AVALIAÇÃO DA MICRODUREZA NAS LIGAS DE FE-CU-NB OBTIDAS POR PRENSAGEM A QUENTE

MICROHARDNESS EVALUATION IN FE-CU-NB ALLOYS OBTAINED BY HOT PRESSING

Autoria

Oliveira, Hellen Cristine Prata de; Silveira, Raissa Capanema Mendes da; Assis, Paulo Santos

Oliveira, Hellen Cristine Prata de

Eu sou esse autor

Silveira, Raissa Capanema Mendes da

Eu sou esse autor

Assis, Paulo Santos

Eu sou esse autor

DOI

10.5151/1516-392X-31651

Downloads

Resumo

Esse trabalho, tem como intuito estudar as ligas metálicas 56,66%Cu – 28,33%Fe – 15%Nb; 50%Cu – 25%Fe – 25%Nb; 43,34%Cu – 21,67%Fe – 35%Nb e 36,33%Cu – 18,33%Fe – 45%Nb, submetidas à sinterização nas condições de prensagem a quente a 800°C/35MPa/3 min. Foi observado o comportamento da estrutura quando se aumenta o teor, em peso, de nióbio nas ligas. Para maior entendimento das propriedades mecânicas das matrizes metálicas, com ênfase a relação da microdureza Vickers com a dureza, fez-se difração de raios X, microscopia ótica, microscopia de varredura, medição da dureza e microdureza Vickers, além da densidade relativa e porosidade. Avaliou-se o processo de sinterização e a efetividade da mesma entre os elementos de Fe, Cu e Nb. Os resultados revelam o aumento do teor de nióbio, favorecendo a formação de soluções sólidas, indicando melhor propriedades mecânicas. Além disso, percebe-se relação direta entra a dureza com a microdureza Vickers.

This paper has as objective to study specific metal alloys used in the metal matrix composites to compound rock cutting tools. The alloys compositions studied are 56,66%Cu – 28,33%Fe – 15%Nb; 50%Cu – 25%Fe – 25%Nb; 43,34%Cu – 21,67%Fe – 35%Nb e 36,33%Cu – 18,33Fe – 45%Nb. Those materials were submitted to sintering conditions of 800ºC temperature, 35Mpa pressure and 3min time. It was observed the structure behavior when the Nb weight grade is increased in the alloys. For a better mechanical properties comprehension of the metal matrixes, some tests were made as follows: x-ray diffraction, optical microstructure characterization, scanning electron microscopy, bulk density and porosity and, mainly, Vickers Hardness and Microhadness. The sintering process was assessed, as well as, its effectiveness using those elements. The results show that the Nb increase favors sloid solutions formation, indicating better mechanical properties. Besides that, realize the direct relation between Vickers Hardness and Microhardness.

Palavras-chave

Caracterização microestrutural; Microdureza Vickers; Prensagem a quente

Microstructural characterization; Vickers Microhardness; Hot pressing