AVALIAÇÃO DA INFLUÊNCIA DO TIPO DE ESCÓRIA DE ALTO FORNO (EAF), NAS PROPRIEDADES DO GEOPOLÍMERO

EVALUATION OF THE INFLUENCE OF BLAST FURNACE SLAG TYPE (EAF) ON GEOPOLYMER PROPERTIES

DOI

10.5151/2594-5327-41351

Downloads

Baixar Artigo 3 Downloads

Resumo

ESTE ESTUDO AVALIA A INFLUêNCIA DE DIFERENTES TIPOS DE ESCóRIA DE ALTO FORNO (EAF) NAS PROPRIEDADES DE GEOPOLíMEROS, VISANDO ALTERNATIVAS MAIS SUSTENTáVEIS AO CIMENTO PORTLAND. A PESQUISA, CONDUZIDA NO LABORATóRIO DE PRáTICAS TECNOLóGICAS DA UFPA, UTILIZOU METACAULIM E TRêS TIPOS DE EAF COMO PRECURSORES. OS RESULTADOS MOSTRAM QUE A COMPOSIçãO QUíMICA DAS ESCóRIAS IMPACTA SIGNIFICATIVAMENTE AS PROPRIEDADES DOS GEOPOLíMEROS. O GEOPOLíMERO COM EAF TIPO 3 APRESENTOU A MELHOR PERFORMANCE, COM RESISTêNCIA à COMPRESSãO DE 35,8 MPA, MENOR ABSORçãO DE áGUA (6,04%), POROSIDADE APARENTE (12,67%) E MAIOR DENSIDADE (2,40 G/CM³). ESSES RESULTADOS INDICAM UMA MATRIZ MAIS COMPACTA E COESA, REFLETIDA NA ANáLISE MICROSCóPICA, QUE REVELOU UMA ESTRUTURA UNIFORME E HOMOGêNEA NA PASTA COM EAF TIPO 3, SEM AS BOLHAS PRESENTES NAS PASTAS DOS TIPOS 1 E 2. A PESQUISA CONCLUI QUE A ESCOLHA ADEQUADA DO TIPO DE EAF é CRUCIAL PARA OTIMIZAR AS PROPRIEDADES DOS GEOPOLíMEROS, COM EAF TIPO 3 MOSTRANDO-SE PARTICULARMENTE PROMISSOR. ESTE TRABALHO CONTRIBUI PARA A SUSTENTABILIDADE NA CONSTRUçãO CIVIL AO OFERECER UMA ALTERNATIVA VIáVEL E AMBIENTALMENTE AMIGáVEL AO CIMENTO PORTLAND.

 

THIS STUDY EVALUATES THE INFLUENCE OF DIFFERENT TYPES OF BLAST FURNACE SLAG (BFS) ON THE PROPERTIES OF GEOPOLYMERS, AIMING FOR MORE SUSTAINABLE ALTERNATIVES TO PORTLAND CEMENT. THE RESEARCH, CONDUCTED AT THE TECHNOLOGICAL PRACTICES LABORATORY OF UFPA, USED METAKAOLIN AND THREE TYPES OF BFS AS PRECURSORS. THE RESULTS SHOW THAT THE CHEMICAL COMPOSITION OF THE SLAGS SIGNIFICANTLY IMPACTS THE PROPERTIES OF THE GEOPOLYMERS. THE GEOPOLYMER WITH BFS TYPE 3 EXHIBITED THE BEST PERFORMANCE, WITH A COMPRESSIVE STRENGTH OF 35.8 MPA, LOWER WATER ABSORPTION (6.04%), APPARENT POROSITY (12.67%), AND HIGHER DENSITY (2.40 G/CM³). THESE RESULTS INDICATE A MORE COMPACT AND COHESIVE MATRIX, REFLECTED IN THE MICROSCOPIC ANALYSIS, WHICH REVEALED A UNIFORM AND HOMOGENEOUS STRUCTURE IN THE PASTE WITH BFS TYPE 3, WITHOUT THE BUBBLES PRESENT IN THE PASTES OF TYPES 1 AND 2. THE RESEARCH CONCLUDES THAT THE APPROPRIATE CHOICE OF BFS TYPE IS CRUCIAL TO OPTIMIZE THE PROPERTIES OF GEOPOLYMERS, WITH BFS TYPE 3 SHOWING PARTICULAR PROMISE. THIS WORK CONTRIBUTES TO SUSTAINABILITY IN CIVIL CONSTRUCTION BY OFFERING A VIABLE AND ENVIRONMENTALLY FRIENDLY ALTERNATIVE TO PORTLAND CEMENT.

Palavras-chave

Geopolímero; Escória de Alto forno; Resíduos

Geopolymer; Blast Furnace Slag; Waste.

Como citar

SANTANA, RAYANNE OLIVEIRA LEÃO; FERREIRA, PAULO ANDERSON ARANHA; FRANÇA, GIOVANA ZAGALO DE; SANTANA, VITOR LEÃO; SILVA, ALISSON CLAY RIOS DA; CANDIDO, VERÔNICA SCARPINI. AVALIAÇÃO DA INFLUÊNCIA DO TIPO DE ESCÓRIA DE ALTO FORNO (EAF), NAS PROPRIEDADES DO GEOPOLÍMERO , p. 3109-3117. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.