AVALIAÇÃO DA PROFUNDIDADE DO IMPACTO BALÍSTICO NO COMPÓSITO CARBETO DE SILÍCIO E ALUMINA : EVALUATION OF THE DEPTH OF THE BALLISTIC IMPACT ON THE SILICON CARBIDE AND ALUMINA COMPOSITE

O USO DE COMPóSITOS COM DIFERENTES PROPORçõES VEM SENDO AMPLAMENTE DIFUNDIDO E ESTUDADO, PARA APLICABILIDADE NA ENGENHARIA E INDúSTRIA, DE MANEIRA GERAL. A GAMA DE APLICAçõES DO CARBETO DE SILíCIO E DA ALUMINA, EM VáRIOS SETORES, DEVIDO AS SUAS EXCELENTES PROPRIEDADES COMO RESISTêNCIA MECâNICA, ALTA RESISTêNCIA à ABRASãO E ELEVADA DUREZA, MOSTRA A VIABILIDADE DE UNIR DOIS MATERIAIS PARA APLICAçõES DIVERSAS. O PRESENTE ESTUDO USA ESSES DOIS ELEMENTOS, EM PROPORçõES DE 40 E 60%, EM PESO, PARA A CONFECçãO DE UM COMPóSITO PARA ANALISAR A APLICABILIDADE EM POSSíVEIS PROTEçõES BALíSTICAS INDIVIDUAIS, POR MEIO DE ENSAIO BALíSTICO E ANáLISE DA PROFUNDIDADE DE IMPACTO. COM O APOIO DO CENTRO DE AVALIAçõES DO EXéRCITO (CAEX), FOI POSSíVEL A REALIZAçãO DOS TESTES BALíSTICOS, CONFORME A NORMA NIJ 0101.04, COM USO DE CALIBRE 7,62 X 51MM. O COMPóSITO ESTUDADO é UM PRODUTO COMERCIAL DA EMPRESA CETARCH. OS CORPOS DE PROVA EXPERIMENTADOS FORAM CONFECCIONADOS COM PLACA DE AçO INOX, COLA DE POLIURETANO E O INSERTO CERâMICO. OS DADOS OBTIDOS, EXPERIMENTALMENTE, MOSTRARAM QUE A ESPESSURA EFICAZ, PARA A ANALISAR A PROFUNDIDADE, DEVIDO A PENETRABILIDADE PARCIAL, OCORREU COM 6,5 MM DO COMPóSITO, TENDO O VALOR DE 11,30 MM DE PROFUNDIDADE EM RELAçãO AO IMPACTO DO PROJéTIL. A EFICáCIA DO INSERTO MOSTROU SER CAPAZ A IMPLEMENTAçãO DO MESMO PARA A PROTEçãO BALíSTICA INDIVIDUAL, PORéM COM A NECESSIDADE DE MAIORES TESTES DE ACORDO COM A NORMA ESPECIFICADA.

THE USE OF COMPOSITES WITH DIFFERENT PROPORTIONS HAS BEEN WIDELY DISSEMINATED AND STUDIED FOR APPLICABILITY IN ENGINEERING AND INDUSTRY IN GENERAL. THE RANGE OF APPLICATIONS OF SILICON CARBIDE AND ALUMINA, IN VARIOUS SECTORS, DUE TO THEIR EXCELLENT PROPERTIES SUCH AS MECHANICAL STRENGTH, HIGH RESISTANCE TO ABRASION AND HIGH HARDNESS, SHOWS THE FEASIBILITY OF JOINING TWO MATERIALS FOR DIFFERENT APPLICATIONS. THE PRESENT STUDY USES THESE TWO ELEMENTS, IN PROPORTIONS OF 40 AND 60%, BY WEIGHT, TO MANUFACTURE A COMPOSITE TO ANALYZE THE APPLICABILITY IN POSSIBLE INDIVIDUAL BALLISTIC PROTECTIONS, THROUGH BALLISTIC TESTING AND IMPACT DEPTH ANALYSIS. WITH THE SUPPORT OF THE ARMY ASSESSMENT CENTER (CAEX), IT WAS POSSIBLE TO CARRY OUT BALLISTIC TESTS, IN ACCORDANCE WITH THE NIJ 0101.04 STANDARD, USING A 7.62 X 51MM CALIBER. THE COMPOSITE STUDIED IS A COMMERCIAL PRODUCT FROM THE COMPANY CETARCH. THE TESTED SPECIMENS WERE MADE WITH STAINLESS STEEL PLATE, POLYURETHANE GLUE AND CERAMIC INSERT. THE EXPERIMENTALLY OBTAINED DATA SHOWED THAT THE EFFECTIVE THICKNESS, TO ANALYZE THE DEPTH, DUE TO PARTIAL PENETRABILITY, OCCURRED AT 6.5 MM OF THE COMPOSITE, WITH A VALUE OF 11.30 MM IN DEPTH IN RELATION TO THE IMPACT OF THE PROJECTILE. THE EFFECTIVENESS OF THE INSERT PROVED TO BE CAPABLE OF IMPLEMENTING IT FOR INDIVIDUAL BALLISTIC PROTECTION, BUT WITH THE NEED FOR FURTHER TESTING IN ACCORDANCE WITH THE SPECIFIED STANDARD.

Palavras-chave

Compósito, Carbeto de silício, profundidade de impacto

Composite, Silicon carbide, Impact depth.

Como citar

RIBEIRO, SHANELY DA SILVA; FORTINI, JEREMIAS ISMAEL NUNES; PEREIRA, ALTAIR SÓRIA; LIMA, EDUARDO DE SOUSA. AVALIAÇÃO DA PROFUNDIDADE DO IMPACTO BALÍSTICO NO COMPÓSITO CARBETO DE SILÍCIO E ALUMINA , p. 3562-3568. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-41499