESENVOLVIMENTO DE NOVOS MATERIAIS.
COMPOSITE MATERIALS HAVE EMERGED FROM THE INDUSTRY'S NEED FOR MATERIALS WITH SUPERIOR MECHANICAL PERFORMANCE COMPARED TO CONVENTIONAL MATERIALS, COUPLED WITH CONCERNS ABOUT SUSTAINABILITY. THE USE OF WASTE FROM MINING INDUSTRIES CONSTITUTES RAW MATERIALS THAT CAN BE USED IN THE COMPOSITION OF THESE MATERIALS. THE OBJECTIVE IS TO PRODUCE COMPOSITE MATERIALS WITH A POLYMER MATRIX AND KAOLIN WASTE AS A FILLER. THE COMPOSITES WERE MANUALLY PRODUCED USING SILICONE MOLDS, FOLLOWING ASTM D638-2014 AND ASTM D790-2017 STANDARDS. SUBSEQUENTLY, MECHANICAL TESTS WERE CONDUCTED TO EVALUATE THE MATERIAL'S MECHANICAL PROPERTIES. IN THE TENSILE TEST, TENSILE STRENGTH, YOUNG'S MODULUS, AND DEFORMATION WERE ANALYZED, WHILE IN THE FLEXURAL TESTS, FLEXURAL STRENGTH AND ELASTICITY MODULUS WERE EVALUATED. ACCORDINGLY, FOR TENSILE STRENGTH, THE COMPOSITION WITH 15% KAOLIN WASTE ADDITION SHOWED THE HIGHEST TENSILE STRENGTH, HIGHEST YOUNG'S MODULUS, AND LOWEST DEFORMATION. FOR FLEXURAL STRENGTH, THE COMPOSITION WITH 10% WASTE SHOWED THE HIGHEST FLEXURAL STRENGTH AND ELASTICITY MODULUS. IT IS CONCLUDED THAT THE STUDY OF WASTE ADDED TO THE POLYMER MATRIX PRESENTS GOOD MECHANICAL CHARACTERISTICS, MAKING THEM PROMISING FOR THE DEVELOPMENT OF NEW MATERIALS.
Palavras-chave
Compósitos; Resíduo; Caulim; Sustentabilidade.
Composites; Waste; Kaolin; Sustainability.
Como citar
BOTELHO, EMILY DE FÁTIMA PINHEIRO;
NASCIMENTO, DAMARES DA CRUZ BARBOSA;
SOUSA, PALOMA SUELLEN LIMA DE;
SOUZA, SARAH GABRIELLY BRANDÃO DE;
NASCIMENTO, JOELLY VERA;
CANDIDO, VERÔNICA SCARPINI;
SILVA, ALISSON CLAY RIOS DA.
AVALIAÇÃO DA INFLUÊNCIA DE RESÍDUO DO CAULIM COMO AGENTE DE CARGA NAS PROPRIEDADES MECÂNICAS DE COMPÓSITOS DE MATRIZ POLIMÉRICA
,
p. 336-347.
In: 22º Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas,
São Paulo, Brasil,
2024.
ISSN: 2594-4711
, DOI 10.5151/2594-4711-41056