Título

AVALIAÇÃO DAS PROPRIEDADES MECÂNICAS E ENERGIA DE PROJÉTIL ABSORVIDA EM COMPÓSITOS EPÓXI-FIBRAS DE CARNAÚBA APLICADOS EM BLINDAGEM BALÍSTICA

EVALUATION OF MECHANICAL PROPERTIES AND THE PROJECTILE’S LOSS ENERGY OF CARNUBA FIBER EPOXY COMPOSITES APPLIED IN BALLISTIC ARMOR

Autoria

Junio, Raí Felipe Pereira

DOI

10.5151/2594-5327-34254

Downloads

Baixar Artigo 12 Downloads

Resumo

O CRESCENTE AUMENTO DA VIOLÊNCIA EVIDENCIADO NAS ÚLTIMAS DÉCADAS PREOCUPA AUTORIDADES ENVOLVIDAS NA SEGURANÇA PÚBLICA. TAL FATO IMPULSIONA O DESENVOLVIMENTO DE ESTUDOS DIRECIONADOS À PRODUÇÃO DE NOVOS MATERIAIS DESTINADOS PARA APLICAÇÕES BALÍSTICAS, DESTACANDO-SE A UTILIZAÇÃO DE FIBRAS NATURAIS LIGNOCELULÓSICAS (FNLS) EM MATRIZES POLIMÉRICAS. NESSE ÂMBITO, DESTACA-SE A IMPLEMENTAÇÃO DE FIBRAS DA FOLHA DA CARNAÚBA (COPERNÍCIA PRUNÍFERA) COMO REFORÇO EM COMPÓSITOS POLIMÉRICOS DESTINADOS À PROTEÇÃO BALÍSTICA. PARA TAL FORAM PRODUZIDOS COMPÓSITOS NAS FRAÇÕES DE 0, 10, 20, 30 E 40% EM VOLUME DE FIBRAS, OS QUAIS FORAM ENSAIADOS POR TRAÇÃO E COMPORTAMENTO BALÍSTICO PRELIMINAR. OS COMPÓSITOS APRESENTARAM PROPRIEDADES MECÂNICAS SUPERIORES A RESINA EPÓXI PURA, COM RESISTÊNCIA A TRAÇÃO ENTRE 38 A 41 MPA, MÓDULO DE ELASTICIDADE NO INTERVALO DE 2,3 E 2,6 GPA E DEFORMAÇÃO TOTAL DE 1,5%. AS PLACAS APRESENTARAM REDUÇÃO SIGNIFICATIVA DA ENERGIA DE ABSORÇÃO, ONDE O COMPÓSITO DE 40% DE FIBRAS APRESENTOU 43,4% DE DECRÉSCIMO DA PROPRIEDADE.

 

THE GROWING INCREASE IN VIOLENCE SEEN IN RECENT DECADES WORRIES AUTHORITIES INVOLVED IN PUBLIC SECURITY. THIS FACT DRIVES THE DEVELOPMENT OF STUDIES AIMED AT THE PRODUCTION OF NEW MATERIALS INTENDED FOR BALLISTIC APPLICATIONS, HIGHLIGHTING THE APPLICATION OF NATURAL LIGNOCELLULOSIC FIBERS (NLFS) IN POLYMERIC MATRIX. IN THIS CONTEXT, HIGHLIGHT THE IMPLEMENTATION OF THE CARNAUBA LEAF FIBERS (COPERNICIA PRUNIFERA) AS REINFORCEMENT IN POLYMERIC COMPOSITES INTENDED FOR BALLISTIC PROTECTION. FOR THIS PURPOSE, COMPOSITES WERE PRODUCED IN FRACTIONS OF 0, 10, 20, 30 AND 40% IN VOLUME FRACTION, WHICH WERE TESTED BY TENSILE TESTS AND PRELIMINARY BALLISTIC BEHAVIOR. THE COMPOSITES SHOWN MECHANICAL PROPERTIES SUPERIOR TO NEAT EPOXY RESIN, WITH TENSILE STRENGTH BETWEEN 38 TO 41 MPA, ELASTICITY MODULUS IN THE RANGE OF 2.3 AND 2.6 GPA AND TOTAL DEFORMATION OF 1.5%. THE COMPOSITES PLATES SHOWN A SIGNIFICANT REDUCTION IN THE ENERGY OF ABSORPTION, WHERE THE COMPOSITE OF 40% OF FIBERS PRESENTED 43.4% DECREASE IN PROPERTY.

Palavras-chave

Compósitos; Propriedades mecânicas; Blindagem balística.

Composites; Mechanical properties; Ballistic armor.