AVALIAÇÃO DA RESISTÊNCIA AO IMPACTO IZOD DE UM COMPÓSITO COM MATRIZ EPÓXI REFORÇADO COM FIBRAS DE JUNCO-SETE-ILHAS (CYPERUS MALACCENSIS LAM.) POR ANÁLISES ESTATÍSTICAS

EVALUATION OF IZOD IMPACT RESISTANCE OF AN EPOXY MATRIX REINFORCED WITH (CYPERUS MALACCENSIS LAM.) SEDGE FIBERS BY STATISTICAL ANALYSIS

Autoria

Neuba, Lucas de Mendonça

DOI

10.5151/2594-5327-34396

Downloads

Baixar Artigo 24 Downloads

Resumo

COMPÓSITOS EPOXÍDICOS REFORÇADOS COM 10, 20 E 30% EM VOLUME DE UMA FIBRA LIGNOCELULÓSICA CIENTIFICAMENTE NOVA EM TERMOS DE SUA APLICAÇÃO COMO UM MATERIAL DE ENGENHARIA CONHECIDA NO BRASIL COMO JUNCO-SETE-ILHAS (CYPERUS MALACCENSIS LAM.). PROPRIEDADES MECÂNICAS ASSOCIADAS COM O ENSAIO DE IMPACTO IZOD FORAM INVESTIGADAS. AS DIMENSÕES DOS CORPOS DE PROVA FORAM DE 60,25 X 12,7 X 10 MM CONFORME A NORMA ASTM D256 E CONFECCIONADOS EM UM MOLDE DE AÇO MISTURANDO FIBRAS ALINHADAS COM UMA RESINA EPÓXI ENDURECIDA COM TRIETILENO TETRAMINA. OS RESULTADOS DEMONSTRARAM QUE OS COMPÓSITOS DE 30% APRESENTAM UM REFORÇO MAIS EFETIVO. ANÁLISES ESTATÍSTICAS REALIZADAS PELO MÉTODO DE WEIBULL, ANÁLISE DE VARIÂNCIA (ANOVA) E TESTE DE TUKEY CONFIRMARAM QUE REFORÇO DE 30% EM VOLUME DE FIBRAS DE JUNCO-SETE-ILHAS APRESENTOU A MAIOR ABSORÇÃO DE ENERGIA, REVELANDO UMA DIFERENÇA SIGNIFICATIVA ENTRE A FRAÇÃO VOLUMÉTRICA DE 10% E A MATRIZ DE EPÓXI PURA. A ANÁLISE DE WEIBULL EXIBIU UM AJUSTE LINEAR SATISFATÓRIO CONFIRMANDO UMA HOMOGENEIDADADE DOS CORPOS DE PROVA DE CADA GRUPO.

 

EPOXY COMPOSITES REINFORCED WITH 10,20 AND 30% IN VOL. OF A SCIENTIFICALLY NEW NATURAL LIGNOCELLULOSIC FIBER IN TERMS OF ITS USE AS AN ENGINEERING MATERIAL KNOWN IN BRAZIL AS SEVEN-ISLANDS-SEDGE (CYPERUS MALACCENSIS LAM.) WERE, INVESTIGATED FOR MECHANICAL PROPERTIES ASSOCIATED WITH IZOD IMPACT TEST. SPECIMENS WITH DIMENSIONS OF 60.25 X 12.7 X 10 MM, AS REQUIRED BY ASTM D256 STANDARD AND WERE FABRICATED IN A STEEL MOLD BY MIXING ALIGNED FIBERS WITH AN EPOXY RESIN HARDENED WITH TRIETHYLENE TETRAMINE. THE RESULTS HAVE SHOWN THAT THE COMPOSITE WITH 30 VOL% FIBER PRESENTS MORE EFFECTIVE REINFORCEMENT. STATISTICAL ANALYSES OF THE IMPACT ENERGYSS DATA OBTAINED, WERE PERFORMED BY WEIBULL METHOD, ANOVA AND TUKEY TEST. BOTH THE ANOVA AND TUKEY TEST ANALYSES WERE BASED ON A 95% CONFIDENCE LEVEL. THE TUKEY TEST CONFIRMED THAT THE REINFORCEMENT OF 30 VOL% OF SEVEN-ISLANDS-SEDGE FIBERS IN EPOXY COMPOSITES PRESENTS THE HIGHEST ABSORPTION ENERGY SHOWING A SIGNIFICANT DIFFERENCE FOR A PURE EPOXY MATRIX AND A 10% OF VOLUME FRACTION REINFORCING COMPOSITES. THE WEIBULL ANALYSES EXHIBITED A SATISFACTORY LINEAR ADJUSTMENT CONFIRMING AN HOMOGENEITY IN THE SPECIMENS GROUP.

Palavras-chave

Fibras de junco-sete-ilhas; ANOVA; Análise de Weibull

Seven-islands-sedge fibers; ANOVA; Weibull analysis.