AVALIAÇÃO DA INFLUÊNCIA DO TEOR DE PÓ DE ACIARIA ELÉTRICA NA AUTORREDUÇÃO DE BRIQUETES PRODUZIDOS COM BIOMASSA DE CAPIM ELEFANTE

EVALUATION OF THE INFLUENCE OF ELECTRIC ARC FURNACE DUST CONTENT ON THE SELF-REDUCTION OF BRIQUETTES PRODUCED WITH ELEPHANT GRASS BIOMASS

Autoria

Medeiros, Giulio Antunes de; Caldas, Rayla de Souza; Silva, Leonardo Martins; Araújo, Giselle de Mattos; Castro, José Adilson de

DOI

10.5151/2594-357X-33686

Downloads

Baixar Artigo 219 Downloads

Resumo

Para analisar a redução direta de briquetes autorredutores produzidos a partir de variados teores de pó de aciaria foram produzidos três lotes de misturas homogêneas a base de biomassa de capim elefante, minério de ferro, cimento e pó de aciaria elétrica em teores crescentes, os quais foram submetidos a ensaios termogravimétricos em forno de mufla e TGA em temperaturas e tempos variáveis. Foram obtidas as curvas dos graus de redução e os briquetes reduzidos foram analisados por microscopia eletrônica de varredura (MEV) e difração de raios-X (DRX). Os resultados demonstraram que a redutibilidade do aglomerado decresceu com o aumento do teor de pó de aciaria, havendo variações neste resultado para temperaturas mais elevadas. As microestruturas encontradas foram de particulado esférico, estrutura porosa ou whiskers. A partir da DRX, considerou-se provável que a diminuição do grau de redução com o aumento do pó de aciaria esteja relacionado à reação entre hematita e zincita, que se espera ser controlada pela difusão do zinco.

 

To analyze the direct reduction of self-reducting briquettes producted with different electric arc furnace dust contents, three sets of homogeneous mixtures were produced with elephant grass biomass, iron ore, cement and furnace dust in increasing levels, which were submitted to thermogravimetric tests in muffle furnace and TGA furnace at variable temperatures and times. The curves of degree of reduction were obtained and the reduced briquettes were analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results showed that the reducibility of the agglomerates is diminished by the increase of furnace dust, with variations of this result at higher temperatures. The observed microstructures were spherical particles, porous structure or whiskers. Based on XRD results, it was considered probable that the decrease of the degree of reduction with the increase of furnace dust content is related to the reaction between hematite and zincite, which is expected to be controlled by zinc diffusion.

Palavras-chave

Autorredução; Termogravimetria; Pó de Aciaria Elétrica; Capim Elefante

Self-reduction; Thermogravimetry; Electric Arc Furnace Dust; Elephant Grass