Anais do Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas


ISSN 2594-4711

Título

AVALIAÇÃO DA RESISTÊNCIA À COMPRESSÃO DE GEOPOLÍMEROS A BASE DE METACAULIM DA PARAÍBA COM DIFERENTES TEMPERATURAS DE CALCINAÇÃO

EVALUATION OF COMPRESSION RESISTANCE OF GEOPOLYMERS BASED ON METACAULIM DA PARAÍBA WITH DIFFERENT CALCINATION TEMPERATURES

DOI

10.5151/2594-4711-41272

Downloads

Baixar Artigo 1 Downloads

Resumo

OS GEOPOLíMEROS SãO MATERIAIS CIMENTíCIOS QUE SãO SINTETIZADOS A PARTIR DA GEOPOLIMERIZAçãO DE UMA FONTE DE ALUMINOSSILICATOS JUNTO A UMA SOLUçãO ALCALINA. A PARTIR DA FORMAçãO DE LIGAçõES DE SI-O-AL, APRESENTAM PROPRIEDADES DE ALTO DESEMPENHO MECâNICO, INERCIA QUíMICA E DURABILIDADE, COM POTENCIAL DE SUBSTITUIR O CIMENTO PORTLAND, POR SE TRATAR DE UMA TECNOLOGIA VERDE, COM BAIXA DE EMISSãO DE GASES POLUENTES. O PRESENTE ESTUDO TEM COMO OBJETIVO AVALIAR A RESISTêNCIA à COMPRESSãO DAS PASTAS GEOPOLIMéRICAS PRODUZIDAS COM METACAULIM DO ESTADO DA PARAíBA, CALCINADO A DIFERENTES TEMPERATURAS (650°C, 750°C E 850°C POR DUAS HORAS). AS PASTAS GEOPOLIMéRICAS FORAM PRODUZIDAS UTILIZANDO SILICATO DE SóDIO E HIDRóXIDO DE SóDIO COMO SOLUçãO ALCALINA, E COMO MATERIAL PRECURSOR, FOI UTILIZADA ESCóRIA DE ALTO FORNO COMO FONTE DE CáLCIO E METACAULIM COMO FONTE DE ALUMINOSSILICATOS. APóS A IDADE DE CURA DE 7 DIAS, FORAM REALIZADOS ENSAIO MECâNICO E FíSICO DE RESISTêNCIA à COMPRESSãO E ABSORçãO DE áGUA, RESPECTIVAMENTE. POR FIM, FORAM FEITAS ANáLISES MORFOLóGICA DOS FRAGMENTOS DAS PASTAS ATRAVéS DE MICROSCóPIO óPTICO. OS RESULTADOS DEMONSTRAM QUE A RESISTêNCIA MECâNICA DA PASTA GEOPOLIMéRICA AUMENTA DE ACORDO COM A ELEVAçãO DA TEMPERATURA DE CALCINAçãO, ATINGINDO SEU PICO MáXIMO DE 37 MPA, E ATRAVéS DA ANáLISE POR MICROSCOPIA óPTICA, OBSERVOU-SE UMA MICROESTRUTURA DENSA E HOMOGêNEA, COMPROVANDO QUE O METACAULIM DEVE ALCANçAR SUA FASE METAESTáVEL PARA QUE HAJA UM EFICIENTE PROCESSO DE GEOPOLIMERIZAçãO.

 

GEOPOLYMERS ARE CEMENTITIOUS MATERIALS THAT ARE SYNTHESIZED FROM THE GEOPOLYMERIZATION OF A SOURCE OF ALUMINOSILICATES IN AN ALKALINE SOLUTION. BASED ON THE FORMATION OF SI-O-AL BONDS, THEY PRESENT PROPERTIES OF HIGH MECHANICAL PERFORMANCE, CHEMICAL INERTNESS AND DURABILITY, WITH THE POTENTIAL TO REPLACE PORTLAND CEMENT, AS IT IS A GREEN TECHNOLOGY, WITH LOW EMISSION OF POLLUTING GASES. THE PRESENT STUDY AIMS TO EVALUATE THE COMPRESSIVE STRENGTH OF GEOPOLYMERIC PASTES PRODUCED WITH METAKAOLIN FROM THE STATE OF PARAíBA, CALCINED AT DIFFERENT TEMPERATURES (650°C, 750°C AND 850°C FOR TWO HOURS). THE GEOPOLYMERIC PASTES WERE PRODUCED USING SODIUM SILICATE AND SODIUM HYDROXIDE AS AN ALKALINE SOLUTION, AND AS A PRECURSOR MATERIAL, BLAST FURNACE SLAG WAS USED AS A SOURCE OF CALCIUM AND METAKAOLIN AS A SOURCE OF ALUMINOSILICATES. AFTER THE CURING AGE OF 7 DAYS, MECHANICAL AND PHYSICAL TESTS OF COMPRESSIVE STRENGTH AND WATER ABSORPTION WERE CARRIED OUT, RESPECTIVELY. FINALLY, MORPHOLOGICAL ANALYZES OF THE PASTE FRAGMENTS WERE CARRIED OUT USING AN OPTICAL MICROSCOPE. THE RESULTS DEMONSTRATE THAT THE MECHANICAL RESISTANCE OF THE GEOPOLYMERIC PASTE INCREASES ACCORDING TO THE INCREASE IN THE CALCINATION TEMPERATURE, REACHING ITS MAXIMUM PEAK OF 37 MPA, AND THROUGH OPTICAL MICROSCOPY ANALYSIS, A DENSE AND HOMOGENEOUS MICROSTRUCTURE WAS OBSERVED, PROVING THAT METAKAOLIN MUST REACH ITS METASTABLE PHASE FOR AN EFFICIENT GEOPOLYMERIZATION PROCESS TO OCCUR.

Palavras-chave

Geopolímero; Metacaulim; Calcinação

Geopolymer; Metakaolin; Calcination.

Como citar

FRANÇA, GIOVANA ZAGALO DE; FERREIRA, PAULO ANDERSON ARANHA; SANTANA, RAYANNE OLIVEIRA LEÃO; SANTOS, DIEGO JOSÉ DA SILVA; SILVA, ALISSON CLAY RIOS DA; CANDIDO, VERÔNICA SCARPINI. AVALIAÇÃO DA RESISTÊNCIA À COMPRESSÃO DE GEOPOLÍMEROS A BASE DE METACAULIM DA PARAÍBA COM DIFERENTES TEMPERATURAS DE CALCINAÇÃO , p. 481-489. In: 22º Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, São Paulo, Brasil, 2024.
ISSN: 2594-4711 , DOI 10.5151/2594-4711-41272