Título

AVALIAÇÃO DA MICROESTRUTURA E DA TAXA DE CORROSÃO POR PITES APÓS TRATAMENTO TÉRMICO EM AÇO BAIXO CARBONO

EVALUATION OF MICROSTRUCTURE AND PITES CORROSION RATE AFTER HEAT TREATMENT IN LOW CARBON STEEL

Autoria

Pinheiro, Flávia Wagner; Pereira, Elaine Cristina; Gomes, Gustavo de Azevedo Barreto

DOI

10.5151/2594-5327-34210

Downloads

Baixar Artigo 8 Downloads

Resumo

A CORROSÃO É UMA DAS CAUSAS PRINCIPAIS DE FALHAS EM TUBULAÇÕES E EQUIPAMENTOS DA INDÚSTRIA PETROQUÍMICA. ESSAS FALHAS ACARRETAM EM CUSTOS ELEVADOS DE MANUTENÇÃO, PREJUDICAM O PROCESSO, ALÉM DE PROVOCAR RISCOS AO MEIO AMBIENTE. OS CUPONS DE CORROSÃO SÃO UTILIZADOS PARA AVALIAR A CORROSIVIDADE DE VÁRIOS SISTEMAS, PARA MONITORAR A EFICÁCIA DOS PROGRAMAS DE MONITORAMENTO DE CORROSÃO E PARA AVALIAR A ADEQUAÇÃO DOS DIFERENTES METAIS AOS AMBIENTE E SISTEMAS ESPECÍFICOS. EM GERAL, EMPRESAS DE MONITORAMENTO DE CORROSÃO ADQUIREM CUPONS DE DIFERENTES TIPOS DE FORNECEDORES, NACIONAIS OU IMPORTADOS, E POUCO SE OBSERVA QUANTO AO TIPO DE PROCESSAMENTO DURANTE A FABRICAÇÃO, A COMPOSIÇÃO QUÍMICA, A MICROESTRUTURA, O TAMANHO DE GRÃO, O TIPO DE TRATAMENTO TÉRMICO ENTRE OUTROS PARÂMETROS E O QUANTO, PODEM ALTERAR A CONFIABILIDADE DOS RESULTADOS OBTIDOS. O PRESENTE TRABALHO TEM COMO OBJETIVO AVALIAR A INFLUÊNCIA DE DIFERENTES TRATAMENTOS TÉRMICOS NA MICROESTRUTURA E NO MONITORAMENTO DA CORROSÃO POR PITES EM CUPONS DE PERDA DE MASSA DE AÇO AISI 1010

 

CORROSION IS A MAJOR CAUSE OF FAILURES IN PIPELINES AND EQUIPMENT IN THE PETROCHEMICAL INDUSTRY. THESE FAILURES RESULT IN HIGH MAINTENANCE COSTS, IMPAIR THE PROCESS, IN ADDITION TO CAUSING RISKS TO THE ENVIRONMENT. CORROSION COUPONS ARE USED TO ASSESS THE CORROSIVENESS OF VARIOUS SYSTEMS, TO MONITOR THE EFFECTIVENESS OF CORROSION MONITORING PROGRAMS AND TO ASSESS THE SUITABILITY OF DIFFERENT METALS FOR SPECIFIC ENVIRONMENTS AND SYSTEMS. IN GENERAL, CORROSION MONITORING COMPANIES ACQUIRE COUPONS FROM DIFFERENT TYPES OF SUPPLIERS, NATIONAL OR IMPORTED, AND LITTLE IS OBSERVED ABOUT THE TYPE OF PROCESSING DURING MANUFACTURE, CHEMICAL COMPOSITION, MICROSTRUCTURE, GRAIN SIZE, TYPE OF HEAT TREATMENT AMONG OTHER PARAMETERS AND HOW MUCH, CAN CHANGE THE RELIABILITY OF THE RESULTS OBTAINED. THE PRESENT WORK AIMS TO EVALUATE THE INFLUENCE OF DIFFERENT HEAT TREATMENTS ON THE MICROSTRUCTURE AND ON THE MONITORING OF PITTING CORROSION IN AISI 1010 STEEL LOSS COUPONS.

Palavras-chave

Corrosão por pites; Cupom; tratamentos térmicos

Pitting corrosion; Cupon; Heat Treatment