Título

AVALIAÇÃO DA RESISTÊNCIA À TRAÇÃO E DO MÓDULO DE ELASTICIDADE DO COMPÓSITO DE MATRIZ EPÓXI REFORÇADO COM TECIDO DE CÂNHAMO

EVALUATION OF TENSILE STRENGTH AND ELASTIC MODULUS OF THE EPOXY MATRIX COMPOSITE REINFORCED WITH HEMP FABRIC

Autoria

Ribeiro, Matheus Pereira; Neuba, Lucas de Mendonça; Silveira, Pedro Henrique Poubel Mendonça da; Silva, Thuane Teixeira da; Monteiro, Sergio Neves

DOI

10.5151/2594-5327-34386

Downloads

Baixar Artigo 24 Downloads

Resumo

AS FIBRAS NATURAIS TEM SE MOSTRADO COMO UMA OPÇÃO DE REFORÇO QUE CADA VEZ MAIS VEM SENDO ESTUDADA. DENTRE OS TIPOS DE FIBRAS NATURAIS, AS FIBRAS LIGNOCELULÓSICAS (FNLS) TEM MAIOR ACEITAÇÃO NA INDÚSTRIA E NA COMUNIDADE CIENTÍFICA DEVIDO A SUA RENOVABILIDADE E DISPONIBILIDADE. NESTE TRABALHO, INVESTIGOU-SE O USO DO TECIDO DE CÂNHAMO (CANNABIS RUDERALIS) COMO REFORÇO DE UMA MATRIZ POLIMÉRICA EPOXÍDICA. COMPÓSITOS DE FRAÇÕES VOLUMÉTRICAS DE 10, 20 E 30% FORAM CARACTERIZADOS QUANTO À SUA RESISTÊNCIA À TRAÇÃO E MÓDULO DE ELASTICIDADE. ASSIM, OS RESULTADOS PERMITIRAM VISUALIZAR QUE OS COMPÓSITOS DE 30% V/V TIVERAM UM DESEMPENHO RELEVANTE FRENTE AOS DE 10 E 20%. MOSTROU-SE TAMBÉM QUE ESTAS FRAÇÕES NÃO MOSTRARAM DIFERENÇA SIGNIFICATIVA NA RESISTÊNCIA À TRAÇÃO E DUREZA PELO MÉTODO DE ANÁLISE DE VARIÂNCIA (ANOVA).

 

NATURAL FIBERS HAVE BEEN GROWINGLY RESEARCHED REINFORCEMENT IN COMPOSITES. AMID OF NATURAL FIBRES, THE LIGNOCELLULOSIC FIBRES (LNF) ARE THE MOST ACCEPTED BY THE INDUSTRIES AND RESEARCHES DUE TO ITS RENEWABILITY AND AVAILABILITY. AMONG THE NLFS, THE HEMP FIBERS HAVE SEVERAL APPLICATIONS AND IS HISTORICALLY USED IN TEXTILE INDUSTRIES, PAPERS AND EVEN AS MEDICINE. HOWEVER, ONLY SCARCE STUDIES OF HEMP FIBERS APPLIED TO ENGINEERING MATERIALS EXIST. THUS, THIS PAPER AIMS TO INVESTIGATE THE USE OF HEMP FABRIC AS REINFORCEMENT TO AN EPOXY MATRIX. COMPOSITES WITH VOLUME FRACTIONS OF 10, 20 AND 30% WERE CHARACTERIZED FOR TENSILE STRENGTH AND ELASTIC MODULUS. THE RESULTS SHOWED THAT THE 30% COMPOSITES PRESENT A RELEVANT PERFORMANCE COMPARED TO THE OTHERS COMPOSITES INVESTIGATED. FURTHERMORE, IT WAS SHOWED BY THE ANALYSIS OF VARIANCE (ANOVA) THAT THE 10 AND 20% VOLUMETRIC FRACTIONS COMPOSITES HAVE NO SIGNIFICANT DIFFERENCE IN BOTH PARAMETERS.

Palavras-chave

Tecido de cânhamo, Epóxi, Tração, elasticidade

Hemp fabric, Epoxy, Tensile, elasticity