AVALIAÇÃO DA SUBSTITUIÇÃO DE UM ANEL DE VEDAÇÃO PTFE POR UM ANEL DE BRONZE CUAL COM ADIÇÃO SUPERCIAL ATRAVÉS DO TRATAMENTO TERMOQUÍMICO DE SN

EVALUTION OF THE SUBSTITUTION OF A PTFE SEALING RING FOR A BRASS CUAL WTIH SUPERFICIAL ADDITION OF SN BY THERMOCHEMICAL TREATMENT

Autoria

Neuba, Lucas de Mendonça

DOI

10.5151/2594-5327-34454

Downloads

Baixar Artigo 12 Downloads

Resumo

O METAL BABBITT ESTÁ SENDO AMPLAMENTE UTILIZADO DURANTE ANOS COMO MATERIAL DE ROLAMENTO, EMBORA POSSUA UM ALTO CUSTO. O PRESENTE TRABALHO VISA O USO DE UMA LIGA BRONZE ALUMÍNIO CUAL COM ESTANHO (SN) SUPERFICIAL COMO UM SUBSTITUTO PARA O POLÍMERO POLITETRAFLUOROETILENO (PTFE) USADO PELA INDÚSTRIA EM MUITAS APLICAÇÕES TRIBOLÓGICAS, DESTACANDO SEU USO EM ROLAMENTOS, SELOS E ANÉIS DE VEDAÇÃO. EMBORA, POSSUAM MUITAS CARACTERÍSTICAS POSITIVAS FORNECIDAS PELO MATERIAL, OS MESMOS FALHAM EM ALTAS PRESSÕES E TEMPERATURAS. POR ESSA RAZÃO E VISANDO REDUZIR CUSTOS, ADQUIRINDO UM MATERIAL QUE ATUE SOB ESSAS CONDIÇÕES POSSUINDO UM BAIXO CUSTO, A PRESENTE PESQUISA UTILIZOU AMOSTRAS DE BRONZE ALUMÍNIO CUAL SAE-68D SUBMETIDO A UM PROCESSO DE TRATAMENTO TERMOQUÍMCO PARA DIFERENTES PERÍODOS DE 3, 4 E 5 HORAS EM TEMPERATURAS ACIMA DE 150°C. A MAIOR DIFUSÃO SE ENCONTRA PRESENTE NO PERÍODO DE 5 HORAS. DEPOIS DISSO ALGUMAS ANÁLISES DE MICROSCOPIA ELETRÔNICA POR VARREDURA E EDS FORAM REALIZADAS PARA VERIFICAR AS DIFERENÇAS DE GRADIENTE PRESENTES NAS AMOSTRAS.

 

BABBITT METAL ALLOYS ARE WIDELY APPLIED AS BEARING MATERIALS FOR YEARS, DESPITE THEIR HIGH COST. THE PRESENT WORK AIMS TO USE A BRASS ALUMINUM CUAL ALLOY COATED WITH SUPERFICAL TIN (SN) AS A REPLACEMENT OF POLYTETRAFLUOROETHYLENE (PTFE) POLYMER WIDELY USED IN INDUSTRY FOR MANY TRIBOLOGICAL APLICATIONS, HIGHLIGHTING THEIR USE IN PLAIN BEARINGS, RINGS AND SEALS. DESPITE, SOME POSITIVE CHACRACERISTICS GIVEN BY THIS MATERIAL IT MAY FAIL AND LOSE THEIR PROPERTIES AT HIGH PRESSURES AND TEMPERATURES. FOR THIS REASON AND AIMING TO REDUCE SOME COSTS BY ACQUIRING CHEAPER MATERIALS, THE PRESENT RESEACH WORKED WITH SAMPLES OF CUAL BRASS SAE-68D SUBJECTED TO A THERMOCHEMICAL TREATMENT PROCESSES FOR DIFFERENTS PERIODS OF 3, 4 AND 5 HOURS AT TEMPERATURES ABOVE 150°C. THE HIGHER DIFFUSION HAVE OCURRED IN THE PERIOD OF 5 HOURS. AFTER THAT SOME ANALYSIS OF SCANNING ELECTRON MICROSCOPY (SEM) AND EDS HAVE BEEN DONE TO VERIFY THE DIFERRENCES OF THE GRADIENTS OF SN PRESENT ON THE SPECIMENS.

Palavras-chave

Tratamento termoquímico; Difusão; MEV; EDS.

Thermochemical treatment; Diffusion; SEM; EDS.