AVALIAÇÃO DAS PROPRIEDADES TERMOMECÂNICAS DE FIOS SUPERELÁSTICOS DE NITINOL MICROSOLDADOS PELO PROCESSO TIG

EVALUATION OF THE THERMOMECHANICAL BEHAVIOR OF SUPERELASTIC NITINOL WIRES MICRO WELDED BY TIG ARC PULSES

DOI

10.5151/1516-392X-24439

Downloads

Baixar Artigo 442 Downloads

Resumo

O processo de micro soldagem se mostra eficiente para a união de Ligas com Memória de Forma (LMF) do sistema NiTi devido a alta precisão e localização do calor, diminuindo os tamanhos da zona fundida (ZF) e da zona termicamente afetada (ZTA), promovendo melhorias nas propriedades mecânicas destes tipos de juntas. Este estudo teve como objetivo geral determinar as variações das propriedades termomecânicas em juntas soldadas de fios de NiTi. Para o trabalho, fios superelásticos de uma LMF NiTi (ASTM F2063) com 0,9 mm de diâmetro, foram divididos em dois grupos: (a) fios sem tratamento térmico (NiTiA) e (b) fios com tratamento térmico a 400°C durante 20 minutos (NiTi400). Em seguida estes fios foram soldados pelo processo TIG, utilizando a microsoldadora Micromelt (EDG Equipamentos e Controles). A caracterização termomecânica dos fios íntegros e microsoldados foi realizada utilizando ensaios de calorimetria diferencial de varredura (DSC), análise dinâmico-mecânica (DMA), ensaios de tração uniaxial, microscopia óptica (MO), microscopia eletrônica de varredura (MEV) e microindentação Vickers. Os resultados mostraram a eficiência do processo TIG ao soldar os fios NiTi de ambos os grupos. As juntas soldadas apresentaram propriedades de superelasticidade semelhante aos fios íntegros e a análise da fratura dos fios com solda mostra características dúcteis.

 

Micro welding is an efficient way for joining shape memory alloys (SMA) due to high accuracy and location of heat, reducing the size of the molten zone and heat affected zone (HAZ) promoting improvements in mechanical properties in these types of joints. This study aimed to determinate variations in thermomechanical properties of welded joints of NiTi wires. In this work, superelastic NiTi wire (ASTM F2063) 0.9 mm diameter were divided into two groups: (a) as received wires (NiTiA) and (b) heat treated wires at 400°C for 20 min (NiTi400). Then, these wires were welded by TIG process, using Micromelt welder (EDG Equipment and Controls). The thermomechanical characterization of micro welded wires was performed using tests of differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), uniaxial tensile test, optical microscopy (OM), scanning electron microscopy (SEM), and Vickers microhardness. The results show the efficiency of TIG welding wires to both groups. Welded joints showed similar properties to reference wires and the fracture surface analysis showed a ductile profile.

Palavras-chave

Ligas com memória de forma; NiTiNOL; Microsoldagem; TIG; Superelasticidade

Shape memory alloys; NITINOL; Micro welding; Superelasticity

Como citar

Fernando Andrade Amorim; Luiz Fernando Alves Rodrigues; Carlos José de Araújo; João Baptista da Costa Agra de Melo; Theophilo Moura Maciel. AVALIAÇÃO DAS PROPRIEDADES TERMOMECÂNICAS DE FIOS SUPERELÁSTICOS DE NITINOL MICROSOLDADOS PELO PROCESSO TIG , p. 6735-6746. In: 69° Congresso Anual da ABM - Internacional, São Paulo - Brasil, 2014.